The Statistics and Analysis for Defects of In-service Sphere Tank

Author: FeiDongHui
Tutor: ChenBingBing；ZuoGuoRong
School: Zhejiang University of Technology
Course: Mechanical Engineering
Keywords: Sphere tank Crack Statistics Inner surface Girth weld Stress corrosion
CLC: TQ053.2
Type: Master's thesis
Year: 2011
Downloads: 77
Quote: 0
Read: Download Dissertation

Abstract


The sphere tank has been widely used as one large-scale storage tank with the development of petroleum chemical industry. The risk for the safe usage of sphere tank and threats the routine production of enterprise, because of the existence of defects in the tank. To find some laws about the types, the dangers and the parts easy to occur, it is necessary to process the statistics, classification and analysis scientifically for such defects. which may be benefit to the manufacture, the usage, the inspection and the maintenance of the sphere tank.The present shows some laws about defect types, the corresponding location and the potential hazards of in-service sphere tanks by statistical method, mathematic analysis, summary and conclusion based on the sample of twenty tanks inspected by Ningbo Special Equipment Inspection Institute. And analysis of the simple rule of defects by the method of theoretical analysis, data calculation and finite element analysis, etc. It can be summed up as follows:(1)The cracks are the main defects for in-service sphere tanks,mostly occurred near the fillet welds of support leg, inner surface of the tank and girth welds, another area is unusual;(2)At Inner surface cracks ,including spherical crack of stress corrosion with the tendency, which is 2.4 times to those without the stress corrosion tendency;(3)The back repair rate is high for the fillet weld cracks of the leg, the inner surface cracks and the girth cracks as well as the nozzle fillet welds. And comparatively low for outer surface cracks, longitudinal seam cracks and butt welds of polar plate. Also the tanks with SC is higher than the tanks without SC. (4)The low heat input in welding, large intensity of restraint and assemblage induced residual stress are the main factors leading to more cracks and high back-repair rate. Stress corrosion induced cracking (SSIC) dominates the service condition of inner surface. Poor welding quality and stress concentration are two important factors controlling the crack amount and back-repair rate of the leg fillet welds.

Related Dissertations

  1. Study on Hydraulic Fracturing of Low Permeability Reservoir,P618.13
  2. Game technical statistics in Gymnastics Sports Science Research,G832
  3. Study on the Subsurface Crack of Supporting Roller Made of Austempered Ductile Iron,TG156.3
  4. Design and Implementation of Xinjiang vocational colleges online teaching assessment system,TP311.52
  5. Failure Analysis on Superheat Section Connecting Pipe Flange of Ethylene Cracking Furnace,TQ221.211
  6. Research on Pavement Crack Detection Algorithom Based on Digital Image Processing,TP391.41
  7. Theoretical Analysis and Related Tests on Concrete Beam Prestressed with FRP Bars,TU375.1
  8. Based on non- parametric statistical characteristic quantities Gaussian kernel network traffic anomaly detection method,TP393.07
  9. DDoS detection technology,TP393.08
  10. 316LN austenitic stainless steel stress corrosion cracking of welded joints,TG407
  11. The mechanical properties of fiber reinforced concrete research and finite element analysis,TU528.572
  12. ECAP for Mg-Zn-Zr-Gd alloy fatigue behavior of,TG379
  13. Implementation of People Alculatio System of Binaocular Camera Based on DSP,TP368.1
  14. The Instability Mechanism and Research of Deformation Prediction in Ding Jiafen Landslide,P642.22
  15. Research on Vibration Fatigue of Stiffened Aluminum Alloy Panel,O346.1
  16. Mixed-mode (I/II) Cracks in Crystal Diamond: A Molecular Dynamics Study,O346.1
  17. Simulation of the Interface Closure for Particulate Reinforced Composites with Voronoi Cell Finite Element Method,TB33
  18. Experimental Study on Anti-crack Performance of Hybrid Fiber Reinforced Concrete,TU528.572
  19. Mathematical Statical Analysis & Reliability Research on the Basic Strength Features of Recycled Concrete,TU528
  20. Temperature Control and Crack Prevention of Mass Concrete for Foundation of High-rise Building,TU755
  21. Influence of Surface Impregnation with Silane on Corrosion of Steel in Concrete,TU375

CLC: > Industrial Technology > Chemical Industry > General issues > Chemical machinery and apparatus, equipment > Chemical general machinery and equipment > Container chemical equipment
© 2012 www.DissertationTopic.Net  Mobile