The Preparation and Properties of Phosphorus-Containing Styrene/Acrylic Copolymer Flame-Retardant Adhesive

Author: HuangZuo
Tutor: CaiZaiSheng
School: Donghua University
Course: Textile Chemistry and Dyeing and Finishing Engineering
Keywords: flame-retardant adhesive phosphorus-combined styrene acrylate emulsion polymerization
CLC: TQ433.43
Type: Master's thesis
Year: 2012
Downloads: 109
Quote: 0
Read: Download Dissertation

Abstract


Acrylate adhesive have practical applications in construction industry, textile industry. But acrylate copolymer is mainly composed of carbon, hydrogen and oxygen. When they are used in the retardant field such as interior materials of public building and vehicle, they are requested to have flame-retardant properties. Adhesives always add flame retardants to provide flame retardant properties, but expense of stickiness as a price. In this paper, a series of polyacrylates were synthesized by copolymerized general acrylates with vinyl unsaturated phosphate monomers through pre-emulsified seed emulsion polymerization in order to prepare a phosphorus-combined adhesive. The flame retardant ability of the adhesive can be easily achieved with mixing a few inorganic flame retardant. So the compound adhesive had excellent performance of stickiness and flame retardance. The main conclusions can be drawn as follows:Firstly, adhesive SA was successfully synthesized by pre-emulsified seed emulsion polymerization with styrene (St), butyl acrylate (BA), ethyl acrylate (EA), methyl methacrylate (MMA) and acrylic acid (AA). The effects of the amount of St, emulsifiers and initiator, the polymerization temperature and the pre-emulsion dropwise time on emulsion and film properties were systemically investigated. The optimum polymerization process was obtained as follows: w(St):w(BA):w(EA):w(MMA):w(AA)=16:90:60:24:5,3% of emulsifier(m(Peregal O): m(SDS)=2:1),0.4% of initiator,30min pre-emulsion dropwise time. The product had milky blue light appearance,98% of monomer conversion rate, emulsion particle size<200nm, had excellent peel strength and film forming.Secondly, a flame-retardant styrene/acrylic copolymer adhesive(BSA) was successfully prepared with blending additive APP in SA adhesive. The effects of the amount of APP and St on emulsion stability, peel strength and flame retardant ability were systemically investigated. The thermal properties of BSA were studied by means of thermogravimetric analysis (TG). The results showed that BSA had good peel strength and flame retardant ability with used 20% of APP,9% of St.Thirdly, a compound flame-retardant adhesive(CPSA) was successfully prepared with blending a few additive APP in phosphorus-combined styrene/acrylic copolymer which was synthesized by pre-emulsified seed emulsion polymerization. The effects of the amount of vinyl unsaturated phosphate monomers, APP and St on emulsion stability, peel strength and flame retardant ability were systemically investigated. The thermal properties of CPSA and PSA were studied by means of thermogravimetric analysis (TG) and scanning electron microscope(SEM). The results showed that CPSA had good peel strength and flame retardant ability with used 4% vinyl unsaturated phosphate monomers and 12% of APP.

Related Dissertations

  1. The Preparation of Polyaniline-Metal Complex and the Study on Its Catalytical Property,O634
  2. Preparation and Characteration of Composite Microspheres with Dual-, Triple- Responsive Properties,O631.3
  3. Study of the Particles Design and Size Contorl in Styrene-Acrysic Emulsion Poltmerization,TQ316.334
  4. Core-shell polymer microspheres synthesis, modification and application,O631.3
  5. Synthesis of Fluorinated Short-chain Alkyl Acrylate Co-polymer Emulsion and Application on Texitle Finishing,TS195.2
  6. Study on Determination of Urinary Metabolites of Toluene, Styrene, N-Hexane by HPLC,O657.72
  7. Synthesis of Novel Stabilizers and Their Application in Miniemulsion,TQ316.334
  8. Chemical modification of the surface of carbon nanotubes and properties of,TB383.1
  9. Improve SBR conversion rate of,TQ333.1
  10. Crosslink Network Evolution and Stress Softening of Composite System of Butadiene Styrene Rubber and Metallic Methacrylate (Zinc、 Magnesium),TQ330.1
  11. Preparation of Imidization Products of PS-b-(alt) SMA and Application as Pour Point Depressant for Crude Oil,O631.3
  12. Mechanism of RAFT Emulsion Polymerization and Synthesis of Poly(Styrene-b-n-butyl Acrylate-b-styrene),TQ316.322
  13. Studies on Stability and Viscosity of Polymer/Polyether Polyols Suspension,TQ317
  14. Preparation and Characterization of Toughened Poly (Vinyl Chloride) Resins,TQ325.3
  15. Copolymerization Characteristics of TMI and Styrene,O631.3
  16. Synthesis of Eco-friendly Fluorinated Acrylate Copolymer and Its Application in Stone Protection,O631.3
  17. Research of Fluorinated Acrylate (Polyurethane) Copolymer Latex under Microwave Radiation,TQ316.334
  18. The Study of Silicon and Nano-Silica Modified Polyethylene Acrylate Latex,TQ630.4
  19. Synthesis of Fluorinated Copolymer and Its Application in Epoxy Coating,TQ630.4
  20. The new research system and application performance micro sol,TE39
  21. Research on Am/2-EHA Copolymer as Profile Control Agent,TE39

CLC: > Industrial Technology > Chemical Industry > Adhesive Industry > Synthetic adhesive > Rubber, resin as raw material adhesive > Synthetic resin adhesive of the raw materials
© 2012 www.DissertationTopic.Net  Mobile