FePt Films Fabricated by Electrodeposition

Author: ShiShiYi
Tutor: DuXueYan
School: Lanzhou University of Technology
Course: Materials Physics and Chemistry
Keywords: L10 phase FePt electrodeposition FePt codeposition films Fe/Pt multilayers magnetic property
CLC: O611.4
Type: Master's thesis
Year: 2011
Downloads: 25
Quote: 0
Read: Download Dissertation

Abstract


FePt codeposition films and Fe/Pt multilayers were prepared via an electrodeposition process in Na2SO4 solution, where FeSO4·7H2O and H2PtCl6·6H2O solution were used as Fe2+source and Pt4+source, respectively. XRD、SEM、EDX and VSM were used to characterize the morphology and magnetic properties of FePt codeposition films and Fe/Pt multilayers before and after annealing. The detailed researches were given as follows:（1） FePt codeposition films were prepared on pure Cu substrate on condition that the potential changed from -1V to -6V. Fe content increases and Pt content reduces with the decrease of the potential. FePt codeposition film,where the Fe/Pt ratio was close to 1:1,was prepared at the potential of -4.7V. It can be seen from SEM photos that the grain size of the films have relationship with potential. The grain of -4.7V film is uniform and compact, and the surface is smooth,but O content reached to the top,while O content of Fe rich films and Pt rich films is low. Annealed at 550°C for 30 min under H2 atmosphere, the coercivity and saturation magnetization of the as-prepared FePt film increased from 2.19kA/m to 12.5kA/m, and from 408.6kA/m to 456.3kA/m, respectively.（2） According to the results of FePt codeposition films,-4V,-5V,-6V were chosen as Fe rich layer potential and -2V,-3V,-4V were chosen as Pt rich layer potential. The Fe/Pt multilayers were obtained through the deposits of Fe and Pt reduplicatively.This paper investigated potentials、deposition time、substrates and etc which have effects on Fe/Pt multilayer preparation.The results shows that: When Pt rich layer potential was fixed and Fe rich layer potential was different or Fe rich layer potential was fixed and Pt rich layer potential was different,the multilayers have distinction on the morphology because of the difference of current density,and there is some regularity on the composition of the multilayers.Fe/Pt multilayers which have ideal composition were chosen and annealed at 550°C for 30 min under H2 atmosphere. After annealing,O is reduced,and Fe、Pt content are improved respectively, grain size of the multilayers is bigger, the coercivity and saturation magnetization of the films are greatly increased.Fe/Pt multilayer（t-2V=12min, t-6V=8min, 2 cycles）has a clear sight of layers.The morphology of this film is fine compared to Fe/Pt multilayers of other deposition time.The adhesion of Fe/Pt multilayer deposited on the conductive glass substrate is less than pure Cu,and the film on glass has a less compact morphology.

Related Dissertations

  1. A Study on the Electrodeposition of Zn-Co and Zn-Ni Alloys in the Reline Room Temperature Ionic Liquid,TQ153.1
  2. Methyl sulfonate system tin plating additives and process,TQ153.13
  3. Preparation of Electrode by Electrodeposition and Study on Performance of Degradation Phenol Wastewater,X703
  4. Syntheses, Structures and Properties of Transition Metal Complexes Based on Pyridyl Ligands,O627.2
  5. The Preparation and Application of Amorphous Carbon Nanoparticles and Composite Materials,TB383.1
  6. Synthesis and properties of self-cross -linked acrylic resin,TQ325
  7. Electrodeposition La-Mg-Ni Alloys,TG139.7
  8. Electrodeposited Pt Electrode Preparation and Electrocatalytic oxidation of ammonia,O643.3
  9. Study of the Annealing Treatments of Electrodeposited CuInSe2 and Cu（In,Ga）Se2 Thin Films,TB43
  10. Influence of Silane Treatment on the Surface of Co-Cr Alloy about the Anticorrosive Property,R783
  11. Research on Automatic Temperature Control System of Drying Room of Cathode Electrophoresis Coating Line Based on Fuzzy PID Control,TP273
  12. Fluorescence Determination of DNA and Electrochemical Behaviors of Based,Q523
  13. Eutectic ionic liquid solvent-based system to take the study of metallic zinc from zinc oxide,TF813
  14. Nanocomposite Coatings pulse electrodeposition preparation process and performance,TG174.4
  15. Prepared by pulsed electrodeposition Ti-based the lead composite electrode material and performance,TG174.4
  16. Preparation and Microstructure of Nano-crystalline Zn-Ni Alloy by Jet Electrodeposition,TG174.4
  17. Preparation , Structure and Properties of electrodeposited Ni - W alloy coating,TQ153.2
  18. Pulse electrodeposited nickel alloy Process,TQ153
  19. Study of Non-Cyanide Gold Plating Process Using Hydantoin as Complexing Agent,TQ153.1
  20. Study on New Electrodeposition Processes of Aluminum Alloys and Stainless Steel,TQ153
  21. Study on Belt-type ZnO Photoanode for Dye-sensitized and Quantum-dot Sensitized Solar Cells,TM914.4

CLC: > Mathematical sciences and chemical > Chemistry > Inorganic Chemistry > Chemical elements and inorganic compounds > Inorganic synthetic chemistry
© 2012 www.DissertationTopic.Net  Mobile