Synthesis and Characterization of Modified Styrene-Acrylic Emulsion and Study of Coating

Author: LvXiuBo
Tutor: GuoWenLu
School: Jiangsu University of Science and Technology
Course: Applied Chemistry
Keywords: emulsion polymerization styrene-acrylic emulsion modified by organosilicon characterization study of coatings
CLC: TQ630.6
Type: Master's thesis
Year: 2010
Downloads: 288
Quote: 0
Read: Download Dissertation

Abstract


In this thesis, the study of styrene-acrylic emulsion modified by organosilicon both at home and abroad was reviewed. The stable styrene-acrylic emulsion modified by organosilicon was prepared by preemulsified addition. The performance and characterization of the product was studied. The effect of surfactants, initiator, content of organosilicon, temperature on modified styrene-acrylic emulsion was investigated,and the best formulation of emulsion modified by organosilicon was determined. The best formulation condition of modified emulsion could be obtained when the contents of surfactants was 3%, the ratio of surfactants was 1/3, the contents of reactive surfactant was 1%, the content of initiator was 0.6%, the best polymerization temperature was 75℃～80℃, the ratio of soft monomer to hard monomer was 1/1, the content of organosilicon was 2%. The structure of styrene-acrylic emulsion modified by organosilicon was characterized by Fourier transform infrared spectroscopy, the peaks at 842cm-1 and 1030cm-1 correspond respectively to the stretching motion of Si-C and Si-O, so organosilicon have joined in the polymer. The differential scanning calorimetry was employed to monitor the glass transition temperature of styrene-acrylic emulsion modified by organosilicon(Tg=20℃),this temperature was bigger than unmodified styrene-acrylic emulsion(Tg=15℃). The thermal graviting analysis was employed to monitor the thermal stability of emulsions, found that the thermal stability of modified emulsion was higher than unmodified emulsion. The stability of frost and thaw and proofwater tests confirmed that the styrene-acrylic emulsion modified by organosilicon possessed higher thermal stability, waterproof ability compared to styrene-acrylic emulsion.The coating was prepared with modified styrene-acrylic emulsion. When some performances of coating was studied, we found that the waterproof ability and weatherproof ability of modified coatings exceeded unmodified coatings. The effect of various additive agent on the coating was investigated, the results showed: the best content of defoamer was 0.6%～0.8%, the content of film additive was 1.5%～2.0%, the content of leveling agent was 0.1%～0.15%, the content of bodying agent was 0.2%～0.3%, the content of dispersant was 1.0%～1.2%, the best formulation of coating modified by organosilicon was obtained.

Related Dissertations

  1. The convergence of mathematics teaching in primary and secondary schools under the new curriculum with the problem representation,G633.6
  2. Studies on Synthesis, Characterization and Properties of Fe-V Co-doped TiO2 Catalyst,O614.411
  3. Characterization of Corn Lectin and Application to Screen of Growth-promoting Bacteria from Corn Rhizosphere,S513
  4. Health-based and Ecological Risk Assessment of Contaminated Sites,X820.4
  5. Preliminary Research on Characterization of Thermophilic Protease Pasey and Helicase Htc16,Q814
  6. Cloning and Expression of Xylanase Gene from Thermobifida Halotolerans YIM 90462~T,Q78
  7. Isolation and Characterization of Carbendazim-Degrading Strains, Cloning and Expression of the mheI Gene,X172
  8. Characterization of an Atrazine-Degrading Strain, Cloning of Key Degrading Related Genes and Construction of a Gene Cluster,X172
  9. Preparation and Characteration of Composite Microspheres with Dual-, Triple- Responsive Properties,O631.3
  10. Study on the Characteristics of Endoproteases and Changes of Main Nitrogenous Components during Brown Rice Germination,TS210.1
  11. Characterization and Combining Ability of New CMS Lines Improved Using Zhenshan 97 B, an Early Maturity Maintainer, in Indica Rice (Oryza Sativa L.),S511.21
  12. Characterization of a New L-amino Acid Oxidase from Agkistrodon Blomhoffii Ussurensis Snake Venom,Q55
  13. Preparation, Separation of Monascus Pigments and Structural Characterization of Monascus Yellow Pigment,TS264.4
  14. Written by English bilingual mental representation of word recognition and activation process of,B84
  15. Molecularly Imprinted Polymer Microspheres and Evaluation,O631.3
  16. Complexes of two iodine three Allylthiourea together Synthesis and Characterization of cadmium,O627
  17. 1,4 - bis (4 - amino-2 - (trifluoromethyl) phenoxy ) benzene -type Schiff base imide copolymer synthesis and characterization,O631.3
  18. New water-based whiteboard ink water development,TS951.23
  19. Core-shell polymer microspheres synthesis, modification and application,O631.3
  20. Quad core and single-core 1,3,5 - triazine pentadiene Synthesis and characterization of metal,O627
  21. The Frequency Characteristics of Mind Wandering: Questionnaire Development,B841

CLC: > Industrial Technology > Chemical Industry > Paint Industry > General issues > Paint production process
© 2012 www.DissertationTopic.Net  Mobile