Scale Clean and Inhibition of Heat Exchanger in Sulfate Titanium Dioxide Process

Author: LiZhiYun
Tutor: XiangBin
School: Chongqing University
Course: Physical and chemical
Keywords: Titanium dioxide Heat exchanger cleaning Corrosion inhibition Scale inhibitor Anti-scaling with DC electrostatic field
CLC: TQ621.12
Type: Master's thesis
Year: 2011
Downloads: 47
Quote: 0
Read: Download Dissertation

Abstract


Titanium dioxide is one of the most important chemical raw materials at home and abroad. In hydrate-sulfuric titanium dioxide process,the problem that the heat exchanger was easily scaled and blocked had restricted the development of the hydrate-sulfuric titanium dioxide process,which caused the prombles of uncontinuous production and the negative influence on equipment service life.The sample of heat exchanger dirty obtained from certain factory was evaluated with chemical analysis, X-ray Fluorescence (XRF), X-ray diffraction ( XRD),and so on. The results indicated that the main ingredients of scale sample were calcium sulfate, mixed with some compounds of titanium and iron.Descaling by pickling the scale with hydrochloric acid after soaking with carbonate proved that the best parameters of descaling is as follows: graphite heat exchanger tube soaked in the 12%~14% sodium carbonate solution at the constant temperature 60℃for 5 hours, then soaked with hydrochloric acid for 10 minutes, the removal efficiency is more than 95%. Scale of copper exchanger soaked in the 14% sodium carbonate solution at the constant temperature 60℃for 24 hours,then soaked with hydrochloric acid for 10 minutes, repeated the above procedures for 3 times, at last the average removal rate of the scale is more than 69%. The corrosion inhibition of copper exchanger in hydrochloric acid was studied, too. Results show that the corrosion inhibition efficiency is more than 89% when the thiourea concentration is 0.01M. The corrosion inhibition efficiency is a little increased when sodium hexametaphosphate and thiourea was formulated, and the highest inhibition efficiency is about 93% with concentration ratio of sodium hexametaphosphate to thiourea equaling to 1:3,which meets the requirement of copper exchanger cleaning.Scale inhibitor containing functional groups of phosphonic acid, carboxyl acid and sulfonic acid was synthetised. The Anti-scaling rate is 75% when the addition of above mentioned scale inhibitor is 4ml/250ml. Besides,the influence and scale inhibition effect of direct current (DC) electrostatic field on the precipitation of the scale was studied and the results as follows:the anti-scaling rate is less than 3% with 36V DC voltage,but between 30 to 40 percent with 1300V DC voltage.

Related Dissertations

  1. Studies on Synthesis, Characterization and Properties of Fe-V Co-doped TiO2 Catalyst,O614.411
  2. Characterization and mechanism of the titanium dioxide surface envelope,TQ621.12
  3. Iron, lanthanum -doped nano TiO \u003csub\u003e 2 \u003c/ sub\u003e Preparation and photocatalytic properties,O614.411
  4. Stuy of TiO2 Powder and Films Prepared by Sol-Gel Method,TB383.3
  5. Preparation of Zeolite Doping Nano-TiO2 and Research of the Photocatalytic Properties,TB383.1
  6. Typical odor substances in raw water Photocatalytic Degradation,O643.32
  7. DJ Group Expansion into High-grade Titanium Dioxide Project Management of Safety,F426.3
  8. Modification of high titanium slag leaching of acid hydrolysis,TF823
  9. Research Capability of Composite Scaling-corrosion Inhibitor,TQ085.4
  10. Scale Inhibitor Containing Fluorescent Naphthalene Units Used in Seawater, the Preparation and Performance Thereof,P747
  11. Photocatalytic Degradation of Humicaid by Nano TiO2 Codoped with Fe and I2,X703
  12. A Study on Anticorrosion and Scale Inhibition Slowness Release Technology in Oily Sewage of Alkali-Surfactant-Polymer Flooding,TE983
  13. Synthesis and Evaluation of High-performance Scale Inhibitor Used in Oilfield,TE39
  14. Controllable Synthesis of Titania Nanospheres with Hierarchical Structures and Research on Their Performances,TB383.1
  15. High Weatherability Titania Preparation Techinique and pH Control Method of Aqueous Suspension,TQ621.12
  16. Synthesis and Properties of Polyepoxysuccinic Acid,TQ317
  17. Studies on the Electrochemical Sensing Properties and Analytical Applications of Mesoporous Oxide and Nano-oxide Modified Electrodes,TB383.1
  18. Synthesis and Performance of Itaconic Acid-Styrene Sulfonic Sodium-Maleic Anhydride Inhibitor,TQ085.4
  19. Study on Preparation and Performances of WO3-TiO2 Electrochromic Materials and Devices,TB34
  20. Study on the Preparation and Properties of Doped and Co-Doped TiO2,O614.411
  21. Study on Preparation and Characterization of Metal Modified Titanium Dioxide Nanotube and Its Photoelectric Performance,TB383.1

CLC: > Industrial Technology > Chemical Industry > Pigment Industry > Achromatic pigments > White pigment > Titanium dioxide,calcium titanium dioxide
© 2012 www.DissertationTopic.Net  Mobile