Synthesis and Application of the chloro- methoxy fatty acid methyl esters

Author: SunGuoQiang
Tutor: WangZhengPing
School: Guangzhou University
Course: Chemical processes
Keywords: plasticizer tension test thermal stability hardness chloro-methoxy fatty acid methyl ester
CLC: TQ414.8
Type: Master's thesis
Year: 2011
Downloads: 18
Quote: 0
Read: Download Dissertation

Abstract


A new type plasticizer is developed.A new process to chloro-methoxy fatty acid methyl ester from fatty acid methyl ester as main starting material is introduced when methanol is methylating reagent,benzoperoxide is catalyst and chlorine is chlorinating agent.The effect of reaction time, flow rate of chlorine gas and temperature to the reaction are studied.The experimental results showed that when reaction time is between 7 h and 8 h, flow rate of chlorine gas is 50~60 mL/min,temperature is 70~85℃, methanol is 10% of fatty acid methyl ester,the quality of product is the best.The chlorine concentration of chloro-methoxy fattyacid methyl ester is about 25%, its color and luster is very good and its properties is well-behaved.On this basis,How to rise up the decomposition temperature of chloro-methoxy fat acid methyl ester is studied by adding addictives.The effect of synthesized conditions and ratio of heat stabilizer are studied.Maximum force, tensile strength, elongation at break and surface hardness are measured in cable material specimen as plasticizer DOP replaced different proportions of chloro-methoxy fatty acid methyl ester in the formula of cable feed.In last article surface hardness and plasticizer mobility change are studied.When the plasticizer containing 40% DOP,60% chloro-methoxy fatty acid methyl ester(containing chlorine 24.62%) compares with that containing 100% DOP,the experiment result shows that the performance parameter of the former plasticizer is better than the latter.Its maximum force is 375N,apparently larger than latter 287N.The material tensile strength increases 31%.Compared to elongation at break,their performance index is well-matched,one 330% and the other 358%.PVC material maximum tensile strength is 16.25Mpa,incresed 33.6%, when the methoxy group content and DOP content are diffirent. At this point, the methoxy group content is 8.5%,DOP is 60%.PVC material elongation at break is 410.80% and the surface hardness is almost the same when the methoxy group content is 6.5% and DOP is 40%.Chloro-epoxidized fatty acid methyl esters is produced in order to do comparative test. The experimental results showed that the plasticity of chloro-methoxy fatty acid methyl ester is better than Chloro-epoxidized fatty acid methyl ester.

Related Dissertations

  1. Thermal Stability of Complexes of Chitosan Quaternary Ammonium Salt and Metal Ion,O634
  2. Study on Technics & Performance of Nano Electroless Composite Plating on 20~# Steel,TQ153
  3. Prototype Development of Intimate Apparel Mannequin,TS941.2
  4. Molecular Identification of Hardness-related Genes and Analysis of Molecular Mechanism of PINA Null in Bread Wheat,S512.1
  5. Syntheses, Structures and Properties of Metal-organic Frameworks Based on Dicarboxylate Ligands,O621.13
  6. Research on the Plasticizers of Starch Sizing Agents,TS103.846.1
  7. Study of the Thermal-Stability for Polylactide and Its Blends,TQ323.4
  8. The Curing and Phase Separation Study on Reactive Plasticizer in Polyvinyl Chloride Matrix,TQ325.3
  9. Ability to affect the mechanical properties of rare earth elements on the CuZrAl based bulk amorphous alloy formation,TG139.8
  10. Relationship between Fatigue Properties and Process Parameters of Friction Stir Welding Joints for Aluminum Alloy,TG407
  11. Fe-C-B alloy microstructure and properties of basic research,TG113
  12. Stainless steel surface spray WC-Ni base alloy coating,TG174.4
  13. Research on GFA, Thermal Stability and Magnetic Performances of Mult-elemental Fe-based Bulk Amorphous Alloys,TG139.8
  14. Study of Effects on Glass Forming Ability and Magnetic Property with Rare Earth Elements Addition in the FeCoNiBSiNb Bulk Glassy Alloys,TG139.8
  15. Preparation, Characterization, OSC and NSC of Ceria Zirconia Solid Solutions,O643.3
  16. Surface Characteristic Analysis of Workpiece Machined by Powder Mixed EDM,TG661
  17. Arc method of single-walled carbon nanotubes , purification and modified styrene,TB383.1
  18. Studies on Synthesis, Characterization of ⅠB-ⅡB Metals Chalcogenides Coordination Compound,O641.4
  19. Study on Modification and Properties of Polyether Polyurethane(Urea),TQ323.8
  20. Azo-Dye Intercalated Ldhs with Supramolecular Structures,O621

CLC: > Industrial Technology > Chemical Industry > Production of solvents and plasticizers > Plasticizer > Chlorinated plasticizers
© 2012 www.DissertationTopic.Net  Mobile