Microstructures and Properties of Brazing Joint of Al2O3 Ceramic and Q235 Steel

Author: WangXinYang
Tutor: LiYan
School: Henan University of Science and Technology
Course: Materials Science
Keywords: Cu-Ti filler alloy Al2O3 ceramics Q235 steel brazing interface joint properties
CLC: TG407
Type: Master's thesis
Year: 2010
Downloads: 61
Quote: 0
Read: Download Dissertation

Abstract


To achieve a solid connection between Al2O3 ceramics and Q235 steel can play the excellent high-temperature performance, corrosion resistance, wear resistance of ceramic materials, and can also take full advantage of easy processing characteristics of metallic materials, which is extremely important in both theory and practice. In this research, Al2O3 ceramics were bonded with Q235 steel by active brazing with the filler alloys of Cu-Ti. The wetting properties of Cu-Ti active filler alloy were studied, and effects of the composition of filler alloys and brazing parameters such as temperature, holding time on joining strength and interface microstructures were investigated and analyzed by means of SEM、EDS、XRD and precision universal testing machine, etc. The interfacial properties and the fracture model of the joints were also discussed.The experimental results showed that the content of Ti in filler had an immediate impact on the wettability of the filler alloy, and the wettability increased with increasing Ti content in the experimental alloy composition range. The microstructure and properties of the joint depended on the composition of filler alloy and brazing parameters. Different shear strength of the joints was obtained as a result of different interface microstructures when using filler alloys with different ratios. Too high or too low brazing temperatures and too long or too short holding times were not conducive to obtain joints with good performance and compact organizations. When brazed at 1050℃for 30min with a filler alloy of Cu75Ti25 and exerted a pressure of 74Pa, a best joint was obtained with compact and few defects such as cracks and micropores in the interfacial-binding region and the average shear strength of the joint is 99.3MPa.The analysis of microstructure of the joints showed that interface-binding region could be divided into three layers. The three layers were reaction layer close to the ceramic, brazing alloy layer and diffusion layer close to the steel. The liquid braze alloy filled the micropores of ceramic and formed the reaction layer. Cu3Ti3O, TiFe, TiFe2 and Cu-base solid solution were confirmed as the reaction products. A metallurgical bonding had been achieved between the ceramics and the steel. According to the research of interfacial properties of the brazed joint, the hardness of interfacial zone was higher than the Q235 steel, and the hardness of the interfacial zone smoothed their transition, which indicated an excellent joint.Different bonding strength of brazed joints showed different characteristics of the shear fracture. There were two fracture modes of the joints, when the bonding strength was high, the fracture occurred in the ceramic side completely, when the bonding strength was low, the fracture occurred in the interface of ceramic and metal.

Related Dissertations

  1. Study for Calcareous Deposits under Initial Cathodic Protection in Simulated Deep Ocean Environment,P734.33
  2. Corrosion Inhibition of novel nitrogen-containing corrosion inhibitor of carbon steel in acidic medium,TG174.42
  3. Research on Brazing of Hydrogenated TC4 Titanium Alloy,TG454
  4. Theory and Experimental Investigation on Laser Hot-Assisted Machining Al2O3 Engineering Ceramics,TQ174
  5. Studies on the Friction and Wear of Y-TZP Matrix Ceramic Materials,TB321
  6. Study on Welding of Magnesium Alloy to Steel, Aluminum Alloy by Hybrid Laser-TIG Technique Based on the Interlayer Design,TG457.1
  7. Study on Inhibition Performance of Imidazoline Derivative Inhibitor Against CO2 Corrosion in Oil and Gas Field,TG174.42
  8. Study on the Al2O3-TiO2 Based Composite Microwave Dielectric Ceramics,TQ174.1
  9. The Microstructural Analysis and Accurate Figure of Alumina Crystal and Ceramics,TB383
  10. The Statistic Analyses to the Strength of Materials,TB301
  11. Study on the Corrosion and Protection of Container for Energy-Storage Aluminum Alloy,TG179
  12. A Study of Brazing Process and Mechanism of Si3N4 Ceramic Using High-Temperature Filler Alloy,TG454
  13. Study of Microstructure and Properties of Si3N4/40CrMo Joint Brazed by Active Brazing Alloy,TG407
  14. The Research on Laser Assisted Cutting of Alumina Ceramics,TG665
  15. STUDY ON MICRO-ARC OXIDATION OF THE HOT-DIPPING ALUMINUM COATIONGS ON Q235,TG174.443
  16. Effect of Adding Nano SiC Particles on the Structure and Performance of Q235 Steel,TG142.15
  17. The Research on Aluminizing Inside Steel Tube by Electronic-contact-heating,TG156.86
  18. Effect of Alloying Elements and Aging on Microstructure and Solder Interface of Sn-Zn Lead-free Solders,TG425
  19. The Experimental Research on Brazing Process of Fe3Al and High Temperature Heat-resistant Alloy,TG454
  20. Study of Self-assembled Monolayers on the Surface of Copper and Q235 Steel,TG174.4

CLC: > Industrial Technology > Metallurgy and Metal Craft > Welding, metal cutting and metal bonding > Welding general issues > Mechanical properties of welded joints and Intensity
© 2012 www.DissertationTopic.Net  Mobile