Synthesis and Properties of Graphene Oxide/Manganese Oxide/Polyaniline Composites

Author: YaoTianYuan
Tutor: HaoQingLi
School: Nanjing University of Technology and Engineering
Course: Materials Science
Keywords: Graphene oxide manganese oxide polyaniline ternary composites supercapacitor
CLC: TB332
Type: Master's thesis
Year: 2014
Downloads: 45
Quote: 0
Read: Download Dissertation

Abstract


Carbon, manganese oxide and polyaniline are three kinds of commonly used materials for supercapacitors. In this thesis, a ternary nanocomposite of graphene oxide (GO)/manganese oxide/polyaniline (PANI)(GOM) was prepared by soft chemical methods, and its reduced composites obtained under different conditions were studied. Fourier transform infrared spectrometer (FT-IR), energy dispersive spectrometer (EDS), X-ray diffraction analyzer (XRD), Raman spectrum analyzer (Raman) and transmission electron microscopy (TEM) were used to analyze the microstructure and morphology of the composite materials. Electrochemical workstation and Land battery system were used for testing electrochemical properties. The main results are as follows:(1) A graphene oxide/manganese oxide/polyaniline ternary composite was prepared at room temperature by one-step method, using KMnO4as the oxidant, aniline as reducing agent. The microstructure of ternary composite is sheet-like. It showed good electrochemical performance with the specific capacitance of about323.8F·g-1and the capacitance retain proportion is nearly76%after600cycles.(2) Three ternary nanocomposites of RGOM were obtained under hydrothermal and normal pressure conditions at90℃using4M and8M NaOH. The manganese oxides in three composites showed one dimensional nanofiber structures in different degrees. The result showed that the harsh reaction conditions (such as hydrothermal method or high concentration of alkali) are favorable for the formation of the nanofiber structure. Among three reduced composites, the highest specific capacitance is about333.8F·g-1and the capacitance retain proportion is nearly73%after850cycles.(3) RGOM4with the smooth nanofiber-like structure was prepared by the treatment using4M NaOH at120℃. While RGOM5obtained using8M NaOH showed a rough and sheathed nanofiber-like structure. The composites exhibited great electrochemical performance due to the specific nanostructure. The specific capacitance of RGOM5is about343.8F·g-1. The capacitance retain proportion is nearly100%after800cycles, indicating high stability of this electrode material. RGOM5is a good candidate for surpercapacitor electrode materials.

Related Dissertations

  1. The Preparation of Polyaniline-Metal Complex and the Study on Its Catalytical Property,O634
  2. Preparation and Anticorrosion Properties of Doped Polyaniline/Epoxy Coating,TQ637
  3. Preparation and Property Study of Polyaniline/Polyester Composite Conductive Fabric,TS195.6
  4. Research on Electrochemical Synthesis and Application of Conductive Polyaniline,O633.21
  5. Polyaniline / short fiber reinforced natural rubber properties,TQ330.1
  6. SnO 2 / CNTs composite Controllable Preparation and Gas Sensitivity Study,TB383.1
  7. Preparation of polyaniline nanostructures , characterization and biomedical applications,TB383.1
  8. The Study of Conductive Polymer Sound-absorption Film Material,TB383.2
  9. Flexible Electrodes Material Based on Polypyrrole Composites and Capacitance Properties for Supercapacitor,TM53
  10. Synthesis and Characterization of Polyaniline Micro/nano Structure and Its Composites,TB383.1
  11. Polyethylenimine-Grafted Graphene Oxide as an Efficient Gene Delivery Vector,R450
  12. Prepration of Manganses Dioxide and Investigation on the Performance of Supercapacitor,TM53
  13. Preparation, Characterization, and Application in Polymer Composites of Graphene,TB383.1
  14. Study on Electhode Materials of High Surface Area Activated Carbon with Different Pore Structures for Supercapacitor,TM53
  15. Preparation of Metal Oxides Electrode by Eelectrospining and Studies on Electrochemical Supercapactors,TM53
  16. Tuning Fluorescence and Catalytic Characterization of Polyaniline,O643.32
  17. Research of the Influence of La2O3 on the Formation and Performance of PANI Nanofiber Materials,TB383.1
  18. In-situ Composition of Polyaniline and Titanium Oxides,O634
  19. Template-free Synthesis and Properties of Polyaniline Nanostructures,TB383.1
  20. Study on Synthesis and Properties of Conductive Polyaniline and PANI/GO Composite Material,TB383.1
  21. Structural Control of Hierarchical Porous Carbon and Its Composites and Their Electrochemical Performance,TM53

CLC: > Industrial Technology > General industrial technology > Materials science and engineering > Composite materials > Non-metallic composite materials
© 2012 www.DissertationTopic.Net  Mobile