Research on reliability of wafer level chip size package thermal - Mechanical

Author: HongRongHua
Tutor: Wang
School: Fudan University
Course: Materials Physics and Chemistry
Keywords: Wafer level chip scale package thermal-mechanical reliability statisticalanalysis failure analysis fatigue failure model
CLC: TN405
Type: Master's thesis
Year: 2012
Downloads: 125
Quote: 0
Read: Download Dissertation

Abstract


With the miniaturization and high density improving of electronic packaging, wafer level chip scale package (WLCSP) has been developed in the past few years and become one of the most advanced packaging concepts.RDL and Bumping technology have been used in WLCSP, which greatly decrease packaging volume. It fulfills the demand for small, lightweight and portable handheld electronic devices. WLCSP is typically used without underfill, so when WLCSP were mounted on the board, the coefficient thermal expansion (CTE) mismatch between silicon and printed board (PCB) causes a reliability issue. The solder joints will deform plastically and rise to crack generation and grow, which leads to the complete failure of the solder joints. Thus, the solder joint thermal-mechanical reliability of WLCSP is a prime concern in its application. In the thesis, we combined finite element method (FEM) with reliability experiments to analyze the thermal-mechanical reliability of WLCSP. The major contents include:To begin with, the effect of micro-solder joint design parameters on its thermal-mechanical reliability was analyzed. The design parameters which have significant effect on thermal stress of solder joint and under bump metal (UBM) were obtained by2D finite element simulation. Furthermore, full-factorial experiment and analysis of variance (ANOVA) were used to exhibit quantitative sensitivity information of design parameters.Besides, thermal stress and strain distribution of WLCSP was analyzed when it was under thermal cycle loading by3D finite element analysis (FEA).The3D submodel simulation was carried out to show the effect of solder joint material type, shape and radius on its thermal-mechanical reliability. The elastic-plastic-creep constitutive model was used and effect of temperature profile on its reliability was analyzed.Furthermore, thermal shock and thermal cycle experiment were carried out when WLCSP were assembled on PCB board, and reliability result such as characteristic life was got. Failure mechanism was discussed by failure analysis method such as X-ray and SEM. Finally, experiment and simulation result were combined to get fatigue life model which build up relationshipbetween thermal shock and thermal cycle.The results revealed that (1) solder joint radius is critical factor for thermal stress of solder joint,passivation diameter and solder joint radius are critical factors for thermal stress of UBM.(2) With the increased of distance between solder joint and center location, the maximum thermal stress and strain increased. The corner solder joint is the critical one. Solder joint material type and shape had significant influence on thermal stress of solder joint and UBM, respectively. The maximum stress of critical solder joint was decreased with the increase of solder joint radius.(3)There are two failure models of solder jointsin thermal-mechanical reliability test. Firstly,"V shape" crack generated and grew between solder joint and UBM. Secondly,"reciprocal V shape" crack generated and grew between solder joint and copper pad. The relationship between inelastic strain energy density and reciprocal of ramp rate can be fitted as exponential curve. When dell time and temperature range dwell was fixed, the fatigue life of critical solder joint was the function of ramp rate. The relationship between thermal shock and thermal cycle can be built up by this function.

Related Dissertations

  1. Research on the Failureanalysis of Plate Heat Exchanger,TK172
  2. Research on the Metal Erosion-corrosion Base on a Failure Analysis about the Elbow,TG172
  3. Al Wire Bonding Failure and Automatic Optical Inspection on Power Device Leadframe,TG441
  4. The production-proven 45nm NOR Flash,TP333
  5. Advanced EFA electrical failure analysis the positioning technology PFA physical verification technology research,TN407
  6. GaAs heterojunction and a high electron mobility transistor technology to improve the yield of the device,TN405
  7. TSV interconnect technology Reliability,TN405
  8. The Application of Failure Analysis for DRAM Product,TN407
  9. On the Dipole Transmitter Testing Method of Cross-dipole Acoustic Well Logging Instrument,P631.83
  10. Solder joint reliability problems unleaded stacked CSP package drop test,TN405
  11. ESD Protect Circuit and Failure Analysis in Semiconductor IC,TN407
  12. Mobile phone printed circuit board solder joint cracking and failure blind hole Characterization Analysis and Research,TN929.53
  13. Based on the reliability test PCBA failure mechanism and numerical simulation,TN405
  14. Integrated Circuit Failure Analysis Investigation,TN406
  15. Research of the Fault Analysis and Fault Location of Power Cable,TM755
  16. Heavy Truck Crankshaft Performance Analysis of Heat Treatment Process,TG156.82
  17. Experimental Research on Fatigue Failure of Connecting Nodes with High-strength Bolts,TU391
  18. Failure Analysis on Superheat Section Connecting Pipe Flange of Ethylene Cracking Furnace,TQ221.211
  19. Analysis and Research for CT Equipment Malfunction,R812
  20. Defective Carburizing Layer Related to Internal Oxidation and Its Influence on Service Properties,TH140
  21. Study on the Impact of Flexible Pressurized Anchor’s Structure Parameters and Wall Rock Pressure on Anchoring System,TD353.6

CLC: > Industrial Technology > Radio electronics, telecommunications technology > Microelectronics, integrated circuit (IC) > General issues > Manufacturing process
© 2012 www.DissertationTopic.Net  Mobile