Preparation and Properties of SIC High Temperature Ceramics Coating

Author: ZhaoJianMin
Tutor: SuiShaoHua
School: Harbin Institute of Technology
Course: Materials Processing Engineering
Keywords: SiC Ceramics coating Argon-arc Cladding epitaxial growth Ablation Resistance inert oxidation
CLC: TG174.453
Type: Master's thesis
Year: 2010
Downloads: 172
Quote: 1
Read: Download Dissertation

Abstract


SiC high Temperature Ceramics coatings were prepared on the surface of graphite block by Argon-arc Cladding. The influence of different composition designs on preparation of coating was studied under some technological parameters. Analyzed interface behavior and mechanisms of coating. Microstructure, phase and hardness of coating were analyzed by use of SEM, EDS, XRD and HV-test. Ablation resistance and oxidation resistance of coating were tested by use of Plasma Flame and Box Resistor-Stove, respectively. The results showed that the craft applied to fabricate SiC high Temperature Ceramics coating by Argon-arc Cladding was feasible, in which SiC coatings were prepared by the mix of Si and C powerders. Compared with the coating,which was prepared by the mix of SiC and Si powerders. Complete chemical reaction of pre-coating occurred in the composition design of n（SiC）:n（Si）=1:0.5 which formed the dense uniform organization of SiC under welding current 135A and the same other processing parameters. Perfect bond quality between coating and substrate was proved by using SEM in each design sysytem. XRD showed that each coating contained newly formedβ-SiC.The formation of SiC coating growth mechanism ofβ-SiC is proposed. SiC in the coating raw materials sublimate to the level of gaseous C-Si atoms as the source, under high temperature of Argon-arc. Si powder in the coating raw materials show liquid in the role of the Argon-arc, wet and spread in the graphite matrix, reactive formate the most easily nucleatedβ-SiC with C atoms in the graphite matrix. The newly formed SiC played a role in seed crystal. The gas of sublimated C-Si atoms also enter into the graphite matrix, under the Argon-arc to achieve epitaxial growth in theβ-SiC.The introduction of coating improved ablation resistance and oxidation resistance of pure carbon materials. Mass loss rate of Graphite materials with protective coating under the composition design of n（SiC）:n（Si）=1:0.5 was 10.5mg/s, about 1/2 that of graphite substrate. The rate of mass change per unit area of the coating is just 0.7×10-3mg/（mm2h）, in air for 10h at 1400℃, under the composition design of n（SiC）:n（Si）=1:0.8, is much less than The rate of mass change per unit area of graphite, -3.75mg/（mm2h） in air for 12h at 800℃. During ablation or oxidation process, SiC changed into SiO2 which formed a self-healing protective layer. Thus the introduction of SiC could strongly improve ablation resistance and oxidation resistance of the graphite matrix.The passive oxidation mechanism of the SiC coating is proposed. The coating layer formed SiO2 oxide film which was thin, dense, combined strongly to matrix at high temperatures. The diffusion coefficient of oxygen in the coating the very small. Therefore, SiC coating is very slow oxidated.

Related Dissertations

  1. A Moledular Dynamics Simulation Study of Effects of Temperature on Epitaxial Growth in Cu-Ni Thin Flim,O611.3
  2. Study of Titanium-modified Phenolic Resins,TQ323.1
  3. Argon-arc Clad Injection Diamond Surface Composite Coating,TG174.44
  4. Research on Wear Mechanism and Resistant Measures of CFB Boiler,TK228
  5. The Investigation on the Microstructure and Properties of In-situ Synthesis TiC Particulate Reinforce Ni60A Composite Coatings by Argon Arc Cladding,TG174.4
  6. The Investigation on the Microstructure and Wear Mechanism of In-situ Synthesis TiC-TiB2 Particulates Reinforce Metal-matrix Composite Coatings by Gas Tungsten Arc Cladding,TG174.44
  7. Study on Heat-resistant Property of Ti-based Ti5Si3 Layers Prepared by Argon Arc Cladding,TG174.4
  8. Study on In-situ Particulate Reinforced Ni-based Composite Coating by Argon Arc Cladding,TG174.44
  9. Preparation and Doping of Wide Band Gap Cubic Boron Nitride Films,TB383.2
  10. The Ordered Structure of FCC Alloy Thin Film Tailored by the Epitaxial Growth Kinetics,O484.1
  11. Preparation and Properties of Aluminophosphate Molecular Sieve Films,O613
  12. Research on the Structure and Properties of YBCO Thin Films by the TFA-MOD Process,TB383.2
  13. The Preparation and Characterization of the Mesoporous Zeolite Membranes,O611.4
  14. Low pressure chemical vapor epitaxial growth of micro - structural properties of SiC thin films Research,O484.1
  15. Simulation Studies on the Film Nucleation and Growth Kinetics in the Submonolayer Regime,O484.1
  16. Strain and Electric Field Effects on Adsorption Energetics and Structures on Si Surfaces,O472.1
  17. The Growth and Homogeneity of 3-Inch Double-Sided YBCO Thin Films,TB383
  18. Experimental and theoretical studies of advanced CMOS high-k gate dielectric,TN43
  19. Boron Nitride Nanotubes Preparation and Properties of Materials,TB383.1
  20. Thermoelectric Nanomaterials Synthesis and Physical Properties of Liquid,TB383.1

CLC: > Industrial Technology > Metallurgy and Metal Craft > Metallurgy and Heat Treatment > Metal corrosion protection,metal surface treatment > Corrosion control and protection > Metal surface protection technology > Inorganic complex layer of protection > Ceramic stratified
© 2012 www.DissertationTopic.Net  Mobile