Preparation and Research on Water-borne One Component Polyurethane Wood Finish and Primer

Author: XuNing
Tutor: ChenZhongHua；ChenHaiHong
School: South China University of Technology
Course: Materials Engineering
Keywords: one component polyurethane water-borne wood finish film forming at low temperature primer stuffing
CLC: TQ630.7
Type: Master's thesis
Year: 2011
Downloads: 175
Quote: 0
Read: Download Dissertation

Abstract


This paper mainly studied the formula composition of water-borne one component polyurethane wood finish and its primer, and prepared the wood surface paint and supporting primer with excellent comprehensive performance. The whole paper includes two parts as follows:In the first part, influences of the film performance were studied by using different kinds of resins and additives, prepared the wood surface paint with excellent comprehensive performance. The results showed that the polyurethane emulsion A and acrylic emulsion D with the mass ratio of 1:1 as film forming matter, the film presents optimal comprehensive performance. The FT-IR analysis shows that the two resins occur to cross-linking reaction and hydrogen bond interaction. DSC results showed that polyurethane A’s glass transition temperature (Tg) is 22.5℃, and presents a good film performance at low temperature; acrylic resin D’s glass transition temperature (Tg) is 50.9℃, it can provide high hardness for film ,but need to increase the amount of film forming additives to present a good film performance at low temperature; Airex 901W as defoaming agent, the film presents good surface effect with the amount of 0.02% (mass percentage); Tg700 as wetting agent, the film presents most level-off and a good adhesion with the amount of 0.4%; dipropylene glycol n-butyl ether (DPnB) and dipropylene glycol methyl ether(DPM) with the mass ratio of 1:1 as film forming additives, the film presents good film surface effect and high hardness at low temperature 5℃w ith the am ount of 3.5% respectively; ZC 501 as thickening agent, the film presents high gloss and good construction performance with appropriate dosage; TS-100 powder as matting agent, the matting effect is excellent with less dosage and hardness of paint film was increased; SN-5040 as dispersant, matt finish has excellent storage stability.In the second part, the formula composition of supporting primer was studied, varieties of special acrylic emulsions for wood primer, film forming additives, grinding stuffing, anti-sedimentation additives, and different dosages’influence to the film were discussed, prepared the wood primer with excellent comprehensive performance. The experimental results showed that the acrylic resin H has excellent mechanical properties and chemical resistance performance; DSC results showed that acrylic resin H’s glass transition temperature (Tg) is70.9℃, dipropylene glycol n-butyl ether (DPnB) and dipropylene glycol methyl ether (DPM) as film forming additives, the film presents good film surface effect and high hardness at low temperature℃5 with the amount of 3.5% and 6.5% respectively; talcum powder MK-7 with 1250 mesh number as grinding auxiliaries, the film presents well burnished ability with the amount of 10%; cellulose ether E230X as anti-sedimentation additives, the wood primer has optimal stable storage performance with the amount of 0.2%.

Related Dissertations

  1. Development of EST-SSR Primers and Application in Analysis of Genetic Realtionships in Tree Peony,S685.11
  2. Synthesis and Biocompatibility of different types of hydrophilic surface - modified polyurethane,R318.08
  3. Hydrophilic structure of different types of surface -modified polyurethane material and coagulation 12 factor nine peptide fragments,and fibrinogen P1 fragment of computer simulation of the interaction,O631.3
  4. Establishing and Applying a Rapid Detection System of Yersinia Enterocolitica,TS207.4
  5. Research on PSA/Cotton Blend Fabric of Coatinging of Water Resistance and Moisture Permeability,TS195.6
  6. Prototype Development of Intimate Apparel Mannequin,TS941.2
  7. Synthesis and Properties of the new anti-clotting material in modified ammonium phosphate zwitterion,R318.08
  8. The Research of SSR for Distinctness and Uniformity Evaluation of Henan Wheat (Triticum Aestivum) Varieties,S512.1
  9. Preparation and Application of Water-based Polyurethane to Improve Wet Rubbing Fastness,TS193.2
  10. Synthesis, Modification of Dimer Acid Diisocyanate and It’s Application on Fabric Finishing,TS190.2
  11. Synthesis of Water-based Polyurethane and Applications As Paper Strength Agent,TS727
  12. Evaluation of Biocompatibility of Titanium Alloy Coating by Polyurethane,R318.08
  13. Poly ( urethane - vinyl imidazole ) copolymer / graphene nano- composites,TB383.1
  14. The Study of the Surface Treatment of TA2 Titanium Alloy for Shipbuilding and Its Matching Primer,U668.2
  15. Identification and Characterization of Differentially Expressed Genes in Ovary and Testis of Marsupenaeus Japonicus,S917.4
  16. Study on Gene sh2 Identification and the Heredity of Main Qualitative Traits in Super Sweet Corn,S513
  17. Study on Waterborne Polycarbonate Urethane in Leather Finishing,TS529.5
  18. The Preparation and Property Research of Exterior Water-based Anticorrosive Paints for Containers,TQ630.7
  19. Study on Rapid Detection of Vibrio Cholerae by Loop-Mediated Isothermal Amplification,R440
  20. The Synthesis of 4-(1,4-naphthoquinone-2-yl)-N-hydroxyphthalimide and Its Catalytic Behaviors,O625.6
  21. Association of HLA-DRB1~*0701、DRB1~*1201 Alleles with Vitiligo in the Uyghur Nationality of Xinjiang Region,R758.41

CLC: > Industrial Technology > Chemical Industry > Paint Industry > General issues > Coating products
© 2012 www.DissertationTopic.Net  Mobile