Influence of Ni-P Electroless Platting on 6063 Aluminum Alloy and Research on Modification of YG8 Hard Alloy after High Current Pulsed Electron Beam Irradiation

Author: ChuZuo
Tutor: RenZuo
School: Liaoning Technical University
Course: Materials Processing Engineering
Keywords: High current pulsed electron beam Electroless Ni-P plating YG8 hard alloy Microhardness Wear resistance
CLC: TQ153.1
Type: Master's thesis
Year: 2010
Downloads: 28
Quote: 0
Read: Download Dissertation

Abstract


High current pulsed electron beam is developing as a useful tool for surface modification of materials in recent years. When concentrated electron flux transferring its energy into a very thin surface layer within a short time, superfast processes such as heating, melting, evaporation and consequent solidification, as well as dynamic stress induced may impart the surface layer with improved physico-chemical and mechanical properties. This paper presents our research work on influence of electroless Ni-P plating on 6063 aluminum alloys and surface modification of YG8 hard alloy with high current pulsed electron beam equipment of type Nadezhda-2. Microstructure formed in the surface layers of treated samples are characterized by metallographic microscope, SEM, X-ray diffractometry, EPMA. Meantime, we also measure the Microhardness, wear resistance and roughness before and after high current pulsed electron beam treatment.Influence of electroless Ni-P plating on 6063 aluminum alloys with high current pulsed electron beam: The HCPEB irradiation could replace the pre-treatment of aluminum substrate as required in ordinary chemical plating with a decreased surface roughness of Ni-P ally plating layer. The plates exhibit an amorphous microstructure as demonstrated by XRD analysis. While the plates produced with the routine of HCPEB irradiation, activation and chemical plating give good quality and wear resistance, when using HCPEB irradiation of 10 pulses, even better than that of traditional chemical plating technique. And meanwhile, it has good binding force with substrate.Research on modification of YG8 hard alloy with high current pulsed electron beam: The HCPEB irradiation led to the melting and smoothing of irradiated surface. The WC hard particles changed to be regular and round, and dissolved partially into the Co bonding base. Peaks belonging to the Co3W3C phase were detected for the sample treated with 23.4 KV for 3 pulses. With the increase of the number of pulses up to 50, the peaks of Co3W9C4 phase was concomitantly recorded with those of the Co3W3C phase. The microhardness from the original HK 2180.8 increased to HK 3523.6 and the wear resistance was improved about 19%, the roughness of YG8 hard alloy after HCPEB treatment is a little height relative to initial state, but still smoothness and flat.

Related Dissertations

  1. Multicomponent gradient composition of rigid composite film cutter,TG71
  2. NiTi alloy coated stainless steel surface preparation,TG174.44
  3. Carbon steel liquid plasma electrolytic carbonitriding research,TG156.8
  4. Failure Analysis and Processing Technology Improvement of the Bicycle Flywheel Parts and Its Molding Die,U484
  5. Effect of Dentin Demineralization Processed by Solution with Ethylenediamine Tetraacetic Acid,R781.2
  6. Experimental Study on the Application Three Kinds Glutinous Material to Preventive Restoration,R783
  7. Experimental Study of Cold Light Bleaching on Dentin Surface Microhardness,R781.05
  8. Study on the Ni-nWC Nano-Composite Coating by Electroplating,TG174.4
  9. Research on Microstructure Evolution in Pre-heat Treatment and Cold Ring Rolling,TG142.15
  10. The Structure and Properties of Laser Alloying Layers Coated with Sub-Micron Ceramics,TG174.44
  11. The Microstructure and Phase Transformations of the New High Chromium Ferritic Heat-Resistant Steel,TG142.73
  12. A Study on Microstructure and the Wear Resistant of Laser Cladding Ni/WC Composite Coating,TG174.44
  13. Study on the Wear Resistant of Ni-Based Tungsten Carbide Composite Coating in Different Depths,TG174.4
  14. Al_2O_3/Al wrapped powder and nano gradient coating of metal substrates,TG174.4
  15. Preparation on the PPS/PES Based Antifriction Composite,TQ320.7
  16. Corrosion Resistance Andmechanical Property of AZ31 Magnesium Alloy by Ion Implantation,TG174.3
  17. Study of Super-hard Multi-constituent Composite Nitride Reactive Films,TG174.4
  18. Technology and Property of Composite Coating by Arc Spraying Feeding from Outside,TG174.4
  19. Study on Aluminium Matrix Multilayered Composite Produced by Accumulative Roll Bonding,TG339
  20. Research on NdFeB Electroless Plating Ni-P-Al2O3 Alloy,TQ153
  21. Surface Integrity in Hard Milling H13 Steel,TG54

CLC: > Industrial Technology > Chemical Industry > Electrochemical industries > Electroplating industry > A single metal plating
© 2012 www.DissertationTopic.Net  Mobile