A Study on the Nox Storage-Reduction Catalysts of the BaCo1-xFexO3 Perovskite and the Supported Ba/Co/TiO2-ZrO2

Author: PanGuangHong
Tutor: MengMing
School: Tianjin University
Course: Industrial Catalysis
Keywords: BaCo1-xFexO3-δ Perovskite NOx storage Sulfur resistance Mechanism
CLC: O643.36
Type: Master's thesis
Year: 2010
Downloads: 27
Quote: 0
Read: Download Dissertation

Abstract


A series of NSR catalysts including bulk perovskite BaCo1-xFexO3-δ（x = 0, 0.1, 0.2, 0.3, 0.4, 0.5, 1.0） and supported Ba/Co/ZrTiO4 were prepared. Their structures, properties and NOx storage mechanism were characterized by the techniques of XRD, BET, in-situ DRIFTS, FT-IR and H2-TPR.Calcination condition shows obvious effect on the BaCoO3-δperovskite. In flow air which is pretreated by soda lime to removed CO2, the perovskite is more completely formed. The NOx storage capacity （NSC） and oxidation ability of the sample calcined at 700 oC are better than other samples. However, it exhibits poor sulfur resistance and small surface area.The support ZrTiO4 was prepared by co-precipitation. Ba and Co nitrates were supported on ZrTiO4-700 support by wet impregnation. After calcination, new active phase BaTiO3 and BaTi0.75Zr0.25O3 are formed. Compared with bulk perovskite, a much higher specific surface area of 20 m2/g is obtained, as a result, more active sites can be accessed on the supported sample, improving the oxidation ability of the catalysts and facilitating the diffusion of the NO2. Although BCTZ-700 catalyst shows better NOx storage capacity and sulfur resistance than bulk perovskite, the active phases on the support can also easily react with SO2 during the sulfate process, in addition, the storage component can be reduced to Ba and Co oxides during reduction regeneration, resulting in the total destruction of perovskite structure. In comparison, BCTZ-600 catalyst possesses higher NSC, better sulfur resistance and reduction performance. The active phases on the support are better dispersed, whose structure is only destroyed partly during the sulfur-aged process. After reduction regeneration, the NOx storage capability of sulfur-aged sample is almost the same as that for the fresh sample. In-situ DRIFTS results show that the main NOx storage species are the ionic nitrate and bidentate nitrate on the supported catalysts.To enhance the sulfur resistance of the catalysts, a series of BaCo1-x FexO3 catalysts were prepared using the same preparation method. After sulfur-aging, the NSC of Fe-doped BaCo0.8 Fe0.2O3 only decreases 3%, suggesting that the sample possesses rather good sulfur resistance performance. However, its NSC is only 31% of that for the non-doped catalyst BaCoO2.93. As the content of doped Fe is increased to 40%, the formed BaCo0.6 Fe0.4O3 exhibits higher NOx storage capacity and better sulfur resistance. The NSC of the fresh BaCo0.6 Fe0.4O3 is nearly the same as that for the fresh BaCoO2. 93. After sulfation it decreases 18%. The results of FT-IR show that the main stored species are bulk nitrate and monodentate nitrate. The main redox active sites are Co sites.

Related Dissertations

  1. Study on Hermetic EDGE Sealing of Anodic Bonding for Vacuum Glazing,TQ171.1
  2. Reactive Hot-Pressing and Mechanical Properties of （ZrB2-ZrO2）/BN Composites,TB332
  3. Research on Mechanism Analysis and Modeling Simulation of Horizontal Well Tractor,P631.83
  4. The Effect of Composite Additive on the SNCR,X701
  5. Kunming Transient Population Community Present Situation, Question and Countermeasure Preliminary Study,C924.25
  6. The Research on a New Modular Self-Reconfigurable Robot,TP242.2
  7. Study on Wastewater Purification Effect of the Free Surface Wetland with Different Substrates and Plant Combination,X703
  8. The Research of the Dynamic Process of Advertising Public Opinion,G206
  9. Research of Multicast Protocol in Wireless Sensor Networks,TN929.5
  10. Study on Application of Non-phosphate Additive in Frozen Penaeus Vannamei and Mechanism of Water-holding,TS254.4
  11. Incentive Mechanism Research of the New Generation of Migrant Workers,F272.92
  12. Shandong Province,university research projects Integrated Management Model,G644
  13. Process and Mechanism of Eucalyptus Pulp Bleaching Catalysed by Cu2+/Co2+,TS745
  14. The Environmental-Friendly Method and Process of Removing Non-Cellulosic Matters from Bamboo for Textile Fiber,TS652
  15. Minority environmental rights,D922.68
  16. Research and Implementation on Service-Oriented Multi-Agent System Cooperation Mechanism,TP393.09
  17. Studies on the Models of the Reform of Chinese Marine Management System,D630
  18. Gel - Foam Preparation of porous alumina insulation materials,TQ174.1
  19. The Research on Sulfate Leaching Properties of Cation-exchange Resin Used in Power Plants,TQ425.23
  20. Preparation and Anticorrosion Properties of Doped Polyaniline/Epoxy Coating,TQ637
  21. Practice and prospects of the Clean Development Mechanism in China,X38

CLC: > Mathematical sciences and chemical > Chemistry > Physical Chemistry ( theoretical chemistry ),chemical physics > Chemical kinetics,catalysis > Catalytic > Catalyst
© 2012 www.DissertationTopic.Net  Mobile