Study on Magnesium Alloy Micro-arc Oxidation Process of Zirconium Salt Solution System and the Corrosion Resistance

Author: ZhangLiNa
Tutor: HaoJianMin
School: Chang'an University
Course: Materials Processing Engineering
Keywords: Micro-arc oxidation Magnesium alloy Solution system Corrosion resistance
CLC: TG174.4
Type: Master's thesis
Year: 2009
Downloads: 168
Quote: 2
Read: Download Dissertation

Abstract


In this paper, a large number of experiments have been carried for the successful preparation of zirconium salt solution system to inspect the influence to ceramics level thickness and surface roughness of micro-arc oxidation technological parameter for zirconium salt solution system;By comparing the density of ceramics between the zirconium salt solution system and the silicic acid salt solution system, the paper indicate that the zirconium salt solution system ceramics have the better compactness, and determine the ceramics level degree of hardness to achieve above 1000HV in the zirconium salt solution system.In this paper, neutral sodium chloride immersion test and salt spray corrosion test are used to study the corrosion resistance of ceramic coating for magnesium alloy micro-arc oxidation, and the results show that the corrosion resistance of ceramic layer in the zirconium salt solution system is nearly 3 times to that in a silicate salt solution system, achieved no pitting 496h; At the same time, the best combination of process parameters are selected by the micro-arc oxidation process of magnesium alloy in zirconium salt solution as follows: current density, 2.0A/dm2; frequency, 600Hz; duty cycle , 15%.Finally, with energy spectra and XRD diffraction analysis of ceramic layer of zirconium salt solution and its component elements contained in that layer, the results show that a larger mass fraction of elements and a large proportion of zirconium zirconia phase were in existence; Contrasting with the surface of 496h salt-fog corrosion samples, we can see that the ceramic layer of zirconium salt solution erode more light with that relatively thicker, and by observing the cross-section morphology of ceramic layer, we can find that: layer ceramic of zirconium salt solution has better homogeneity and density.

Related Dissertations

  1. Preparation of Micro-Arc Oxidation Ceramic Coating on Mg Alloy and the Research of Galvanic Corrosion,TG174.453
  2. Microstructure and Mechanical Properties of Mg-Zn-Y-Zr Alloys,TG146.22
  3. Research on Electrochemical Synthesis and Application of Conductive Polyaniline,O633.21
  4. Investigate of Chromate Conversion Coatings on Aluminum Alloy,TG174.4
  5. Surface Modification of Al-alloy for Improving Bonding Strength with Pps and the Corrosion Resistance of Al-alloy,TG174.4
  6. The Research on Extrusion Parameters Through the Plate Billet of Magnesium Alloy,TG379
  7. The Research on Rolling and Heat Treatment Technology of AZ31 Magnesium Alloy Thin Sheet,TG166.4
  8. New Grain Refiners and Their Refining Behaviors of AZ31 Magnesium Alloy,TG146.22
  9. Study of the Preparation and Properties of the Trivalent Chromium Black Passivation with Non-cobalt Sulfate System,TG174.4
  10. Study on Chemical Coloring and Sealing Processing of Stainless Steel,TG177
  11. Preparation and Properties of Reactive Thermal Sprayed Ternary Boride Cermet Coatings,TG174.4
  12. Study on the Preparation and Properties of Composite Ceramic Coating on AZ31B Alloy by Thermal Spraying,TG174.44
  13. Study on Preparation Technology and Properties of Al2O3-TiB2 Solid-state Reaction Multiphase Ceramic Coating on AZ31B Alloy,TG174.44
  14. Prepaation of Hybrid Membrane on Carbon Steel and Anti-corrosion Properties Research,TG174.4
  15. The Comparative Study on Ni-P and Ni-Ce/W-P Electroless Plating and Coating Performance on 27SiMn Steel,TQ153.12
  16. Effects of the Asymmetric Pulse Parameters of Power and TiO2 Sol on Micro-arc Oxidation of AZ91D Magnesium Alloy,TG174.44
  17. Fabrication of Biologic Magnesium Alloy Foil and Stand on Its Anti-corrosion Performance,TG146.22
  18. Study on Preparation and Property of V2O5 /TiO2 Composite Film Via Microarc Oxidation,TB43
  19. Study on the Formability of Magnesium Alloy AZ61 and Its Hot Forming Process for Bevel Gear,TG319
  20. The Research of Fluidity and Hot Tearing for Cast NZ30K Mg Alloy,TG292
  21. Research about Synthesis and Application of Magnesium Borate and Aluminum Borate Nanowiskers,TB383.1

CLC: > Industrial Technology > Metallurgy and Metal Craft > Metallurgy and Heat Treatment > Metal corrosion protection,metal surface treatment > Corrosion control and protection > Metal surface protection technology
© 2012 www.DissertationTopic.Net  Mobile