Influence of Surface Impregnation with Silane on Corrosion of Steel in Concrete

Author: RenZhaoJun
Tutor: ZhaoTieJun；F.H.Wittmann
School: Qingdao Technological University
Course: Structural Engineering
Keywords: steel corrosion surface impregnation with silane liquid chloride carbonization crack drying and wetting cycle
CLC: TU375
Type: Master's thesis
Year: 2008
Downloads: 42
Quote: 0
Read: Download Dissertation

Abstract


The degradation of concrete durability which can reduce the reliability and security of constructures notably,have endangered the normal use greatly.Also durability of concrete has already become a severe problem that the field of engineering construction in our country has faced. There are numerous factors leading to the degradation of concrete durability,and among them the corrosion of reinforcing bar is one of the main reasons causing reduction of concrete structu re durability.Because of the corrosion of reinforcing bar,a lot of concrete structures have to maintain or remove,even collapse,and cause enormous economic losses.Therefore,detection and evaluation in steel corrosion,and taking effectual mearsures to repair and pretect have great significance in improving concrete structure durabilities.Regarding to the steel corrosion of concrete,this paper outlines state of the art in this field comprehensively both at home and abroad,and analyze s the corrosion mechanism correspondingly. Half cell potential,polarisation resistance and mass loss methods are adoptted to study the influence of corrosion development and silane liquid surface impregnation on the steel corrosion under singly and complex action among external chloride ingress,initial chloride,drying and wetting circle,crack and carbonization.Especially,the influence of silane liquid surface impregnation on steel corrosion of concrete in different environmental conditions was studied in details.Corresponding results indicts:(1) Silane liquid surface impregnation concrete can prevent external chloride penetration,so that the treated concrete has good effect on reducing the probility and rate of steel corrosion,delaying the time of initiated corros ion and lowing the mass loss ratio of corroded steel.(2) Silane liquid surface impregnation concrete can not influence corrosion in concrete with initial chloride abviously;however,it can reduce the corrosion rate and degree of initial chloride ingree concrete in drying and wetting cycle actions.(3) Steel corrosion in concrete, for which silane liquid surface impregnation is carried on first and then induce crack,is more severe than the ones crack inducing first and silane liquid surface impregnation later.The mass loss ratio of above treatment in two W/C ratios from max to rain is given as following: MWC4-0.6＞MCW4-0.6＞MWC4-0.4＞MCW4-0.4＞MWC1-0.6＞MWC1-0.4＞MCW1-0.6＞MCW1-0.4. (4) In the complex action of carbonization,crack and drying and wetting cycle s of water,also silane liquid surface impregnation can reduce corrosion rate to a certain extent,thus improve the durability of concrete;(5) For untreated concrete,the corrosion degree acclerates with increase of W/C, corrosion rate of concrete with W/C=0.6 is two times higher than 0.4 ones.But for silane treated concrete,the effect of water to cement ratio to steel corrosion is not notable.

Related Dissertations

  1. Elastic-viscoplastic Analysis of the Asymptotic Stress Field Near the Tip of a Quasi-static Propagating Crack under Plane Stress Condition,O346.1
  2. The Preparation of Aluminum-Ammonium Cationic Starch and Its Application in Papermaking,TS727
  3. Modification and Application of the Waste Fluorgypsum and the Treating of High Concentrations Fluoride Wastewater,X703
  4. Study on Hydraulic Fracturing of Low Permeability Reservoir,P618.13
  5. Analysis of Concrete Durability under Combined Action of Freeze-thaw Cycles and Chloride Ion Erosion,TU528
  6. Studies on Plant Growth Regulators Relieving the Injury of Azoxystrobin to Maize and Soybean Seedling,S481
  7. Alleviation of Four Compounds in Plant Growth Regulators on Pyraclostrobin Toxicity,S481
  8. Comparative Toxicity of WSHFD with Arsenicals and Mercurials and Cerebral Protective Effect of WSHFD on Ischemia and Reperfusion,R285.5
  9. Injection piperacillin sodium and tazobactam sodium content determination and compatible stability of visits,R927.2
  10. A New Rail Crack Remote Monitoring System,U213.4
  11. Study on Shear Bearing Capacity of HRBF500-Reinforced Concrete Beams,TU375.1
  12. Study on the Subsurface Crack of Supporting Roller Made of Austempered Ductile Iron,TG156.3
  13. Study of Propylene Oxide Wastewater Pretreatment by Five-effect Evaporation Process,X78
  14. Study on the Preparation and Photocatalytic Activity of Titanium Dioxide Nanoparticles,O643.36
  15. Research on Pavement Crack Detection Algorithom Based on Digital Image Processing,TP391.41
  16. Research on Pavement Crack Detection Algorithm,TP274
  17. Theoretical Analysis and Related Tests on Concrete Beam Prestressed with FRP Bars,TU375.1
  18. Rootkit technology in the Third-Party Information Security System Research,TP309
  19. The mechanical properties of fiber reinforced concrete research and finite element analysis,TU528.572
  20. Particle reinforced copper matrix composites mechanical behavior of finite element analysis,TB331
  21. Distributed optical fiber sensing technology in the steel corrosion Monitoring,TU375

CLC: > Industrial Technology > Building Science > Building structure > Concrete structure,reinforced concrete structure > Reinforced concrete structures
© 2012 www.DissertationTopic.Net  Mobile