Research on the Composite Coating Combining Micro-arc Oxidation with Sol-gel on the Surface of Magnesium Alloy

Author: BinYuanHong
Tutor: LiuYing
School: Jinan University
Course: Materials Science
Keywords: magnesium alloy micro-arc oxidation sol-gel corrosion resistance
CLC: TG174.4
Type: Master's thesis
Year: 2011
Downloads: 135
Quote: 0
Read: Download Dissertation

Abstract


Micro-arc oxidation (MAO) coatings were successfully prepared on ZE10 magnesium alloy by micro-arc oxidation in silicates electrolyte system. The effects of voltage, oxidation time, frequency and duty ratio on the thickness, morphology and corrosion resistance of the micro-arc oxidation coatings were investigated by using eddy current thickness measuring gauge, X-ray diffraction, scanning electron microscopy, energy disperse spectroscopy (EDS) and electrochemical workstation, etc. In order to realize the better corrosion resistance, the rare earth was added in the silicates electrolyte and the coating, and sealing treatment by using SiO2 sol was performed respectively, and the thickness, morphology and corrosion resistance of the micro-arc oxidation coatings were discussed.The results indicated that the thickness and hole of MAO coatings was increased with anode voltage increasing from 200V to 350V. The thickness is increased obviously with increasing in the oxidation time in the beginning and basically stable after 20 minutes. Frequency and duty ratio has little effect on the film thickness, smaller pore size obtained at a high-frequency. The corrosion resistance of MAO coatings increase firstly, then decrease with the applied voltage and time increasing; and duty ratio and frequecy are little influential factors of the corrosion resistance of MAO coatings.The coating formed contained three layers, outer loose layer, middle compact layer, inner transitional layer. XRD and EDS show that the MAO coatings are mostly composed of MgO, MgF2, Mg2SiO4.The experiment of different methods addition of rare earth element for MAO show that the Ce element addition in electrolyte and the pre-treatment of rare earth Ce conversion coating can reduce the thickness and cracks, raise density and further improve the corrosion resistance of coating. The least cracks and highest density and best corrosion resistance appeared in the micro-arc oxidation coating as the pre-treatment of rare earth Ce conversion coating was performed and Ce element was added in the electrolyte.Silica sol was prepared using TEOS as the precursor and HNO3 as the catalyst by alkoxide solution. SiO2 sol-gel film was prepared on the surface of MAO coating by dip-coating method and spin-coating method. The results show that dip-coating and spin-coating can be spread uniform on MAO coating surface, sol can enter into the hole of MAO coating and seal the hole effectively. The hole-sealed treatment can further improve the corrosion resistance of MAO coating of magnesium alloy, and dip-coating method is better than spin-coating method.

Related Dissertations

  1. Preparation and Photocatalytic Properties for Water Decomposition of Titanate Photocatalyst,O643.36
  2. Preparation of ITO Quai-1D Nanostructures by Sol-Gel Method Combined with Porous Anodic Aluminum Oxide Template,TB383.1
  3. Study on the Synthesis Bi3.25La0.75Ti3O12（BLT） Nanotubes and Nano Wires,TB383.1
  4. Preparation of Micro-Arc Oxidation Ceramic Coating on Mg Alloy and the Research of Galvanic Corrosion,TG174.453
  5. Microstructure and Mechanical Properties of Mg-Zn-Y-Zr Alloys,TG146.22
  6. Preparation and Electrocaloric Effect of BaxSr1-xTiO3 Ferroelectric Thin Films,TB383.2
  7. Preparation and Performance of V2O5-WO3/MOx/Cordierite Catalyst Modified with Cu、Mn、Ce for DeNOx,X701
  8. Iron, lanthanum -doped nano TiO \u003csub\u003e 2 \u003c/ sub\u003e Preparation and photocatalytic properties,O614.411
  9. Research on Electrochemical Synthesis and Application of Conductive Polyaniline,O633.21
  10. Cobalt Ferrite and Its Performance,O611.4
  11. Preparation of Silica Hollow Spheres with Mesopores in the Walls,TB383.1
  12. Fabrications and Applications of Microelectrode Array of Silicon Dioxide Cavities and Magnetic Ferroferric Oxide Nano-Bioconjunctions,TB383.1
  13. Study on Preparation and Properties of Polyimide/SiO2 Hybrid Films,TB383.2
  14. The Research on Extrusion Parameters Through the Plate Billet of Magnesium Alloy,TG379
  15. Preparation of Titania Photocatalyst Supported on Carbon Fiber and Its Photocatalytic Activity under Visible Light,O643.36
  16. Synthesis of N-doped ZnO Nanorods by Sol-gel and the Study of Its Capability,TB383.1
  17. Synthesis and Characterization of Low-dimensional Nickel Borate/ Lanthanum Borate Nano Materials,TB383.1
  18. Preparation and Characterization of Proton Exchange Membrane of Phosphate Acid Doped Polybenzimidazole by Sol-Gel Method,TM911.4
  19. The Research on Rolling and Heat Treatment Technology of AZ31 Magnesium Alloy Thin Sheet,TG166.4
  20. New Grain Refiners and Their Refining Behaviors of AZ31 Magnesium Alloy,TG146.22
  21. Study of the Preparation and Properties of the Trivalent Chromium Black Passivation with Non-cobalt Sulfate System,TG174.4

CLC: > Industrial Technology > Metallurgy and Metal Craft > Metallurgy and Heat Treatment > Metal corrosion protection,metal surface treatment > Corrosion control and protection > Metal surface protection technology
© 2012 www.DissertationTopic.Net  Mobile