The Study on Thermoplastic Polyurethane Elastomers

Author: LiZuo
Tutor: ZhangJunYing
School: Beijing University of Chemical Technology
Course: Materials Science and Engineering
Keywords: thermal polyurethane chain extender Hydroxy-terminated polystyrene SPUS
CLC: TQ334.1
Type: Master's thesis
Year: 2010
Downloads: 749
Quote: 1
Read: Download Dissertation

Abstract


Thermal polyurethane elastomers are widely used in various industries such as mining, oil field, machinery, transportation, and architecture because of their excellent physical chemical and mechanical properties, the melt fluidity is also important to the processability of thermal polyurethane elastomer, the thermal polyurethane elastomers could be used more widely with both high mechanical properties and melt fluidity. However, the molecular weight, melt fluidity and mechanical strength are mostly contradictory, and it is difficult to be controlled in synthesis.For the purpose of improving the mechanical property while maintaining the thermoplastic of TPU, hydroxy-terminated polystyrene was used to compounded with polyurethane prepolymer. A series of polystyrene-polyurethane-polystyrene (SPUS) based on hydroxy-terminated polystyrene and polyurethane prepolymer were prepared by solution polymerization, which advances a new way to modify polyurethane by polystyrene. The structure and morphology of SPUS were characterized by FTIR, GPC, DMA, XRD, TEM. The results of TEM revealed that PU possesses the ability to coordinate with PS, resulting in the phase separation in the SPUS. Effects of the mass fraction and the molecular weight of hydroxy-terminated polystyrene on the mechanical properties of SPUS were investigated. The results showed that SPUS possessed relatively high tensile strength and elongation at break than TPU under the approximate molecular weight circumstances while maintaining approximate melt fluidity. the increase in mass fraction of PS could increase the tensile strength of SPUS, when the molecular weight and mass fraction of hydroxy-terminated polystyrene is 10000 and 25%, SPUS possessed the best mechanical properties.A series of thermal polyurethane based on polyether polyols as soft segments, Diphenylmethylene diisocyanate (MDI) and micromolecular diatomic alcohol as hard segments were synthesized by prepolymer method. The effect of isocyanate index, chain extender, the mole ratio of mixed chain extender to the properties of thermal polyurethane were discussed. The results showed that thermal polyurethane possessed comparatively better mechanical properties and higher fluidity when the NCO/OH is 0.99; Polyurethane hot melt adhesive based on bisphenol A possessed higher melt index, and thermal polyurethane based on diethylene glycol and bisphenol A when the n(bisphenol A)/n(diethylene glycol) is 1/3 maintain excellent mechanical properties and melt fluidity after treated by high temperature.

Related Dissertations

  1. The Synthesis and Properties Research of High Hydrophilic Polyurethane,TQ323.8
  2. Peptide derivatives based on the new three synthetic polyurethane chain extender,TQ323.8
  3. Preparation of Collagenase Sensitive Polylactic Acid Block Copolyesters by Chain Extension,R318.08
  4. Modification of PLA and Application of the Modified PLA in PLA/Starch Blends,TQ320.7
  5. Aqueous polyurethane resin thermal design, preparation , and the thermal properties of,TQ323.8
  6. Chain Extension of Recycled PET by Reactive Extrusion,TQ323.4
  7. Study on Modification and Fiber Formation of Poly(3-Hydroxybutyrate-Co-3-Hydroxyvalerate) (PHBV),TQ342
  8. Study on the Molecular Wcight and Structual Control of Polylactide Acid by Melt Polycondensation,TQ316.33
  9. Study on Toughening Modification of the PET as the Engineering Plastic,TQ323.4
  10. Studies on the Molecular Design and Modifications of Biodegradable PBS-based Polyesters,TQ323.41
  11. Studies on the Modification of R-PET by Chain Extension and Toughness Enhancement and the Crystallization of PET,TQ323.41
  12. Study on Reactive Extrusion of Carbon Dioxide and Propylene Oxide Copolymer,TQ320.6
  13. Structure and properties of rigid polyurethane foam damping material,TQ323.8
  14. Study on Control of Synthesis Reaction Rate and Performance of Polyurea,TQ630.1
  15. Synthesis, Structure and Properties of Pui,TQ334.1
  16. Synthesis and Characterization of High Solid Content Polyurethane Dispersion Containing Carboxylic and Sulfonic Groups,O633.1
  17. Synthesis and Evaluation of the Acid Resisitant High Temprature Acid Thinckening Agent,TE39
  18. Thermal Degradation and Modified Chain Extended of PLA,O631.3
  19. Study on Novel Polyurethane Chain Extander Based on Quadruple Hydrogen Bond,TQ316.33
  20. Biodegradable polyester poly (butylene succinate) (PBS) Modification Processing,TQ320.6

CLC: > Industrial Technology > Chemical Industry > Rubber Industry > Thermoplastic elastomers > Polyester elastomer
© 2012 www.DissertationTopic.Net  Mobile