|
Bamboo restructuring in the 1990s began to study material of new products. In recent years, with the increase of bamboo recombinant material type, bamboo utilization continues to improve and continue to improve the physicochemical properties of materials, bamboo recombinant materials more and more people attention. But most of the bamboo materials are restructuring to large diameter grade bamboo as raw material, which accounted for a majority of the dwarf bamboo resources have not yet been fully utilized effectively. Fibrosis bamboo veneer scrimber reorganization as a new structural material of bamboo, its development and application, so that large-scale industrialization path miscellaneous bamboo utilization become a reality. Fibrosis Fibrosis bamboo veneer bamboo veneer material using recombinant manufacturing technology, breaking the traditional method for preparing bamboo plywood unit, do not deliberately remove mingled and Shiraia, once the bamboo utilization rate increased to 90% -95 %, and also so that the original can not take advantage of dwarf bamboo resources are efficiently utilized. In addition, the ease of the process of bamboo, the bamboo fiber to avoid damage problem bamboo fiber retains the characteristics of high strength, given the high physical and mechanical properties of plates. Bamboo veneer scrimber fibrosis can not only be used for indoor decoration decoration materials, container floor, etc., but can also be used for wind turbine blades blade material high strength materials and outdoor high durability flooring material. In this study affinis (Neosinocalamus affinis (Rendle) Keng f.), Bamboo (Phyllostachys arcana McClure), red shell bamboo (Phyllostachys iridescens CY Yao et CY Chen), a small bamboo (Phyllostachys edulis (Carr.) H. de Lehaie ), white clip bamboo, bamboo Shou, pervariabilis bamboo bamboo as the main raw material for different adhesive impregnation amount and the different treatment of the basic unit of bamboo exploratory trial design, influence of different process conditions on board the main physical and mechanical the impact of performance and water resistance, and ultimately through the analysis produced under different experimental conditions of the plate thickness swelling, tensile strength, compressive strength, bending strength and elastic modulus and other performance indicators, and fibrosis bamboo veneer scrimber and bamboo timber, bamboo reorganization, A grade bamboo strips laminated timber physical and mechanical properties were compared, concluded fibrosis bamboo veneer scrimber excellent performance, is a sustainable development of new materials, and its development bamboo plywood and applications will enhance the development and utilization of bamboo has a positive meaning. In this study, the following conclusions: 1) the type of adhesive impregnation amount: the amount of repression fibrosis different adhesive impregnated bamboo laminated veneer lumber properties are as follows: Dipped Capacity: 7%, density: 1.12 g/cm3 , bending strength (MOR): 253.2MPa, modulus of elasticity (MOE): 26.3GPa, 100 ℃ 28h cycle boiled water resistance: water width expansion (WS): 3.83%, thickness swelling (TS): 9.83 %; dipping amount: 13%, density: 1.12 g/cm3, bending strength: 246.9MPa, elastic modulus: 26.3GPa, 100 ℃ 28h cycle boiled water resistance: WS: 2.73%, TS: 5.15%. The results show that: with dip increases, the tensile strength of the sheet and MOR tendency to decrease; reduced tensile strength of 18.68%; horizontal shear strength show opposite trends; MOE and compressive strength did not change significantly. Water resistance tests include the sheet resistance and temperature resistance, boiling water blisters, both impregnated with the increase and showed an increasing trend. 2) basic unit processing modes: Bamboo Veneer fibrosis were ease 3,4,5,6,7 times. The results show that: with the increase in the number of passes ease, fibrosis bamboo laminated veneer lumber of MOR showed a gradual upward trend; MOE first increased and then decreased; ease the number of times with water resistance increased with the increase; resistance compressive strength with ease the increase of the number of passes; tensile strength with ease and reduce the increase of the number of passes. 3) exploratory trials in different bamboo species as raw material, suppress fibrosis bamboo laminated veneer lumber, including: bamboo, red shell bamboo, bamboo white clip, Shou bamboo, small bamboo, etc., prepared plates and excellent performance. Exploratory test success for the development of bamboo plywood to provide a broader source of raw materials. 4) developed to fibrosis bamboo veneer bamboo as the basic unit of cement template, exploratory experiment showed that the overall quality of bamboo and cement template with higher added value, with strong market competitiveness and broad market prospects.
|