Study on the Reaction Milling of Cu-H2O Binary System and Cu-Cl-H2O Ternary System

Author: NiSong
Tutor: ChenZhenHua；ChenDing
School: Hunan University
Course: Materials Processing Engineering
Keywords: Mechanochemistry High-energy ball milling Cuprous oxide Chloride ion
CLC: TB383.1
Type: Master's thesis
Year: 2008
Downloads: 25
Quote: 0
Read: Download Dissertation

Abstract


Based on the principle of mechanochemistry, nanosized oxides and H2 as the side product can be obtained by ball milling metal powders (Zn, Mn etc.) in water solution using high-energy ball mill. The metal powders used rank before H in the list of metal activity sequence. However, the study on ball milling metal powders which rank after H in water solution is not available. The Cu powder which ranks after H was selected as the raw material in this experiment to study the phenomenon and principles of Cu-H2O binary and Cu-Cl-H2O trinary reaction ball milling. XRD、SEM and TEM were employed to examine the phase composition、microstructure of the final products. The experimental results were as follows:(1) By ball milling Cu powder in pure distilled water solution, Cu2O was formed by the reaction between Cu and oxygen which was dissolved in water. But the amount of Cu2O was quite limited due to the limited amount of oxygen in the ball milling system. While in the results of mechanical alloying, the reaction between Cu and oxygen was hard to occur, little amount of Cu2O was gained after 110h ball milling, which was less than in the former experiment.(2) By ball milling Cu powder in distilled water solution with a high oxygen pressure, the reaction between Cu powder and oxygen would be activated continuously. The Cu powder can be oxidized to CuO completely due to the sufficient oxygen in system. The pure CuO obtained after 110h ball milling was uniform with the particle size of 100-200nm.(3) By ball milling Cu powder in HCl solution with pH value of 2, a large amount of Cu2O was obtained after 3h milling, together with a little amount of Cu2(OH)3Cl and CuCl. While high purity Cu2O was formed after 70h milling. No other phases were examined. The particle size of Cu2O was 50-100nm.(4) Ball milling Cu powder in CuCl2 solution with [Cl-] of 1.5×10-2mol/L and 7.5×10-2mol/L, complete Cu2O were gained after 25h and 80h milling respectively. Most of the particles were cubic or hexagonal in shape and 50-150nm in size. When the [Cl-] was adjusted to 0.3mol/L, the milling time needed for forming pure Cu2O was 100h. And the particles were apparently larger in size and more abnormal in shape than the former results. When the [Cl-] reached 0.75×10-2mol/L and 0.3×10-2mol/L, pure Cu2O was hard to form in a certain period. It can be concluded that different concentration of Chloride ion would affect the reactions in different milling periods, the needed time for forming pure Cu2O and the size、shape of Cu2O particles.(5) A large amount of Cu2O was obtained after 80h ball milling CuCl in water solution. Most of the Cu2O particles were abnomal in shape and 20-80nm in size. There were also partial particles of cubic and hexagonal shapes.

Related Dissertations

  1. Analysis of Concrete Durability under Combined Action of Freeze-thaw Cycles and Chloride Ion Erosion,TU528
  2. Dairy cow recessive mastitis Occurrence,S858.23
  3. Preparation of Adsorption Nano-material and Its Application in Disposing Dye Waste Water,TB383.1
  4. Study on the Effect of Chloride Ions on the Corrosion Behavior of Reinforing Steel and Corrosion Inhibitors,TG174.42
  5. Discovery and Pharmacological Characterization of Natural Small Molecule Activators of Wildtype and Mutant CFTR Chloride Channels,R285
  6. Design and Implementation of Portable Concrete Permeability Analyzer,TU528
  7. Ultrafine grain growth inhibitors on WC-Co Cemented Carbide,TG135.5
  8. Cuprous Oxide of Micro-nano Structures: Preparation and Characterization,TB383.1
  9. Loads and chloride ions reinforced concrete beams under the law of degradation,TU375
  10. Preparation and Electrochemical Characterization of Porous Novel Materials Composed by Copper and Cuprous Oxides,O614.121
  11. Experimental Study on High-flowing Concrete with Ground Fine Fluidized Bed Combustion Ashes,TU528
  12. Effect of Geopolymer Concrete’s Durability by Oxide Composition,TU528
  13. Preparation of Metail Oxide Semiconductor by Wet Chemical Methods,TN304.21
  14. Mineral admixtures on permeability of concrete research,TU528.041
  15. Effect of Coarse Aggregate Shape on the Physicomechanical Properties of Concrete,TU528
  16. Load and concrete structures under chloride environment Corrosion Study,TU375
  17. The Research of the Effect of One-way Load、Freezing-Thawing Cyclcs and Curing Age on Chloride Permeability of Concrete,TU528
  18. Polypropylene Fiber Concrete Durability Test Research,TU528.572
  19. Concrete deterioration ANFIS chloride ion penetration analysis,TU528
  20. The DecaBDE light degradation and cytotoxicity assays,R114

CLC: > Industrial Technology > General industrial technology > Materials science and engineering > Special structural materials
© 2012 www.DissertationTopic.Net  Mobile