Synthesis and Properties of Light-weight Mullite Refractory by Coal Gangue

Author: LiuJingJing
Tutor: LiYuanBing
School: Wuhan University of Science and Technology
Course: Materials Physics and Chemistry
Keywords: coal gangue mullite light-weight brick light-weight castables
CLC: TD849.5
Type: Master's thesis
Year: 2013
Downloads: 56
Quote: 0
Read: Download Dissertation

Abstract


Coal gangue is a solid wastes resulting from the process of coal mining and washing,accounting for10~20%of the original coal production. Accumulated coal gangue not onlyinvaded land and but also caused other environment pollution. Therefore, fabrication oflight-weight mullite refractory by coal gangue and its performances were studied in this article.The main contents in this paper include two parts. Firstly, influence of sintering temperature,content of coal gangue, content of pore-forming and its particle size as well as content of kyaniteon the properties and microstructure of light-weight bricks were investigated when light-weightmullite brick was prepared by coal gangue as main materials. Properties comparison betweenlight-weight mullite bricks prepared by coal gangue and light-weight mullite bricks at home andabroad were subsequently assessed. Secondly, influence of sintering temperature and coalgangue content on the properties and microstructures of both M70and M55light-weightaggregates were studied when light-weight mullite aggregates were fabricated by coal gangue asmain materials. In addition, M75, M55and common M65light-weight aggregates in marketwere prepared light-weight castables. The detailed results were listed as follows:(1)To light-weight mullite bricks: The light-weight mullite bricks with bulk density ofabout0.83g/cm~3,cold comprehensive strength up to2.5MPa,linear change ratio on reheatingachieved0.24%at1450℃×3h, thermal conductivity of about0.217W/(m·K)（300℃）ismanufactured when coal gangue content is added to60wt%, content and particle size ofpore-forming is50wt%and165um respectively, and kyanite is10wt%. The physical propertiesof prepared light-weight mullite bricks are compared with the bricks at home and abroad. Itsthermal conductivity is lower.(2)To light-weight mullite aggregates: The M70light-weight mullite aggregates with bulkdensity of about1.21g/cm~3, water absorbing ratio up to53.7%, packing density of about0.71g/cm~3and cold comprehensive strength achieved5.24MPa was fabricated at1450℃when coalgangue is added to50wt%; The M55light-weight mullite aggregates with bulk density of about1.32g/cm~3, water absorbing ratio of about42.09%, packing density of about0.97g/cm~3and coldcomprehensive strength of about4.28MPa was fabricated at1300℃when coal gangue is addedto50wt%. The physical properties of light-weight castables manufactured by M70and M55arecorresponding to castables prepared by M65in market and its thermal conductivity is lower，providing an effective way of utilization of coal gangue.

Related Dissertations

  1. Experiments on Microwave Radiation Activation YunNan Unburned Coal-gangue Concrete,TU528
  2. Plastic combined with relatively corundum - mullite composites impact,TQ175.1
  3. Preparation of Mullite from Kaolin Via a Wet Chemistry Method,TQ175.6
  4. Study on Production of PAC by Coal Gangue and Its Application,X703.5
  5. Research on the Environmental Geochemistry of Hazardous Element in Coal Gangue of Fushun Coalfield,X142
  6. Study of Performance of Cordierite Combined Mullite Products,TQ175.71
  7. Analysis on Attrition of CFB in Mixture Combustion of Coal and Coal Gangue,TK229.6
  8. The Study on Preparation and Properties of Wear Resistant Ceramic Coating,TQ637
  9. Study on Safe and Effective Backfill Technology for Steeply Dipping Seam Mining,TD823.7
  10. Microstructure and Oxidation Protection Behavior of Mullite/SiC Coating on C/C Composites,TB332
  11. Application of Wireless Sensor Nets in Environment Monitor Svstem,TN929.5;TP212.9
  12. Study on Dynamic Behavior of Gangue Pollutants Transport Coupled Flow and Temperature,X50
  13. Reductive decomposition of phosphogypsum reductant screening and influencing factors,X705
  14. Investigation on Factors Affecting Properties of Micropored Lightweight Mullite Aggregate,TF065.1
  15. Preparation Organic Multi-Fertilizer Contain Silicon from Coal Gangue/Coal Ash and Crop Straw,TQ444
  16. The Study on Preparing the Porous Mullite with Al Powder and Fly Ash,TQ175.712.1
  17. Comprehensive Stability Research and Governance on Coal Gangue Slope,TU43
  18. A Study on Different Pretreatment Methods for Preventing Coal Slagging,TD94
  19. Zirconia composite ceramic materials research,TQ174.1
  20. The andalusite performance Castables research aluminosilicate,TQ175.73
  21. Study of Synthesis of Mullite by Micro-crystal Muscovite from West Sichuan,P578.959

CLC: > Industrial Technology > Mining Engineering > Mining > Coal and oil shale underground gasification > Comprehensive utilization of coal > Gangue, stone coal
© 2012 www.DissertationTopic.Net  Mobile