The Research of the Heat Treatment of the Low-alloy High Strength Steel

Author: LiuKai
Tutor: WuKaiMing
School: Wuhan University of Science and Technology
Course: Materials Science
Keywords: wear-resistant steel martensite bainite heat treatment quenching
CLC: TG161
Type: Master's thesis
Year: 2009
Downloads: 710
Quote: 2
Read: Download Dissertation

Abstract


At present, the property of the wear-resistant steel that was produced in some country was better than the steel produced in china. It is very important to improve the properties of the wear-resistant steel for many factories and companies. Improving the property of the steel and decreasing the amount of the steel could increase the profits. In this paper, the microstructure and the properties of the SB wear-resistant steel and the B24S wear-resistant steel were studied. With the results of the study, the new heat treatment craft was made to improve the properties of the B24S steel.The microstructures of the B24S steel were observed by using the light microscope and the scanning electronic microscope (SEM). The properties of the steel were tested by using the universal tester. Some heat treatment crafts were designedThe microstructures of the SB steel are bainite and lath martensite. The steel has high tensile strength and high yield strength. The tensile strength is 1360 Mpa, and the yield strength is 1240 Mpa.The microstructures of the B24S steel are bainite and sorbite. There are many carbides and inclusions in the microstructure.After the samples were cooled in the water or the oil, the microstructures were bainite and martensite ,so the samples had high tensile strength and high yield strength. When the sample was cooling , the overcooling austenite transformed to the bainite . the bainite cut up the austensite. When the sample started martensite transformation, the small lath martensite was made, which increased the tensile strength and the yield strength of the steel. When the temper temperature increased, the tensile strength and the yield strength of the sample were decreased.The amount of the bainite of the microstructure influences the property of the steel. With the increasing of the amount of the bainite, the amount of the martensite decreased. And the baintie will be together like the underbrush, the bainite could not cut up the austensite effectively. When the scale of the bainite was 1%, the B24S steel has maximal tensile strength and good yield strength. The tensile strength was1645.43 Mpa, and the yield strength was 1258.69 Mpa.From the research results, the best heat treatment of the B24S steel was that the steel was heated at 900℃for 30 min and cooled to 500℃, isothermal treated for 5 seconds, and cooled in the water. After being treated, the tensile strength was1645.43 Mpa, and the yield strength was 1258.69 Mpa.

Related Dissertations

  1. Study on Key Technology and Its Physiological Basis of Virus Elimination and Rapid Propagation of Phalaenopsis,S682.31
  2. Study on the Subsurface Crack of Supporting Roller Made of Austempered Ductile Iron,TG156.3
  3. The Research on Rolling and Heat Treatment Technology of AZ31 Magnesium Alloy Thin Sheet,TG166.4
  4. Study on PMT Preparation, Structure and Performance of NiCoMnIn Alloy Foam,TG139.6
  5. Effects of Environments on Fracture Toughness and Fracture Behavior of 304 Stainless Steel,TG142.71
  6. Effect of Heat Treatment and Alloy Composition on Microstructure and Properties of Wear-resistant Casting Steel,TG142.4
  7. Development of Cr-Mo Alloy Steels for Liner Applications and Assessment of Its Wear Resistance,TG335.5
  8. Research on Composite Hard Anodic Oxidation of Aluminum Alloys and Mechanism,TG174.44
  9. Study on Extrusion and Heat Treatments of AJ and AE Series Cast Magnesium Alloys,TG166.4
  10. The Effect of Tensile Stress on Transformation Microstructure and Hardness of HQ785 Steel,TG142.1
  11. Reseach on Wear Resistance and Contact Fatigue Performance of Alloy Cast Steel for Roller,TG333.17
  12. Study on B/M Microstructure and Properties of Ultra-High Carbon Steels,TG142.31
  13. High-strength low-alloy steel weld metal microstructure and properties of,TG174.4
  14. Heat Treatment of Cast Al-Cu-Ti-(La) alloy microstructure and mechanical properties of,TG166.3
  15. Hot extruded Mg-Zn-Zr-Gd alloy microstructure and mechanical properties,TG379
  16. Carbon steel liquid plasma electrolytic carbonitriding research,TG156.8
  17. A508-3 nuclear power transformation plasticity of steel forgings and Numerical Simulation,TL341
  18. Microstructure and Strengthening Mechanism of High Strength Low Carbon Bainite Steel,TG142.2
  19. Research on Hydrogen Induced Cracking and Soil Stress Corrosion Cracking of X120 Pipeline Steel,TG142
  20. Research of Laser Technology on 45 Steel Surface Modification,TG174.44
  21. Research on Frictional Wear and Property Resistance of Mooring Chain Steel,TG142.1

CLC: > Industrial Technology > Metallurgy and Metal Craft > Metallurgy and Heat Treatment > Heat treatment > Heat treatment of steel
© 2012 www.DissertationTopic.Net  Mobile