Synthesis and Magnetic Properties of Mesoporous Metal Oxide Use Nanocasting

Author: GuXiaoJian
Tutor: JinHongXiao; GeHongLiang
School:
Course: Materials Physics and Chemistry
Keywords: mesoporous material metaloxide nanocastng hard template
CLC: TB30
Type: Master's thesis
Year: 2012
Downloads: 62
Quote: 0
Read: Download Dissertation

Abstract


Abstract： Mesoporous metal oxides possess excellent catalytic, photovoltaic,electromagnetic properties due to the diversity of the valence state, and haveapplications in many fields, such as solid catalytic, magnetic materials and lithiumbatteries. Synthesis of the ordered structure of the metal oxide based on nanocastingroute is arousing increasing interests in recent years. Many researches have beenfocused on mesoporous metal oxide to investigate the relationship between theregulation of the fine structure of magnetic metal oxides and magnetic behavior.To acheave highly ordered mesoporous metal oxides structure, it is of crucialimportant to adjust the regulation of the hard template pores. Herein, the synthesiesof the hard templates （FDU-12and SBA-16） were first studied. By controlling of thehydrothermal temperature, the synthesis temperature and the TEOS concentration,the pore stuctrues were finely adjusted.Then, face centered cubic ordered mesoporous Co3O4magnetic material wereprepared via the nanocasting route using FDU-12as hard template with differentpore size. The replicas show ordering from sub-nanometer size to micrometer size:1)the walls are highly crystalline;2) a highly ordered3D pore structure is observed;3)the particles are several micrometers in size which compose of nano-spheres. It wasdemonstrated that the sphere diameter （wall thickness） and the distance between thespheres （pore size） in the mesoporous Co3O4can be varied systematically within therange18.2-24.8nm and12.2-9.1nm. We have also studied their rmagnetic behaviorby using the temperature dependence of the magnetization and the applied magneticfield dependence of the magnetization. It was found that that the factors which affectthe magnetic behavior in our Co3O4nano-sphere system are not only the size effectbut also the distance between the spheres at the nanoscale.Thirdly, a series of hollow structure of mesoporous iron oxide nanospheresM-α-Fe2O3, M-Fe3O4and M-γ-Fe2O3were synthesized using concentrated H2SO4treated FDU-12as hard template by impregnation method. Differnet with Co3O4 samples, hollow α-Fe2O3spheres rather then mesoporous solid sphere were obtainedafter the replicating process. The hollow α-Fe2O3spheres were then transformed intoM-Fe3O4in reduction atmospheres （H2/Ar,5/95） and further transformed intoγ-Fe2O3through oxidation. The results show high specific surface area of107.9and91.5and88m2/g for M-α-Fe2O3, M-Fe3O4and M-γ-Fe2O3respectively. Magneticmeasurement showed that remanent magnetization of the M-α-Fe2O3wasMs=0.02283emu/g. The Tbof the M-Fe3O4and γ-Fe2O3were190°C and185°C,the specific saturation magnetization were53.8emu/g and36.1emu/g, and thecoercivity were1.8Oe and11Oe which can emerge superparamagnetic and class ofthe superparamagnetic effect.

Related Dissertations

  1. Research on Calcium Magnesium Bioactive Materials for Bone Regeneration,R318.08
  2. New graphite and magnetic properties of mesoporous carbon composites and environmental applications,X703
  3. Synthesis and Application Control mesoporous materials,TB383.4
  4. Studies on the Determination of Bisphenol A as Well as on the Simultaneous Determination of AA, UA and XA Using Nano-mesoporous Silica Modified Carbon Paste Electrode,O657.1
  5. Preparation and Application of C-MCM-22 Composite Zeolites,TB383.4
  6. Enhanced Heterogeneous Asymmetric Catalysis Via the Cooperation between the Immobilized Chiral Amine and Achiral Silanols of Mesoporous Support,O643.36
  7. Study on Cr-based Catalysts for Vapor-phase Fluorination to Synthesis CF4 and Preparation of β-AlF3 with High Surface Area,O643.32
  8. Investigation on Synthesis and Antibacterial Property of Mesoporous ZnO,TB34
  9. Study on Synthesis and Acid-base Bifunctionalized Mesoporous Materials MCM-41,O613.72
  10. Studies on the Determination of Bisphenol a as Well as on the Simultaneous Determination of AA, UA and XA Using Nano-mesoporous Silica Modified Carbon Paste Electrode,R927
  11. Synthesis of Hierarchically Porous Materials with Phenolic Resin as a Hard Template,TB383.4
  12. The mesoporous electrode material and its super capacitor performance,TM53
  13. Mesoporous ZSM-5 zeolite synthesis, characterization and catalytic hydrogenation performance evaluation,O643.36
  14. Preparation of Mesoporous Materials Supported Metal Catalysts and Their Application in Glucose Catalytic Oxidation,O643.36
  15. Preparation of Mesoporous Materials Templated by Gelatin and Its Study in the Immobilization of Lipase,TB383.4
  16. Preparation of Mesoporous TiO2 and Study of the Catalytic Property,TB34
  17. Study on Preparation of Mesoporous Ni/CeO2 Catalyst for Water Gas Shift Reaction,O643.36
  18. Synthesis and Characterization of Hierarchical-Structured Mordenite,O643.36
  19. Preparation of Tubular Composite Carbon Membrane for Gas Separation,TQ028.8
  20. The Preparation and Application of Silica-based Mesoporous Materials and Modified Sugarcane Bagasse in Phosphate Adsorption,X703
  21. Study on the Preparation and Properties of MCM-41-Rare Earth Complexes,O482

CLC: > Industrial Technology > General industrial technology > Materials science and engineering > General issues of engineering materials
© 2012 www.DissertationTopic.Net  Mobile