Synthesis of Polyamide-amine with Pendant Benzoxazine Groups and Their Thermal Curing Behavior

Author: ChenJunRen
Tutor: LuYanBing
School: Hunan University
Course: Chemical Engineering and Technology
Keywords: benzoxazine PAMAM curing kinetics dendrimer
CLC: O633.5
Type: Master's thesis
Year: 2010
Downloads: 93
Quote: 0
Read: Download Dissertation

Abstract


Benzoxazine is a novel thermosetting resin, it’s synthesized by phenols, primary amines and formaldehyde through condensation reaction. It has well molecular-design properties. The modification of polybenzoxazine was focused on synthesizing monofunctional and difunctional benzoxazine monomers. However, the study of trifunctional and multifunctional benzoxazine monomers were few reported. In this paper, benzoxazine resin with low curing temperature was synthesized through the molecular design by using entire generation PAMAM as multiamines.Two novel dendrimer compounds with pendant benzoxazine named 1.0G Benzoxazine(1.0G BZ) and 2.0G Benzoxazine (2.0G BZ), were prepared by 1.0G PAMAM and 2.0G PAMAM, phenol, paraformaldehyde.OG Benzoxazine (0G BZ) was prepared by ethylenediamine, phenol, paraformaldehyde. The structure of 1.0G BZ and 2.0G BZ were characterized by FT-IR and’H NMR. By plentiful solubility tests, we found out good component solvent which could remove impurities of 1.0G BZ and 2.0GBZ.Curing behavior of OG BZ, 1.0G BZ and 2.0G BZ were carried out by differential scanning calorimetry (DSC), the curing peak temperature(Tp) of 1.0G BZ and 2.0G BZ were 203.6℃and 213℃, respectively. Compared with the Tp of OG BZ(225℃), the curing temperature was decreased by the introduction of PAMAM, meanwhile, the curing temperature of PAMAM-based benzoxazine is enhancing with the increase the generations of PAMAM and the amount of oxazines, as a result, the Tp of 2.0G BZ is higher than 1.0G BZ.. Compared with the traditional benzoxazine resins, the curing temperature of 1.0G BZ reduced 22℃. The initial curing temperature(Ti) of 1.0G BZ was lower due to the cavity it contained, phenol as excess reactants was not removed completely and resdued in the cavity. When 1.0G BZ is curing, phenol as catalyst provides active hydrogen to catalyze 1.0G BZ ring-openning, therefore, the initial curing temperature of LOG BZ was lower. The curing kinetics of LOG BZ was explored by non-isothermal DSC. The basic cure process was determined through extrapolation. The Flynn-Wall-Ozawa isoconversional method and Kissinger method were used to evaluate the effective activation energy (Ea). The activation energy values(Ea) were 109.15 and 103.11 kJ·mol-1, respectively. The curing reaction order was one order by Crane method.Thermal properties of cured resin of 1.0G PAMAM. 0G PBZ、1.0G PBZ and 2.0G PBZ were investigated by thermogravimetrical analysis (TGA). The char yields of 1.0G PAMAM、OG PBZ、1.0G PBZ and 2.0G PBZ were 53.30%,37.61% and 26.34%,18.05%, respectively. The results showed that the increasing amount of benzoxazine groups can enhance heat resistance, but importing the higher generation of PAMAM results in descending the thermal performance. The later factor is dominant, so the thermal properties of 2.0G PBZ descend in general. The char yeild of 1.0G PBZ is higher than that of 1.0G PAMAM by 19.56%, which show the outstanding thermal properties of the 1.0G PBZ. Thermal gravimetric analysis of 1.0G PBZ and 2.0G PBZ in different atmosphere indicated that 1.0G PBZ and 2.0G PBZ had excellent thermo-oxidative stability. DSC results showed 1.0G PBZ had high glass transition temperature (Tg=161.4℃), higher than the traditional difunctionality of benzoxazine.

Related Dissertations

  1. Synthesis and Self-assembly of Dendrimer and Their In-situ Modification of PMMA,O631.3
  2. Synthesis and Characterization of Star Copolymers,O631.3
  3. Preparation and Properties Research of Carbon Fiber Reinforced Epoxy Resin Prepreg and Composites,TB332
  4. Preparation of Epoxy Resin Cured with Latent Curing Agent at Moderate Temperature,TQ323.5
  5. Bis-GMA -based organic monomer molecular design and its impact on the performance of dental composite resin,R783.1
  6. Dendrimer coated gold nanoparticles as non-viral vectors for gene transfer studies,R450
  7. Dendrimer stabilized bismuth sulfide nanoparticles synthesis , characterization and application of CT imaging,O614.532
  8. Condensation of DNA Caused by PAMAM and Photodetachment of H~- Near the Metal Surfaces,Q523
  9. Studies on Design, Synthesis and Properties of Fatty Polyamines-bonded Silica-gel Adsorption Materials,TB34
  10. Synthesis and Application of Polyamidoamine Dendrimer with a Triethanolamine Core,TB383.1
  11. Studies on Synthesis and Demulsification Performance of Modified Polyamidoamine,TE39
  12. Synthesis and Characterization of the S-triazine Derivatives with Phenoxy, Bi-naphthoxy and Azo-phenoxy,O621.2
  13. Unsaturated Polyester Resin Modified by Unsaturated POSS,TQ323.41
  14. Study on the Preparation and Properties of PDMS-Based Composite Adhesive Membrane and Coatings,R944
  15. Synthetic Methodology Research of Indolizine Derivatives,O621.3
  16. Preparation, Characterization of PAMAM Dendrimers-coated Liposomes and Evaluation for Ophthalmic Drug Delivery,R283
  17. Synthesis, Characterization and Catalytic Activity of Polyamidoamine-salicylaldehyde Schiff Base Dendrimer Palladium Complex,O634
  18. SiO_2 modified rigid foam molding composites and performance analysis,TB33
  19. Synthesis and Properties Research of Poly (Ethylene Glycol)-b-dendritic Poly (Aspartic Acid)s,O631.3
  20. Study on Preparation, Solidification and Properties of Benzoxazine Modified with Lignin,TQ320.1
  21. Synthesis and Characterization of Novel Self-Curing Epoxy Tesin,TQ323.5

CLC: > Mathematical sciences and chemical > Chemistry > Polymer chemistry ( polymer ) > Miscellaneous Chain Polymers > Heterocyclic polymer chain (chain polymer containing heterocyclic )
© 2012 www.DissertationTopic.Net  Mobile