Preparation and Properties of Nano-Coated Microwave Absorbing Materials

Author: SongGe
Tutor: ShiGuiMei
School: Shenyang University of Technology
Course: Condensed Matter Physics
Keywords: Nanocomposite powders Arc Discharge Template Method Microwave Absorbing Properties
CLC: TB383.1
Type: Master's thesis
Year: 2010
Downloads: 88
Quote: 0
Read: Download Dissertation

Abstract


CoAl2O4(Co) and Ni/α-Fe2O3 nanocomposite powders were prepared by changing conditions of coating process. The phase constitution, particles morphologies, size distributions, microstructure and the binding energy of the elements of these different kinds of nanocomposite powders and the structure characteristics of the aggregates have been studied by means of X-ray diffraction (XRD), High-resolution transmission electron microscopy (HRTEM), X-ray photoelectron spectroscopy (XPS) in details. The magnetic characteristics and electromagnetic (EM) properties of the nanocomposite powders were measured by Vibrating sample magnetism (VSM), network vector analyzer. The physical mechanism of the good EM absorption properties in these nanocomposite powders was discussed.The result reveals CoAl2O4(Co) nanocapsules were successfully prepared by arc discharge. HRTEM studies revealed the particles have a distinct shell/core structure, the size of the nanocapsules ranges from 10 to 90 nm and the thickness of shell is in 3-10nm. Based on X-ray photoelectron spectroscopy investigation, the core of the as-prepared nanocapsules is Co, while the shell is mainly composed of CoAl2O4 and a small amount of Al2O3. Co(OH)2,,Co2O3. The results of microwave absorbing capability indicated that the maximum reflection loss of CoAl2O4(Co) nanocapsules reached -21.1dB with 2.5mm and the absorption is less than-lOdB in the range of 5.01-17.87GHz.Ni/α-Fe2O3 nanocomposite powders were successfully prepared by chemical plating, the size of which is 2-5μm and the thickness is in 4-8nm. It is approved that the core isα-Fe2O3 and the shell is Ni measured by XRD and XPS photoelectron spectrum.Magnetism research shows that the saturation magnetization decreases of nanocapsules and the coercive force increases of nanocomposite powders, compared with pure bulk Fe2O3. The reflection loss R(dB) of the Ni/α-Fe2O3 nanocomposite powders/ paraffin wax composite materials were simulated by experimental date. The reflection loss R(dB) of the nanocapsules/paraffin wax composite materials 4 mm in thickness reaches to-16.8dB at 6.82GHz, and EM absorption properties (RL<-10dB) in the 3.97-18GHz range. Although the saturation magnetization of Ni/α-Fe2O3 is lower, this special shell/core structure, ferromagnetic Ni shell and shape anisotropy is an important factor to the appearance of high performance absorbing property.

Related Dissertations

  1. Preparation of ITO Quai-1D Nanostructures by Sol-Gel Method Combined with Porous Anodic Aluminum Oxide Template,TB383.1
  2. Hydrothermal Synthesis of Oxide Hollow Spheres,TB383.4
  3. Preparation of Silica Hollow Spheres with Mesopores in the Walls,TB383.1
  4. Fabrication and Microwave Absorbing Properties of BaFe12-x (Ni （0.5）Cu0.5Zr)x/2O19 Ferrite,TM277
  5. Three-Dimensionally Ordered Sub-Micron Structure Thin Films Fabrication and Their Optical Properties,TB383.2
  6. Study on the Arc Formation and Relevant Parameters in Circuit Breaker,TM564
  7. Study of Electroless Nickel Plating on Cenospheres,TQ153
  8. Preparation and Capability Research of Magnetic Nanocapsules,TB383.1
  9. Synthesis of Ordered Mesoporous C/sio 2 Nanocomposites and Mesoporous Carbon Materials Through Co-template Method,TB383.1
  10. Synthesis and Characterization of Polyaniline Micro/nano Structure and Its Composites,TB383.1
  11. Investigation on Gas Separation Performance of Coal-base Tubular C/C Composite Membrane Prepared by Template Method,TQ531
  12. Preparation of carbon nanotubes , composite materials , as well as the field enhancement factor,TB383.1
  13. Colloidosomes Fabricated Through Emulsion Droplet Template Method and Their Application,TB383.4
  14. Fabrication of Ordered Two-dimensional Ag Nanoarrays and Their SPR/SERS Properties,TB383.1
  15. Studies on the Preparation of Spherical Nano-structured Organic-inorganic Composites by a Microgel Template Method,TB383
  16. Colloidal Crystals, Structural Color of Colloidal Films and Corresponding Macroporous Materials Using Colloidal Crystals as Templates,O648.1
  17. Study on Fabrication of Monodispersed Hollow Barium Ferrite Submicrospheres,TB383.4
  18. Study of Pulsed Power for Electrothermal-Chemical Launcher and Electrical Characteristic of Plasma Generator,TJ399
  19. Template Method Preparation, Characterization and the Photocatalytic Performance of Low-dimension Ordered Titania Arrays,TB383.4
  20. Preparation of Nanowire Array and Composite Films Based on Carbon Nanotubes for the Construction of Electrochemical Biosensors,TP212.3
  21. Synthesis and Microwave Absorbing Properties of Low Frequency Absorber,TB34

CLC: > Industrial Technology > General industrial technology > Materials science and engineering > Special structural materials
© 2012 www.DissertationTopic.Net  Mobile