The Synthesis of Polymer Gelatinizer and the Rheological Properties of Ultra-high Temperature Fracturing Fluid System

Author: HeLiangHao
Tutor: FangBo
School: East China University of Science and Technology
Course: Chemical Engineering
Keywords: polymer gelatinizer ultra-high temperature gel fracturing fluid fracturing fluidrheological property polymer gel
CLC: TE39
Type: Master's thesis
Year: 2013
Downloads: 231
Quote: 0
Read: Download Dissertation

Abstract


In order to carry out the ultra-high temperature fracturing operation for deep well, a new type of synthetic anionic terpolymer gelatinizer was researched and produced in this paper, and the related influencing factors were studied. The temperature resistance, shear resistance and gel breaking performance of cross-linked gel fracturing fluid were also investigated. The ultra-high temperature resistant polymer fracturing fluid system which can resistant200℃was obtained. Furthermore, the pilot and production of polymer gelatinizer was carried out, and the proper pilot production process and polymer gelatinizer powder product were obtained. The oilfield tests for the polymer was performed, and better fracturing stimulation effect was achieved. Main conclusions were obtained as follows:1) Three acrylamide species monomers were taken as raw materials, solution polymerization was used and the anionic terpolymer gelatinizer which molecular weight was about4.5million was obtained. The factors such as monomer mass ratio, monomer mass concentration, reaction temperature, reaction time, initiator content and component, pH of polymerization system, content of the chain-transfer agent, and other factors on the copolymer product properties were illustrated. The laboratory synthesis process of high temperature polymer gelatinizer process was obtained.2) The ultra-high temperature resistant polymer fracturing fluid system which could endure200℃was obtained. The effects of base-solution concentration of polymer gelatinizer, the crosslinking ratio with crosslinker, the pH value of system and the related additives on the fracturing gel were illustrated. Through laboratory evaluation and research, the formulation of ultra-high temperature resistant polymer fracturing fluid system was achieved. At200℃, the crosslinked gel fracturing fluid was sheared at170s-1for120min, the viscosity was retained more than150mPa·s. The gel fracturing fluid possess good viscosity recovery ability under high shear, easily gel broken, less residue, low surface tension and the little filtration, which could be applied in ultra-high temperature deep wells.3) The results of Rheological research were shown that, the base-solution of pilot and laboratory synthesized gelatinizer and crosslinked gel fracturing fluid exhibited shear-thinning property, and excellent visco-elasticity. The sorts of products (laboratory synthesized sample and pilot product), the dry and smash process of pilot product, the amount of dispersant for prilling, the delayed-crosslinking agent on the visco-elastic and shear-thinning property of fracturing fluid were illustrated.4) The pilot and production process were obtained, and7.5t pilot polymer gelatinizer powder was successfully produced. It was proved that the fracturing gel formed with pilot polymer gelatinizer could endure200℃, and its viscosity was retained more than100mPa-s.The oilfield-test showed that, crosslinking ultra-high temperarture gel fracturing fluid system could be injected into the reservoir by multi-stage acidizing and fracturing, and good fracturing stimulation effect was achieved.

Related Dissertations

  1. Assessment of Gel System for Chemical Water Shut-off on H1 Block of Liaohe Oilfeild,TE39
  2. Phenylbornate-Diol Crosslinked Polymer Gels with Reversible Sol-Gel Transition,O631.3
  3. Study of Gel Polymer Electrolyte in Dye-Sensitized Solar Cell,TM914.4
  4. Synthesis of Temperature and Alkali Resistant Polymer Gel Profile Control Agent,TE39
  5. Covalent Cross-linked Polymer Gels with Reversible Sol-Gel Transition and Self-healing Properties,O631.3
  6. Study of Ir Detection and the Treatment Technology of Coal Outcrop and Slag Fire in Ulan Coal Mine,TD752.2
  7. Profile Controlling Technology Research Using Residual Polymer After Polymer Flooding,TE357.46
  8. Research on ASP Compound Flooding Deep Profile Control Technology in Strong Alkali,TE357
  9. Research on Theory and Numerical Simulations of Multi-Phase Media,TU452
  10. Technology Study on Polymer Gel for Enhancing Water Flooding Efficiency in NB35-2 Oilfield,TE357.4
  11. Organic solvents on the conductivity of ionic liquids affect the Research and Application,O645.1
  12. Viscosity Enhancement Technology of Polymer Solution and Assessment of Oil Displacement Applied in Offshore Oilfield,TE357
  13. The Study on PAA-PEG Thermosetting Gel Electrolyte for Quasi-Solid-State Dye-Sensitized Solar Cell,TM914.4
  14. Preparation and Electromagnetic Microwave Absorbing Properties of Nanosized Nickel Ferrite and Its Composites,TB383.1
  15. Polymer glue Factors Influencing the Stability,O648.1
  16. Study on Polymer Gel Electrolyte and TiO2-Ordered Thin Film for Dye-Sensitized Solar Cells,TM914.4
  17. Molecular Configuration and Flow Characteristiscs of Polymer and Gel,TE357.4
  18. The Experimental Study of Polymer Flooding in LD10-1 Oilfield of Bohai Sea,TE357.46
  19. Research on Chemical Plugging Technology for High Permeable Zones in Thich Layers,TE358
  20. For dye-sensitized solar cells AS resin -based polymer gel electrolyte studies,TM914.4

CLC: > Industrial Technology > Oil and gas industry > Oil and gas development and mining > Oil field of Applied Chemistry
© 2012 www.DissertationTopic.Net  Mobile