Synthesisand Properties of Polyurethane Solid-Solid Phase Change Materials

Author: WangYuLing
Tutor: PeiGuangLing
School: Beijing Institute of Clothing Technology
Course: Materials Science
Keywords: Phase change material Polyurethane Solid-solid phase change Methoxy polyethylene glycol(MPEG) Crystallization
CLC: TB34
Type: Master's thesis
Year: 2010
Downloads: 133
Quote: 1
Read: Download Dissertation

Abstract


In this paper,a novel phase change heat storage polyurethane with MPEG-based soft segment and various MDI-NPG、MDI-BDO、MDI-PER、TDI-NPG-based hard segments was synthesized by two-step solution polymerization. FT-IR,DSC,TG,POM were used to study the structure characteristics,phase change behavior,heat storage characteristics and aggregation structure. Then the best process condition of polyurethane can be obtained.The results indicated that the best process condition of polyurethane with MPEG-based soft segment and MDI-NPG-based hard segments was as follows:reaction temperature was 70℃,reaction time is 12 hours, reation R([NCO]/[OH])is 1.01. In this condition, the phase-change temperature and enthalpy of phase change heat storage polyurethane were 43.92℃and 146.64J/g.Polarization Microscope(POM) and DSC investigation showed that the soft segments of Polyurethane phase change materials could crystallize and the crystal structure was spherulites,but the spherulites size was much smaller than that of MPEG because the soft segment MPEG’s crystallization in polyurethane phase change materials was confined by the hard segment. The heat srorage is caused by the transition of the soft segments of polyurethane phase change materials from crystalline state to amorphous. The energy is mainly obtained from heat caused by entropy change between the crystal solid state and amorphous solid state. The hard segments acted as physical cross-linkers to restricted MPEG’s segmental movement. when it is heated to the temperature above MPEG’s melting point, polyurethane phase change materials still doesn’t move freely and keep its solid - solid phase transition state.The polyurethane phase change materials made with MDI-BDO、MDI-PER-based hard segments have good thermal properties, great transition enthalpy, suitable phase transition temperature, good thermal stability, without liquid leakage during the phase transition process and reasonably good stability throughout the cycling process.BDO and PER have not phase transition temperature and transition enthalpy from room temperature to 100℃range. But NPG exists phase transition temperature and transition enthalpy and the transition temperature closes to MPEG’s. To test the performance of MPEG-co-NPG、MPEG-co-BDO and MPEG-co-PER,the results show that the NPG has a synergetic effect on polyurethane phase change materials.The crystalline of polyurethane with MPEG-based soft segment and MDI-NPG-based hard segments was smaller than TDI-NPG’s.

Related Dissertations

  1. Synthesis and Biocompatibility of different types of hydrophilic surface - modified polyurethane,R318.08
  2. Hydrophilic structure of different types of surface -modified polyurethane material and coagulation 12 factor nine peptide fragments,and fibrinogen P1 fragment of computer simulation of the interaction,O631.3
  3. Research on PSA/Cotton Blend Fabric of Coatinging of Water Resistance and Moisture Permeability,TS195.6
  4. Preparation and Application of Water-based Polyurethane to Improve Wet Rubbing Fastness,TS193.2
  5. Study on Preparation and Capability of Two-Component Polyurethane Sealant,TQ436.6
  6. The synthesis of NZP family mesoporous phosphate materials,O643.36
  7. Intelligent control of the electric continuous crystallization machine,TP273
  8. The Research of Preparation, Microstructure and Properties Evaluation of Geopolymer,P574
  9. Research on Recrystallization Behavior of X80 Pipeline in Hot Transmutation,TG111.7
  10. Study on Nd2Fe14B/α-Fe-type Nanocomposite Permanent Magnet,TB383.1
  11. Purifieation and SePeration of Phytosterol from DeodoriZer Distillats of Cotton Seed Oiland Its Funetion Study,TQ645.98
  12. Studies on the Kinetics of Sodium Gluconate Fermentation and Crystallization Process,TQ920.1
  13. Production, Purification and Application of Ligninolytic Enzymes from Phanerochaete Chrysosporium,TQ925
  14. Study on Low-temperature Synthesis and Photocatalytic Performance of Ti-based Catalyst,O643.36
  15. The Synthesize of Mesoporous Nanometer TiO2 and Applied in Dye-sensitized Solar Cell,TM914.4
  16. Design and Optimization Analysis of the Modular Matting Structure and Connecting Mode,U416.2
  17. Study on the Fabricating Techniques and Effective Anisotropy and Coercivity of Nanocomposite Permanent Magnet,TM273
  18. Formation and Thermodynamics Properties of Zrcu-based Bulk Metallic Glass,TG139.8
  19. Prepaption of Mg65Cu25Y10 Amorphous Alloy and Its Crystallization Behavior,TG139.8
  20. Preparation and Research on Molecular Weight Structure of Poly(l-lactide) via Solvothermal Method,O633

CLC: > Industrial Technology > General industrial technology > Materials science and engineering > Functional Materials
© 2012 www.DissertationTopic.Net  Mobile