Preparation and Performance Research of Lithium Ion Battery Anode Material Li4Ti5O12

Author: ZhengShaoWei
Tutor: XuYunLong
School: East China University of Science and Technology
Course: Materials Science and Engineering
Keywords: Lithium ion battery Li4Ti5O12 Solid-state method High-rate Li~+ diffusion coefficient
CLC: TM912
Type: Master's thesis
Year: 2012
Downloads: 186
Quote: 0
Read: Download Dissertation

Abstract


Spinel Li4Ti5O12 is a promising lithium ion battery anode material. It has some evident advantages:there is negligible volume change during charge/discharge process (the so-called "zero-strain insertion material"), so it possesses excellent reversibility; its Li-insertion potential is at about 1.55V vs. Li+/Li, which is high than the reduction voltage of common electrolyte; the diffusion coefficient is 2×10-11 cm2/s, so it has excellent lithium ion mobility that promising for high-rate battery applications. Furthermore, this material accommodates Li+ with theoretical capacity of 175 mAh/g. Compared with graphite anode material, Li4Ti5O12 is considered to be of better rate performance and safety.Anatase TiO2 and Li2CO3 were used as raw material to synthesize Li4Ti5O12 by solid-state method to study the optimal synthesis conditions of Li4Ti5O12. The moral ratio of n(Li)/n(Ti) was 0.84. Water was used as dispersant and ball-milling was used as mixing method. The result showed that the optimal synthesis conditions of Li4Ti5O12 were sintering 12h under 800℃. The initial discharge capacity at 0.5C was 135.8 mAh/g.Li4Ti5O12/C composite was prepared with the optimal synthesis conditions above and Li-citrate was used as carbon source and part of lithium source. The average particle size of as-prepared material was 70nm, while that of virgin Li4Ti5O12 synthesized under the same conditions was 600nm. The material showed excellent electrochemical performances, especially high-rate performances. The initial discharge capacity at 20C was 121.1 mAh/g, and after 100 cycles, it was still 106.1 mAh/g.PITT method was used to measure Li+ diffusion coefficient of Li4Ti5O12. The result showed that DLi+, ranged from 10-12 to 10-10cm2s-1 at various electrode potentials; core/shell structure was formed during charging/discharging process.

Related Dissertations

  1. Investigation on the Modification and Electrochemical Performance of Li4Ti5O12 Anode for Lithium Ion Battery,TM912
  2. Effect of Water Binder on the Electrochemical Performance of Graphite,TM912
  3. Porous electrode material of vanadium pentoxide Synthesis, Characterization and Properties,O614.511
  4. Graphite anode low temperature performance influencing factors and improving research,TM912
  5. New lithium -ion battery anode material Li 4 Ti 5 O 12 Preparation and Modification,TM912
  6. Prepared the Electrode Material and Electrochemical Properties of Lithium-ion Battery,TM912
  7. Study on the Silicon-based Composites as Anode Materials for the Lithium Ion Batteries,TM912
  8. Preparation and Properties of Li4Ti5O12 as Anode Material of Lithium-Ion Batteries,TM912
  9. Bi series Fe , Co oxide preparation , structure and performance,O614
  10. In LiFePO_4 cathode materials for lithium-ion battery production process and properties,TM912
  11. Investigation on Preparation and Performance of Li4Ti5O12,TM912.9
  12. INvestigation on Synthesis and Doping Modification of Li4Ti5O12,TM912
  13. High-temperature lithium titanate solid phase synthesis and recycling,TM912.9
  14. Synthesis Buy Liquid Method and Modification of Lithium Titanate Anode Material for Lithium Ion Battery,TM912.9
  15. Li4Ti5O12 Prepared by Solution-combustion Method as Anode Material for Li-ion Battery,TM912
  16. Lithium-ion battery anode material Modification of Li_4Ti_5O_12,TM912.9
  17. Study on the Performance and Synthesis of Li4Ti5O12,TM912
  18. Investigation on Synthesis and Modification of Li4Ti5O12 as the Anode Material for Lithium-Ion Batteries,TM912
  19. Synthesis of Li4Ti5O12 as Anode Material for Lithium Ion Battery,TM912
  20. Synthesis and Characterization of Li3v2(po4)3 As Cathode Materials for Lithium-ion Batteries,TM912
  21. Analysis and Applications of Battery Temperature Fields in Electric Vehicles,U469.72

CLC: > Industrial Technology > Electrotechnical > Independent power supply technology (direct power) > Battery
© 2012 www.DissertationTopic.Net  Mobile