Study on UV Accelerated Aging and Lifetime Prediction of Pet Fibres

Author: ZhangCuiXin
Tutor: WangHaiYan
School: Yanshan University
Course: Applied Chemistry
Keywords: PET fibres Accelerated UV aging Sunlight exposure Lifetime prediction
CLC: TQ342.2
Type: Master's thesis
Year: 2010
Downloads: 48
Quote: 0
Read: Download Dissertation

Abstract


The sunlight exposure experiment of PET fibres was conducted in Oinhuangdao and the UVA-340/UVB-313 UV accelerated aging experiments were conducted respectively by the self-developed multi-intensity UV irradiation test device. The tensile performance changes of PET fibres in different exposure environments were studied. SEM, FT-IR were used to study the changes of the surface morphology and microstructure of the PET fibres. The lifetime of the PET fibres aged at the user level and in sunlight was predicted by the accelerated degradation data obtained in different UV exposure environments.The results showed that the aging experiments at different UV irradiation intensities can be carried out successfully by the self-developed multi-intensity UV irradiation test device, which can not only shorten the test cycle but also ensure the consistency of test conditions. The experiment results of the UV accelerate tests and the sunlight exposure test showed that in the UVA-340/ UVB-313 accelerate tests and the sunlight exposure test, the tensile performance changes with aging time of the PET fibres are the same; UVA-340 and UVB-313 exposure tests can accelerate the evolution rates of the surface chemical structures of the PET fibres, and their evolution rules are the same with the sunlight exposure test. Thus, both the UVA-340 and UVB-313 UV lamps can be used in UV accelerate tests. The tensile data was analyzed and the UV intensity-failure time inverse power law lifetime prediction model was established by the Matlab R 2007a, the lifetime prediction results showed that the extrapolation lifetime of accelerate tests and actual lifetime of user level are anastomosing and the prediction error is less than 7%, though the prediction error of the sunlight exposure by the data of UVB-313 accelerated tests is enlarged, the results still showed that the inverse power law modle can achieve better lifetime prediction for PET fibres’aging under UV irradiation conditions.

Related Dissertations

  1. Lifetime Prediction and Channel Wall Erosion Accelerate Test of Hall Thruster,V439.2
  2. Research on High Cycle Fatigue and lifetime of Electronic Beam Welded Joint of Titanium-alloy,O346.5
  3. Failure Mechanism Analyzing and Lifetime Predict Method Studying on Laser Gyroscope,V241.5
  4. Reliability Evaluation and Study on New Reinforcing and Reconstructing Techniques of Two-Way Curved Arch Bridge,U445.72
  5. Properties and Application Research of Multi-Antibacterial Polyamide Fibers,TQ342.1
  6. Preparationandapplication of Pan-Based Amphoteric Ion Exchange Fiber,TQ342.31
  7. The Study on the Creep Resistance Property of Ultra-High Molecular Weight Polyethylene Fiber,TQ342.61
  8. Study on Preparing the High Performance Fiber and Nonaporous Fiber by High Viscosity Nylon-6,TQ342
  9. Preparationandapplication of the Strong Alkali Anion Exchange Fiber Based the Polyethylene,TQ342.84
  10. Research on the Resistance of PLA Fiber to Wet-hot, Dry-hot, Acid and Alkali,TQ342
  11. Study on Preparation and Characterization of Polyvinyl Chloride Coated Polyester Multifilament,TQ342.2
  12. Study on the Properties of Cotton-Like Polyester False-Twist Textured Yarn and Its Fabric,TQ342.2
  13. Atmospheric Pressure Plasma Surface Modification of Carbom Fibers and Numerical Simulation of the Discharge,TQ342.742
  14. Processing and Performance of PA6 Negative Ions Fiber,TQ342.1
  15. Intelligent algorithms based carbon fiber spinning process monitoring and optimization,TQ342.742
  16. Preparation of PAN-based ACF electrostatic spinning process on the adsorption properties of,TQ342.742
  17. Step POY / FDY polyester filament formation and differential shrinkage fibers mixed structure control theory and experiment,TQ342.2
  18. Atmospheric pressure pulsed RF plasma discharge for high strength and high modulus polyethylene fiber surface modification,TQ342.61
  19. Imitation cotton copolyester synthesis and fiber preparation,TQ342
  20. The Study on Comparision of Raw Materials and Creep Properties of Ultra-High Molecular Weight Polyethylene Fiber,TQ342.61
  21. Study on Electrospun PAN Nano-ACF and Its Adsorption Property,TQ342.74

CLC: > Industrial Technology > Chemical Industry > The chemical fiber industry > Synthetic fiber > Polyester the Su fiber ( polyester)
© 2012 www.DissertationTopic.Net  Mobile