Preparetion and Application of Adhesive Used in Alumina-silicate Fiber Paper

Author: LiQuanPeng
Tutor: ZhaoChuanShan
School: Shandong Institute of Light Industry
Course: Pulp and Paper Engineering
Keywords: alumina silicate fiber adhesive papermaking PVA fiber heat insulation mechanism
CLC: TS727
Type: Master's thesis
Year: 2010
Downloads: 62
Quote: 0
Read: Download Dissertation

Abstract


Alumina silicate fiber paper as a slim heat barrier material has the advantages of little volumetric weight, low thermal conductivity, excellent thermal insulation properties, environmental friendly and long useful life. Alumina silicate fiber paper can be used in various industries. So we need to prepare alumina silicate fiber papers which have different heat resistance. In this research, the formulation and modification of adhesive used in alumina silicate fiber were investigated. The adhesives suit for alumina silicate fiber paper with different conditions was preparationed. Concrete work and major achievements included as follows:1 The formulation of adhesive①. The alumina silicate fiber paper adding organic adhesive has good physical strength. The effect of phenolic resin was best. But the organic adhesilves have low heat-resistant quality. Inorganic adnesive has good heat-resistant quality while bondstrength was bad. Sodium silicate was good than others.②. The effect of paper strength was good when adhesive were formulated. The retention of adhesive was increased with formulation. The best formulation ratio between CMC and cationic starch was 1:1. The best formulation ratio between CMC and PVA was 8:2. The formulation ratio between ludox and sodium silicate was designed 10:1. And the formulation ratio between sodium silicate and PVA was designed 10:1. The formulated adhesive between sodium silicate and PVA adding in slumina silicate fiber paper can be used in 400℃.2 The modification of inorganic adhesive①. The brittleness and strength performance of sodium silicate were improved by modificated with disodium hydrogen phosphate and borax. The best dosage of disodium hydrogen phosphate was 4%. The best dosage of borax was 2.5%.②. The strength of alumina silicate fiber paper adding modificated sodium silicate was improved. The effect of modification with borax was better than disodium hydrogen phosphate.3 Preparation of modificated organic adhesive①. Phenolic resin was modified with boric acid. The optimum preparation conditions by experimental study were as follows:The best molar ratio of phenol: aldehyde: boric acid was 1:1.5:0.4. The dosage of ammonia liquor as catalyst was 10%. The condensation reaction time was 2.0～2.5 hours in the condition of 60～80℃. The esterification reaction time was 3 hours in the temperature condition of 100℃.②. Modified phenolic resin had a resistance to high temperature up to 600℃, which could be mainly explained by reduce of free hydroxyl group quantity and introduce of boron-oxygen bond whose bonding energy was higher than that of carbon-carbon bond.4 Discussion of solid adhesiveThe optimum conditions of adding PVA fiber used in alumina silicate fiber paper were as follows: the dosage of PVA fiber was 20%, drying temperature was 140℃, and jittertime was 210s. The dosages of formulated adhesive were: CMC was 10%. Sodium silicate, ludox and PAC were 50%.5 Formula of adhesive used in different productions①.The adhesive used in vacuum cup was 10% phenolic resin. The adhesive used in humidifier was 20% sodium silicate and 2%PVA. The adhesive used in high temperature stove was 20% modification sodium silicate with borax.②.The membrane was formed with adhesive used in alumina silicate fiber paper. The convective heat transfer of air was reduced in the impact of membrane. So the heat-shielding performance of alumina silicate fiber paper was improved.

Related Dissertations

  1. The Research about the Processing and Performance of Waterproof Breathable Laminated Fabrics,TS195.6
  2. Study on the Mechanical Properties of Pva-high Toughness Cementitious Composites,TU528
  3. Study on Organic Silicone Modified Epoxy Resins Performance and Preparation of Adhesive,TQ323.5
  4. Different Bottom Structure of Dental Brackets Affect the Adhesiveness-Three Dimensional Finite-element Analysis,R783.5
  5. Research and Engineering Application of Heat-resistant Sodium Water Glass Adhesive,TQ437
  6. Engine controller package bonding layer durability,U464.13
  7. PVA fiber concrete damage evolution acoustic emission monitoring and destructive mechanism,TU528.572
  8. Study on Composite Bridge Deck Waterproof Adhesive Layer for Humid and Rainy Area,U443.31
  9. Development of High-performance Modified Asphalt Emulision for Ultra-thin Wearing Course Interlayer Bonding Materials,U414
  10. The Effect of Three Dentine Desensitizers on Bond Strength of Luting Agents,R783
  11. Effect of Self-etching Adhesive Ⅰ Bond on the Permeability of Dentin with Different Brushing Ways in Vitro,R780.2
  12. Interconnection of the anisotropic conductive film ultrasound the COG devices of Technology,TN405
  13. Study on Biological Acidifieation PreciPitation of Lignin of Pulp Mill Wastewaters,X793
  14. Surface Modification of Precipitated Calcium Carbonate and Its Application in Paper-making Process,TS727
  15. Theoretical and Numerical Investigation on the Residual Thermal Stress Distribution in Single Lap Joint,TG491
  16. Film-forming and Property Evaluation of Algal Polysaccharide Composite Gel,TB383.2
  17. Study on Acrylate Emulsion Pressure Sensitive Adhesive for Biological Surface,TQ436.3
  18. Temperature RTV-1 silicone rubber adhesive of,TQ333.93
  19. Redispersible powder on properties of cement mortar,TU578.1
  20. Study on the Debonding Mechanism and the Protection Capability of Ceramic Composite Armors Against Multi-hit,E923.1
  21. Different Curing Methods on Resin Bond Strength of Fiber Post,R783.1

CLC: > Industrial Technology > Light industry,handicrafts > Paper Industry > Raw materials and auxiliary materials > Auxiliary materials
© 2012 www.DissertationTopic.Net  Mobile