Study on the Preparation and Heat Treatment of Al-Al2O3 Composite Coating

Author: ShiXiaoJuan
Tutor: LingGuoPing
School: Zhejiang University
Course: Materials Science and Engineering
Keywords: Electro-codeposition room temperature ionic liquid heat treatment influence of particles
CLC: TG174.4
Type: Master's thesis
Year: 2011
Downloads: 39
Quote: 0
Read: Download Dissertation

Abstract


Although particulate reinforced metal matrix composites attract more attention due to their improved physical and mechanical properties, both the complexity of the production and high cost restrict its application. In many cases, the cheap material coated by metal matrix composite coating can work like bulk metal matrix composite material. This can save expensive resources at the same time reduce the cost. Electrochemical codeposition is an appropriate technique to easily fabricate composite coatings on substrates with various shapes at low cost. At present, the study on codeposition of metal and particles still widely use aqueous solution as electrolyte. This restricts the codeposition of metal that can not be electrodeposited from aqueous solution and particles.In this study, Al-Al2O3 composite coating was prepared successfully from acid AlCl3-1-ethyl-3-methylimidazolium chloride (EMIC) with 2:1 in molar ratio containing 0-50g/L Al2O3 particles. The deposition was conducted under galvanostatic mode. Influences of Al2O3 codeposition on Al deposit were analyzed by XRD, SEM and so on. Al2O3 particles can achieve stable dispersion in AICl3-EMIC with 2:1 in molar ratio. Content of Al2O3 in composite coating first increases and latter reduces owe to the agglomeration of Al2O3 with the increasement of Al2O3 concentration in electrolyte. Preferred (200) crystallographic orientation of deposited Al is strengthened due to the codeposition of Al2O3. As a result, composite coating appears flat and smooth. Crystallite size of Al in the coating decreases with Al2O3 concentration in electrolyte. Microhardness of composite coating is improved due to the cooperation of Al2O3 dispersion strengthening and Al grain refinement strengthening. In addition, the codeposition of Al2l3 leads to the lattice distortion of deposited Al and reduces the deposition rate of Al.The heat treatment results suggested that Al2O3 particles can impede the diffusion of Al at temperature that is whether higher or lower than melting point of Al. At 670℃, that Al2O3 particles can impede the diffusion of Al atoms is because they decrease the activity of some Al atoms. Despite that composite coating would diffuse into substrate completely with increasing heat time. By contrast, at 600℃, that Al2O3 particles can impede the diffusion of Al atoms is because they gather on the interface of original coating and alloy layer:when Al diffuses into 1Cr17, Al2O3 left would gather on the interface of coating and alloy layer, which would impede the diffusion of Al more effectively. Moreover, there would be more and more Al2O3 gathering on the interface with the diffusion of Al into 1Cr17 and finally would form AlO3-rich layer. Therefore, the diffusion of Al becomes more and harder with the conduct of heat treatment.

Related Dissertations

  1. Study on Key Technology and Its Physiological Basis of Virus Elimination and Rapid Propagation of Phalaenopsis,S682.31
  2. Study on the Subsurface Crack of Supporting Roller Made of Austempered Ductile Iron,TG156.3
  3. The Design and Implementation of Control System for Wire-steel Heat Treatment Direct-fired Furnace,TP273
  4. Study on Process Method and Parameter Optimization of the Remained-heat Treatment of Marine Heavy Forgings,TG316
  5. Study on the Spinnability of Semi-Aromatic Polyamide,TQ340.1
  6. Study on Synthesis and Modified of LiFePO4 as Cathode Materials,TM912
  7. 316LN austenitic stainless steel stress corrosion cracking of welded joints,TG407
  8. Influence of Heat Treatment on Nickel-base Single Crystal Superalloy Containing Re,TG166
  9. Machining complex manufacturing systems - heat integrated scheduling method,TH186
  10. Heat Treatment of Cast Al-Cu-Ti-(La) alloy microstructure and mechanical properties of,TG166.3
  11. Liquid Forging hypereutectic Al-Si alloy microstructure and properties,TG319
  12. Semi-solid / hot extruded hypereutectic Al-Fe alloy heat Mechanism,TG166.3
  13. Hot extruded Mg-Zn-Zr-Gd alloy microstructure and mechanical properties,TG379
  14. GH4169G alloy creep behavior of the organizational structure and,TG146
  15. Mg-Zn alloy microstructure and mechanical properties,TG146.22
  16. Mg-Si alloy sheet Sc on Microstructure and Properties,TG146.2
  17. Ultrasonic deposition of spray forming blank Quality,TF124.39
  18. A508-3 nuclear power transformation plasticity of steel forgings and Numerical Simulation,TL341
  19. 40Cr steel solid research Boronizing,TG156.87
  20. ZG06Cr13Ni4Mo Steel Heat Treatment on Microstructure and Properties of,TG161
  21. ZA35 alloy elements Zr on Microstructure and Properties,TG131

CLC: > Industrial Technology > Metallurgy and Metal Craft > Metallurgy and Heat Treatment > Metal corrosion protection,metal surface treatment > Corrosion control and protection > Metal surface protection technology
© 2012 www.DissertationTopic.Net  Mobile