Study on Synthesis, Modification of Aqueous Polyurethane and Application in Ink

Author: GuLiZheng
Tutor: WangZhengXiang
School: Hunan University
Course: Materials processing
Keywords: aqueous polyurethane ink modify printing ink forplastic film water resistance
CLC: TQ323.8
Type: Master's thesis
Year: 2012
Downloads: 361
Quote: 0
Read: Download Dissertation

Abstract


With the advantages of adhesion, glossiness, abrasion and innocuity,no pollution etc, the aqueous polyurethane ink has become focus ofresearch and development. In this paper, aqueous polyurethane ink withbetter water resistance for plastic film was researched, and the emphasisis to solve water resistance and adhesion. Therefore, It can besummarized as follows:(1) Take the advantage of single factor test, determine the optimalsynthesis condition of the waterborne polyurethane are that thetemperature of prepolymerization reaction is65℃, the content of catalystis96mg(compared to20g polyester glycol), the time is5hours.(2) Different composition and structure of the polyester glycol (PEAand PNA and PE/DEA) were adopted to synthesize waterbornepolyurethane, the conclusion is that: the samples based PNA haveexceedingly good water resistance, but poor adhesion. While the samplesbased PEA have excellent adhesion, but weak water resistance.(3) Based the result of (2), by PNA and PEA’s matching, a series ofwaterborne polyurethane were prepared, and the affects of synthesisconditions were studied. The conclusion is that: when the mass ratio ofpolyester PBA and PNA is3:1, the value of R is1.2, the content ofDMPA is9%, chain extender was1,4-Butylene glycol, the degree ofneutralizer is1.2, the comprehensive performance of the waterbornepolyurethane is preferably.(4) Make the use of alcoholysis between ethylene glycol and tung oil,the hydroxyl was introduced into the chain of tung oil, with this productwaterborne polyurethane based tung oil was prepared. The results showthat the target product was highest when the temperature oftransesterification is120℃,the molar ratio of tung oil and glycol is1:4;the collectivity performance of Polyurethane emusion and film is goodwhen the molar ratio of BDO and single hydroxyl acid ester based tungoil was3:1.(5) To polyether polyurethane, binder Polyester polyurethane, tung oil modified polyurethane formulation of the three types of ink. Theproperties of waterborne polyurethane ink were studied. The result showthat the ink prepared by tung oil modified polyurethane has excellentproperties such as adhesion, water resistance and glossiness etc, and it canmeet the need of printing ink for plastic film.

Related Dissertations

  1. Research on PSA/Cotton Blend Fabric of Coatinging of Water Resistance and Moisture Permeability,TS195.6
  2. Effect of Hydrophobic Modification of the Flame Retardant on the Properties of the Water-borne Intumescent Fire Retardant Coatings,TQ637
  3. Preparation and properties of silicone modified waterborne polyurethane coating agent,TS195.2
  4. Study on Synthesis and Printability of the New Aqueous Polyurethane for Flexible Packaging Printing Ink,TQ638
  5. Influence of Pretreatment Process for Phosphogypsum on Water Resistance of Phosphogypsum Composite Cement,TQ172.1
  6. The Property of Modified Cyanate for High Frequency Printed Circuit Board,TQ320.7
  7. Speed Adjusting Technology and Its Application for High-voltage Electrical Machine in Power Plants,TM921.51
  8. Surface-Fluorinated Polyvinyl Alcohol Functional Membranes: Preparation, Morphology and Surface Property,TB383.2
  9. Molecular Genetic Analysis of One Chinese Family with Leber’s Heriditary Optic Neuropathy,R774.6
  10. Preparation and Properties of Ambient Curing One-component Acrylate Latex,TQ316.334
  11. Experimental Study of High-strength and Water Resistant Compound Gypsum to Suits Plateau Environment,TQ177.3
  12. Response of Liparis Japonica to Water-stress,S682.19
  13. Study on Compatibility of Thermoplastic Polyurethane Elastomer/Nylon 6 Blend,TQ325.14
  14. The Lie-group Shooting Method for Two Classical Ill-posed Problems,O241.82
  15. Pharmaceutical Laboratory Distributed Data Management System,R969.1
  16. Modify the rules of the invention patent application file parsing and system reconstruction,D923.42
  17. Study on the Preparation and Properties Characaterization of PLLA/SA Blends,TQ320.6
  18. Polyacrylate polymer polymerization paper enhancer and applied research,TS727.5
  19. CdSe/ZnS Core/Shell Quantum Dots Synthesis and Modification,O471.1
  20. Study on High Performance Waterborne Polyurethane Latex,TQ331.4
  21. Research on the Preparing Process and Properties of PZT Ceramics,TM282

CLC: > Industrial Technology > Chemical Industry > Synthetic resins and plastics industry > Polycondensation resin and plastic > Polyurethane (poly carbamate ) and plastic
© 2012 www.DissertationTopic.Net  Mobile