Preparation and Surfance Modification of Nano-sized TiO2 and Their Properties of Anti-ultraviolet

Author: LuHongRong
Tutor: ZhengMin
School: Suzhou University
Course: Textile Chemistry and Dyeing and Finishing Engineering
Keywords: nano-sized TiO2 multi-hydroxy silane couple agent surface modify anti-ultraviolet finishing
CLC: TB383.1
Type: Master's thesis
Year: 2010
Downloads: 260
Quote: 3
Read: Download Dissertation

Abstract


The synthesis and application of nano-scale TiO2 attract interest in materials research. And the nano-scale TiO2 can be used widely in many fields such as photocatalst,sterilization,environment et al. Because ultrafine TiO2 is strong polarity material, the nanm-scale TiO2 can not be dispersed in non-polarity solvent well and is easy to agglomerate in the polarity solvent. In order to improve the dispersity in the polarity or non-polarity solvent ,surface treatment of ultrafine titania is necessarily so that it can widen the application fields.In the paper, Nano- TiO2 was synthesized through the sol-gel technique which was simple and green,and Laser Particle Size Analysis,XRD,IR,TG,SEM were used to characterize the properties of the as-synthesized samples. Well-dispersed nano-sized TiO2 slurry in water medium with high concentration was prepared through the coordination action using silane coupling agent and multi-hydroxy compound. And we discuss the application property on textiles.The main research work and results are as follows:（1） The precursor of nanometer TiO2 is synthesized with low-temperature of liquid process,and process was optimized by using tetra-butyl titanate and paraffin as the raw materials , and by changing the conditions such as raw material ratio , reaction temperature. Anatase,rutile and mixed nano- TiO2 were synthesized by changing the curing temperature.（2） Nano-sized TiO2 was modified by the high energy ball milling, using silane coupling agent with multi-hydroxy compound as bridge group. The modification process was optimized by changing the types of silane couple agent,the content of silane couple agent,the pH value of dispersion, the time of milling. Well-dispersed nano-sized TiO2 slurry in water medium with high concentration was prepared through the coordination action using silane coupling agent and multi-hydroxy compound. The coordination action and mechanism was discussed by characterizing the microstructure of the modified TiO2.（3） The cotton textile treated by modified nano-TiO2 slurry shows substantial anti-UV properties When the optimum finishing technology condition is carried out as following: nano-TiO2（Rutile） content 4 g/L , dipping temperature 60℃, baking temperature 150℃. The UPF value of cotton textile is 60.04 and strong washing fastness is also obtained.（4） The silk textile treated by modified nano-TiO2 slurry shows substantial anti-UV properties When the optimum finishing technology condition is carried out as following: pH 7, nano-TiO2 content 6 g/L , dipping time 50min, baking temperature 140℃. The UPF value of silk textile is 66.21 and strong washing fastness is also obtained.In the paper, the precursor of nanometer TiO2 is synthesized with paraffin as dispersant for the first time.The technology is a simplification of multi-procedures,such as traditional preparation,aging,drying,calcinating processes and rubbing. Well-dispersed nano-sized TiO2 slurry in water medium with high concentration was prepared through the coordination action using silane coupling agent and multi-hydroxy compound.The process will provide a reference for other nanoparticles.

Related Dissertations

  1. Studies on the Synthesis and Bioactivity of Novel Substituted Isoxazoline and N-Methylisoxazolinium-Salt Derivatives,TQ450.2
  2. Synthesis and Properties of Cu～(2+)-OMMTs Flame Retardant and Smoke Suppressant of PVC,TQ320.4
  3. Nano TiO_2 synthesis, surface treatment and anti- reunification research,TB383.1
  4. Research on SMC System with Rapid Initation and High Filling,TB332
  5. Study on the Synthesis, Characterization, and Photocatalytic Performance of Novel Nano-photocatalysts,X505
  6. Preparation and Modification of Supported Nanosized TiO2 Photocatalyst by MOCVD and Its Application in Water Treatment,X703.5
  7. Theoretical Investigation on Organic Molecules-Catalyzed Reaction and Organic Functionalization on the Si(100)-2×1 Surface Using DFT Methods,O643.32
  8. Preparation and Photodegradation Property for Organic Pollutants of Magnetically Separable Photocatalyst,X52
  9. Photodynamic Inhibition Mechanism of Nanosized TiO2 and New Amphiphilic Phthalocyanine Zinc Photosensitisers in Liver Cancer Cells,R735.7
  10. Preparation and Surface Modification of Nano-sized TiO2 and Anti-uv Performance on Fabricas,TB383.1
  11. Study on in Vivo Biological Toxicology of Titanium Dioxide Nanoparticles,X174
  12. Studies on Hydrothermal Synthesis of Nanosized Titanium Dioxide with Different Crystal Structures and Their Photocatalytic Activities,O643.36
  13. The nanometer TiO_2 Films hybrid study the physical and chemical properties,O643.3
  14. Surface Modification of the Nanocrystalline TiO2 and Its Application in the Environmentally Friendly Pesticides,TQ450
  15. Preparation and Visible Light Responsive Modification of Nanisized TiO2 Photocatalyst,TB383.1
  16. Study on Modified Nano-Titanium Dioxide Catalyzed Ozonation for Degradation of Oxalic Acid,X703
  17. Preparation of Carbon Molecular Sieve Memberane and Application for Hydrogen Separation,TB43
  18. Preparation of ITO Quai-1D Nanostructures by Sol-Gel Method Combined with Porous Anodic Aluminum Oxide Template,TB383.1
  19. Study on the Synthesis Bi3.25La0.75Ti3O12（BLT） Nanotubes and Nano Wires,TB383.1
  20. Hydrothermal Synthesis of Oxide Hollow Spheres,TB383.4
  21. Preparation and Electrocaloric Effect of BaxSr1-xTiO3 Ferroelectric Thin Films,TB383.2

CLC: > Industrial Technology > General industrial technology > Materials science and engineering > Special structural materials
© 2012 www.DissertationTopic.Net  Mobile