Synthesis and Modification of IPDI-Based Waterborne Polyurethane

Author: WangYao
Tutor: YangJingHui
School: East China University of Science and Technology
Course: Materials Science and Engineering
Keywords: IPDI-Based Waterborne Polyurethane Mixed polyether polyols external crosslinking agent DEA mechanical property
CLC: TQ323.8
Type: Master's thesis
Year: 2012
Downloads: 209
Quote: 0
Read: Download Dissertation

Abstract


IPDI-based waterborne polyurethane was synthesized and modified to get low modulus and high strength PU film for application in gloves and so on.First, the preparation of linear waterborne polyurethane emulsion was studied using polyethylene glycol (PPG) as soft segment and isophorone diisocyanate (IPDI) as hardsegment. It was found that the higher the DMPA content, the film was much easier to absorb water and DMPA of 7% was better. When nNco/noHis about 3.0, film with a lower modulus, higher strength and a suitable elongation at break could be obtained. By adjustment and optimization, basic formula was obtained for preparation of PU film.To improve the mechanical properties of PU film, especially the tensile strength, cross-linked polyurethane film was prepared by adding some types of external crosslinking agent. It was found that cross-linking agent containing carboxyl group could make the emulsion instability, while the cross-linking agent containing hydroxyl group have little effect on stability.To improve the cross-linking efficiency, terminal hydroxyl group content was increased. DEA contains a secondary amine group, had good result than TMP which contains three hydroxyl groups. When DEA was added after the chain extender reacted completely, the water-based PU had a good stability. The higher the DEA content, the better the water resistance and the lower the molecular weight. When the DEA content of 0.5%, and adding BI7963 with 2.8%, the elongation at break, tensile strength and modulus of PU film was up to 995%,14.9MPa and 2.1MPa at 100% elongation modulus, respectively. The stretch recoverability was also good.

Related Dissertations

  1. The Evaluation Research of a University’s Education Investment Benefit Based on the DEA,G647.5
  2. Universities RD input-output hysteresis and evaluation of the relative efficiency,G647
  3. Research of Chinese City Commercial Banks’ Cost Efficiency Based on Data Envelopment Analysis,F224
  4. Research on the Industry Innovation Efficiency of Shanxi Province in the Economic Restructuring,F224
  5. A Study on Competitiveness Evaluation of Urban Commercial Banks in Shandong Province,F832.33
  6. Basing on Industry, Research on the Differences of Regional Innovation Efficiency in Our Country Tale the Large and Medium-Sized Industrial Enterprises as Example,F224
  7. The Analysis of the Financing Efficiency of the Photovoltaic Industry in Jiangxi Province Based on DEA,F426.6
  8. The Development Capability Study of Passenger Integration of the Urban and Rural Road,F542
  9. 440MPa grade high strength deep drawing steel (IF) Development,TG142
  10. High-strength alloy microstructure and properties of lead-based research,TG146.12
  11. The Multi-stage’s Evaluation and Application of Pre-bi-objective GDEA Model,O242.1
  12. Industrial innovation platform evaluation of the effectiveness of,F279.2
  13. Performance Evaluation Study on Listed Companies of Household Electrical Appliance Industry in China Based on DEA Model,F272;F426.61
  14. China's eastern , central and western regions and efficiency of investment activities RD Comparative Study,F224
  15. The Research of Corporate Governance Structure Based on the Present Situation of the Institutional Arrangement,F276.6
  16. Performance analysis of China Banking Electronic Banking,F832.2
  17. A Positive Study on the Efficiency of Commercial Banks in China,F224
  18. The development of microfinance and inclusive financial system research,F832.4
  19. 2124 aluminum alloy heat treatment on creep deformation aging effects,TG166.3
  20. Evaluation Study on Efficiency of Input-output of Biodiversity Conservation of Chongqing,X321

CLC: > Industrial Technology > Chemical Industry > Synthetic resins and plastics industry > Polycondensation resin and plastic > Polyurethane (poly carbamate ) and plastic
© 2012 www.DissertationTopic.Net  Mobile