Preparation Technology and Performance Study on Ti-6A1-4V Alloy Surface Using Micro-arc Oxidation

Author: WangJingQi
Tutor: SuYong;WangJianMin
School: Hefei University of Technology
Course: Materials processing
Keywords: titanium alloy electrolyte surface morphology corrosion resistance micro-arc oxidation
CLC: TG174.4
Type: Master's thesis
Year: 2009
Downloads: 174
Quote: 1
Read: Download Dissertation

Abstract


As a novel technology of surface modification, Microarc Oxidation（MAO） has great potential and abroad application prospect. It has important application background and value in aerospace and aviation fields.In order to obtain a good oxidation coating on surface of Ti-6A1-4V alloy,NaOH、Na2SiO3 and Na2HPO4 coatings were Prepared in the corresponding electrolyte system by micro-arc oxidation （MAO） method,and the optimal MAO parameters were obtained by using direct current constant voltage electrical source. Microstructure of the coatings was characterized using XRD, SEM and EDS techniques. The formation mechanism of MAO coating was investigated. The thickness, rigidity and anti-causticity of coatings were tested. The influence of electrolyte concentration and temperature was discussed to the variational disciplinarian of sparking voltage. As the result of research as follows:When Na2HPO4 and Na2SiO3 solution were choosed as electrolytic solution, the magnitude of sparking voltage minish linearly with the hoist of electrolytic solution and initial temperature. when the concentration was very small, the adust phenomenon took place easily on the edge of nodic titanium alloy board; by contraries, sparking was found difficultly.When Na2HPO4 and Na2SiO3 solution were choosed as electrolytic solution, micro-arc oxidation coatings had the porous structure in different disposal time、electrolytic solution concentration and voltage. The rigidity、thickness、surface roughness and size of tiny hole augment of coating increased gradually, growth velocity and corrosion resistance increased primitively and then minish, but density of tiny hole decreased gradually. The results show that anatase and rutile titania on the titanium surface mostly. Anatase titania droped off and rutile titania increased gradually, which will play a leading role.The quality of oxidation film became more velveter with increase of NaF concentration. Thickness of film and rigidity increased gradually with increase of NaF concentration. Although pore size increased and the number of microporous decreased gradually, corrosion resistance increased gradually, the performance of oxidation film mentioned above two kinds of electrolyte was not the same, so the corrosion resistance of oxidation film was more better to a certain degree in NaOH solution Containing additive NaF.Through the test, the optimized working conditions are determined: electrolyte concentration is 3g/L NaOH +0.4mol/LNaF, micro-arc voltage is 280V, oxidation time is 10min in NaOH solution Containing additive NaF; electrolyte concentration is 0.3mol?L, micro-arc voltage is 180V, oxidation time is 300s, initial temperature of electrolyte is 10℃in Na2HPO4 solution; electrolyte concentration is 50g?L, micro-arc voltage is 280V, oxidation time is 50-150s, initial temperature of electrolyte is 20℃in Na2SiO3 solution; Like this, oxidation film of homogeneous pore size and good compactness can be obtained.In a word, to prepare perfect micro-arc oxidation film, interreaction of various factors must been taken into account.

Related Dissertations

  1. Preparation of Micro-Arc Oxidation Ceramic Coating on Mg Alloy and the Research of Galvanic Corrosion,TG174.453
  2. Electrochemical Performances of Mg-Li and Mg-Li-Ce Alloys,TG146.22
  3. The Evolvement of Quartzs and Phytoliths in Basalt-Derived Chronosequence Soils in Tropics Area of China,S153
  4. Research on Electrochemical Synthesis and Application of Conductive Polyaniline,O633.21
  5. Study on Corrosion Resistance and Condensation Property of Ni-P/Nano SiO2 Composite Coatings,TG174.4
  6. Preparation and Characterization of Doped Cu3N Thin Films by Magnetron Sputtering,O484.1
  7. Study on Preparation and Property of V2O5 /TiO2 Composite Film Via Microarc Oxidation,TB43
  8. Evaluation of Biocompatibility of Titanium Alloy Coating by Polyurethane,R318.08
  9. Preparation, Characterization and Performance of the Bio-coatings on the Surface of Pure Titanium Based on Micro Arc Oxidation,R318.08
  10. Guide lithium polymer electrolyte membrane preparation and application,TB383.2
  11. Research on the Electrolyte for All Vanadium Redox Flow Battery,TM912
  12. Bacterial cellulose gel lithium battery of polymer electrolyte membrane,TM912
  13. Nano- phenyl silicone resin preparation and application,TB383.1
  14. Vacuum casting AZ91 Magnesium Alloy Corrosion Resistance,TG146.22
  15. ZA35 alloy elements Zr on Microstructure and Properties,TG131
  16. Graphite anode low temperature performance influencing factors and improving research,TM912
  17. Research on the Influences of the Walter-electrolytes Metabolism of Athletes by Electrolytes Sports Drinks,R87
  18. Effect of Dentin Demineralization Processed by Solution with Ethylenediamine Tetraacetic Acid,R781.2
  19. The Effects of Acute Hypervolemic Hemodilution Combined with Intraoperative Salvage Autotransfus on Oxygenation and Homeostasis in Patients Undergoing Spinal Surgery,R614
  20. Relationship between Electrolytes and Blood Pressure in Different Nationalities Hypertension,R544.1
  21. Study on the Friction Performance of MAO Film on TC4 Titanium Alloy,TG174.451

CLC: > Industrial Technology > Metallurgy and Metal Craft > Metallurgy and Heat Treatment > Metal corrosion protection,metal surface treatment > Corrosion control and protection > Metal surface protection technology
© 2012 www.DissertationTopic.Net  Mobile