Electric iron chrome aluminum alloy surface insulation and anti-oxidation mechanism

Author: YeFengChun
Tutor: GuoShaoYi
School: Zhejiang University of Technology
Course: Mechanical Design and Theory
Keywords: 0Cr25Al5 surface insulation direct oxidation liquid molten anodic oxidation
CLC: TG132.3
Type: Master's thesis
Year: 2011
Downloads: 50
Quote: 0
Read: Download Dissertation

Abstract


Fe-Cr-Al alloys with high resistance and the low resistance temperature coefficient, high resistance of temperature oxidation, low price and so, is the most widely used metal heating element materials. But in some specific situations, you need to insulate the surface. In this paper, 0Cr25Al5 as the main object of study, were used to direct oxidation, molten salt immersion and anodic oxidation surface of insulating film was prepared. At the same time, the use of SEM, XRD, EDS and other means, test and analysis of the surface insulating film morphology, composition and formation mechanism. In direct oxidation process, the effects of time and temperature on the preparation of the surface insulating film are investigated. In preparation of liquid molten salt leaching process, the time on the preparation of molten salt surface insulation film were investigated. The effects of different current density on the preparation of the surface insulating film are investigated by constant current anodic oxidation.The results showed that: by direct oxidation at 1000℃for 72 hours under the conditions of preparation of the insulating oxide film surface compact and uniform, the resistance of not less than 2K?. Some surface spalling, crystal mainly columnar grains. Almost the entire oxygen insulation layer, aluminum elements, each element of the mass ratio increased with the temperature gradually stabilized. Surface insulation layer is part ofθ-Al2O3 andα-Al2O3. Flux method with immersion time at 450℃with different oxide, which oxide insulating film on the surface 72h to obtain the best effect, the electrical resistance of not less than 20K?. With the oxidation time, the surface grain alignment was tend to order from the chaos, tightly packed grains. Surface layer of aluminum oxide and chromium oxide based chromium oxide Cr2O3 and Cr8O21 mainly composed of aluminum oxide is mainlyα-Al2O3.Through constant current anodic oxidation ,which the surface film prepared by using a current density of 0.4A/dm2 get the best insulation, the resistance of surface no less than 15K?, smoother surface, cracks and pores less. Surface insulation film is mainly from theθ-Al2O3 and Cr3O4 composition, also contains a small amount of chromite spinel andα-Al2O3. Above all, these three methods can be heating in the Fe-Cr-Al alloy prepared insulating film. Prepared by molten salt immersion resistance of the highest insulating film, the surface composition ofα-Al2O3 content of up to; anodic oxidation method followed by the insulation film resistors; insulating film which prepared by direct oxidation is the lowest surface resistance.

Related Dissertations

  1. The Study of Synthesis and Properties of ZSM-5 Zeolite Membrane on Stainless Steel Wire Mesh Substrate,TQ424.25
  2. Fabrication and Properties of Titania Nanotube Arrays by Anodic Oxidation,TB383.1
  3. TiO_2 nanotube , Modification and Application,O614.411
  4. Study on Anodic Oxidation Technology and Corrosion Resistance of Aluminum Silicon Alloy,TG174
  5. The Study of InGaAsN Laser Fabricated with PAO,TN248
  6. A Study on Technique and Property of Anodic Oxidation on Biomedical Pure Titanium,TG174.44
  7. Study on Anodic Oxidation Surface Treatment of PAN-Based High-Modulus Carbon Fibers by Cyclic Voltammetry,TQ342.742
  8. Study on the Conversion of Elemental Mercury in Coal-fired Flue Gas by Direct Oxidation,X701
  9. Synthesis and Characteriazation of ZnO Films by Magnetron Sputtering and Direct Oxidation,O484.1
  10. Study on Aluminum Hard Anodic Oxidation and Coloring Technology,TG174.4
  11. Development of Halogen-free Flux Used for Lead-free Solder Wire,TG42
  12. Effect of Additives on the Direct Oxidation of Sodium Borohydride,TM911.4
  13. Alpine Region of Mass Effects of the Concrete Surface Thermal Simulation Studies,TU755
  14. Study on Preparation and Performance of Direct Oxide Anode for Intermediate-Temperature SOFC,TM911.4
  15. Preparation and Properties of Doped Titanate Anode for Direct Oxidation of Hydrocarbon Fuels in Solid Oxide Fuel Cells,TM911.4
  16. Study on Selective Laser Sintering of SiC and Post Process,TF124.5
  17. Study on the Electrochemical Behavior of Sodium Borohydride,TM911.4
  18. Preparation and Study of Catalyst by Anodic Oxidation Treatment and Adding with the Rare Earth for Volatile Organic Compounds Oxidation,O643.36
  19. Simulation and Study on Temperature and Stress Fields for Mass Concrete Structure,TU375
  20. Micro-Inhomogeneous Structure of Liquid Al-Fe System Alloys,TG113.1
  21. Study of the Fabrification of One Dimensional Nanomaterial on the Anodic Alumina Template,TB383.1

CLC: > Industrial Technology > Metallurgy and Metal Craft > Metallurgy and Heat Treatment > The alloy learn with a variety of properties of alloys > Special physical properties of alloys > Special thermal properties of alloys
© 2012 www.DissertationTopic.Net  Mobile