Research of Increase the Slag Resistance Function of Magnesia Carbon Brick by Changeding Graphite

Author: ChenYang
Tutor: ZhangLing
School: Liaoning University of Science and Technology
Course: Materials Science
Keywords: MgO-C brick Changed graphite Expansion ratio Slag resistance
CLC: TQ175.1
Type: Master's thesis
Year: 2012
Downloads: 18
Quote: 0
Read: Download Dissertation

Abstract


In order to prolong the service life of magnesia carbon brick which using in the slag line of ladle , we deal with the graphite with sulphuric acid and nitric acid ,and put the changed graphite into the brick, we study the effects of different quantity of the expanded graphite on the bulk density, apparent porosity, compressive strength at room temperature, bending strength at high temperature, thermal expansion and slag resistance,and using polarzation microscope to analyze the microstructure of the sample.The result showed that: a little changed graphite of magnesia carbon brick have a little negative affect to the performance,but the changed graphite at high temperature can remedy the matrix contraction and crack between the bricks, thereby increasing the slag resistance; when the quantity of changed graphite is 0.6%,the crack between aggregate and matrix is narrowest, the slag resistance is best.

Related Dissertations

  1. 2.25Cr1Mo0.25V steel deformation defects in the process control simulation study,TG316
  2. Strength characteristics of reinforced expansive soils,TU443
  3. Study on Composition,Structure and Properties of ρ-AL2O3 Bonded Alumina-Magnesia Castable,TB321
  4. Preparation and Properties of Al_4SiC_4,TQ175.1
  5. Experimental Study on the Axial Mechanical Behavior of Preloaded Circular Concrete Columns with CFRP Confinement,TU375.3532.3
  6. After adding inorganic solid foam characteristic parameters of experimental study,TD752
  7. To sudden expansion Down Floor stream eliminate hydraulic characteristics of,TV135.2
  8. A Study on Slag Resistance and Anti-hydration Properties of Calcia-rich Magnesia-Calcia Refractories Used for VOD,TF769
  9. Carbon aluminum titanium nitride composites synthesized by hydrothermal method corundum material impact,TQ163.2
  10. Study on Thermo-mechanical Properties and Behavior of Slag Corrosion Resistance of β-Sialon Containing MgO Based Castables,TG233
  11. Study of the Performance, Configuration and Particular Flow Phenomena of an Ejector,TQ051
  12. Synthesis and Properties of ZrO2-C-ZrB2 Composites,O611.3
  13. Study on Characteristics of the Paraffin Used in Thermostatic Valve,TH134
  14. Study on Effect of Additives on Properties of Al2O3-SiC-C Castable for Iron Trough,TF52
  15. The Erosion Mechanism of Ladle Slag Lining Brick with Different Slagging Condition,TF703.6
  16. Research on Caustic Castable for Slag Line of Secondary Refining,TF769
  17. Research on Improving Service Life of MgO-C Bricks for LF Furnace Slag Line by Changing Composition of LF Slag,TF065.12
  18. The Effect of Zircon on the Performance of A2O3-SiC-C,TF57
  19. Investigation and Development of Magnesia-zircon-chome Non-carbon Refractory Castables for Ladle Slag Line,TQ175.73
  20. Investigation the Extrusion Foaming Process of Polyproylene by Using Supercritical CO2 as Foaming Agent,TQ320.663

CLC: > Industrial Technology > Chemical Industry > Silicate > The refractory industry > Basic theory
© 2012 www.DissertationTopic.Net  Mobile