Synthesis and Characterization of Platinum Group and Their Oxide Nanoparticles by Bydrothermal Method

Author: RenYuHua
Tutor: HuangTao
School: Central South University for Nationalities
Course:
Keywords: Platinum oxide Palladium oxide Hydrothermal method Polyacrylic acid Polyvinylpyrrolidone Octadecyl dimethyl benzylammonium chloride Cetyltrimethylammoniumbromide
CLC: TB383.1
Type: Master's thesis
Year: 2011
Downloads: 41
Quote: 0
Read: Download Dissertation

Abstract


The hydrothermal syntheses of the nanoparticles of platinum group metals and their oxides were studied and the effect of reaction parameters on the sizes, morphologies and dispersions was investigated.PtO2 nanoparticles were prepared by hydrolytic condensation of H2PtCl6 in alkaline aqueous solution with cetyltrimethylammoniumbromide （CTAB） as a stabilizer in the presence of appropriate amount of NaAc by means of hydrothermal method. The products were characterized by UV-vis spectroscopy, TEM and XRD. The effects of reaction parameters on PtO2 nanoparticles were investigated. Rod-like PtO2 nanoparticles with a length of 1.5μm, a cross diameter of 0.4μm, and the aspect ratio of 3.75 were synthesized under the condition of a molar ratio of 30/3/1 of NaAc/CTAB/H2PtCl6. The formation mechanism of the rod-like PtO2 nanoparticles was explored preliminarily.The hydrothermal synthesis of PdO nanoparticles was studied by hydrolytic condensation of H2PdCl4 with PAA as a stabilizer in alkaline environment and the products were characterized by UV-vis spectroscopy, TEM and XRD. The effects of the temperature, the amount of PAA and NaOH on PdO nanoparticles were investigated. PdO nanoparticles with some morphologic aspect were synthesized at 100°C for 10h under the condition of a molar ratio of 40/15/1 of PAA/NaOH/H2PdCl4 and the average diameter was about 9.1nm.The PtO2 nanoparticles were synthezed with hydrolytic condensation of H2PtCl6 in the presence of PVP and CTAB by means of hydrothermal method. The products were characterized by UV-vis spectroscopy, TEM, XRD and XPS. The effects of CTAB, NaOH and PVP on the preparation of PtO2 nanoparticles were investigated. The results showed that ball-chain PtO2 nanoparticles with uniform size, well dispersion and an average diameter of 40.8 nm were obtained at 120°C for 6 h under the condition of a molar ratio of 1/5/12/100 of H2PtCl6/CTAB/NaOH/PVP.Without any reducing agent, the Pd nanoparticles was synthesized with octadecyl dimethyl benzylammonium chloride （1827） as a stabilizer by decomposition of H2PdCl4 via a hydrothermal route. The products were characterized by UV-vis spectroscopy, TEM and XRD. The effects of the reaction time, the amount of 1827 and KOH on Pd nanoparticles were investigated. Polyhedral Pd nanoparticles with an average diameter of 26.5 nm were obtained at 160°C for 10 h under the condition of a molar ratio of 10/4/1 of 1827/KOH/H2PdCl4.

Related Dissertations

  1. Study on the Preparation and Properties of Fabric Luminous Coating,TS195.5
  2. Strain-selecting and Extraction of Jinggangmycin,TQ465
  3. Studies of Equipment and Technology of Making Alpha Hemihydrate Gypsum by Using Desulfurated Gypsum,TQ177.3
  4. Study on Preparation and Luminescence Performance of Red Phosphors Used for White-Light LED,TQ422
  5. Preparation of Functional Phosphate Ester and It’s Application in Waterborne Coatings,TQ630.79
  6. Study of Tin Alloy Carbon Composite Used for Lithium Ion Battery,TM912.9
  7. Synthesis and Characterization of Binaphthol Complexes,O621.13
  8. Synthesis of ZnS Based Nano-Luminescent Materials by Hydrothermal Method,TB383.1
  9. Effect of Cobalt Doping on the Morphology and Magnetism of ZnO Crystals,TB34
  10. Preparation of Mircon-Copper by Hydrothermal Reduction Method,TB383.1
  11. Synthesis of Indium Oxide Nanomaterials and Application for Gas Sensing,TB383.1
  12. Study on the Fabrication of PAN-Ag Composite Nanofibers and Regulation of Its Size,TB383.1
  13. The Fabrication and Characterization of SiCN Nano-fiber Ceramic Materials by Electrospinning,TB383.1
  14. Hydrothermal Synthesis and Applications of CdO2 and ZnO2 Nanoparticles,TB383.1
  15. Zinc hydrometallurgy process of separation of iron and iron resource utilization,TF813
  16. Preparation and Properties of ZnO Based Diluted Magnetic Semiconductor Materials,TN304
  17. Synthesis and Visible-Light Photocatlysis Performance Research of BiVO4 Heterostructure Photocatalysts,O643.36
  18. Synthesis and Application of Xonotlite-type Calcium Silicate Hydrates Fibers,TQ132.32
  19. Hydrothermal Synthesis and Photocatalytic Activity of Doped CeO2 Nano-Materials,TB383.1
  20. Multi-Composite Ferrite Materilas: Preparation, Structurel and Catalytic Properties,TB383.1
  21. Study on Preparation Technique of High-dispersion Nano-zirconia,TB383.1

CLC: > Industrial Technology > General industrial technology > Materials science and engineering > Special structural materials
© 2012 www.DissertationTopic.Net  Mobile