Preparation and Application of Nonlinear Copolymer as Retanning and Filling Agent

Author: WangJiZuo
Tutor: LanYunJun
School: Wenzhou University
Course: Organic Chemistry
Keywords: amidation esterification aqueous solution polymerization emulsion polymerization retanning and filling agent
CLC: TS529.2
Type: Master's thesis
Year: 2011
Downloads: 29
Quote: 0
Read: Download Dissertation

Abstract


Retanning is important in the tanning process, which affects the properties of the leather. In recent years, the nonlinear polymers were used to prepare the retanning agents by leather researchers due to their novel structures and unique properties.In this thesis, diethanolamine and maleic anhydride were used to prepare nonlinear intermediate(DM). aqueous solution of the nonlinear retanning agents(PDMA) were prepared by acrylic acid and DM. And emulsion of nonlinear retanning agents were prepared by addition of 2-ethylhexyl acrylate into the prepared aqueous solution of the nonlinear retanning agents under the effect of mixed emulsifier. The researches include three parts.(1) Preparation of the nonlinear intermediate DMThe different factors of the monoacylation reaction between diethanolamine and maleic anhydride were investigated. The results showed that the optical conditions of monoacylation reaction: mole ratio of diethanolamine to maleic anhydride 1:1, reaction time 210min. the optical conditions of mono esterification was that: diethanolamine acidized by propionic acid, mass fraction of catalyst p-toluenesulfonic acid 0.55%(base on total mass of monomer), reaction temperature 90℃, reaction time 210min, mole ratio of diethanolamine to maleic anhydride 1:2.(2) Study on aqueous solution of the nonlinear retanning agents PDMAThe factors which affected the properties and percent conversion of double bond in DM were investigated and optimized by orthogonal test and by single factor experiment method. The results indicated the optical reaction conditions were that: n(DM):n(AA)1:6, mass fraction of initiator APS6%, the range of reaction temperature 84℃～86℃, dropping time of active monomer 2h, the neutralization time of intermediate 1.5h.The prepared retanning agents of PDMA series exhibited good acid resistance, alkali proof and salt resistance. Besides, they also exhibited excellent retanning and filling properties, strong selecting filling properties, and can partly avoid the negative effect on dying and fatliquoring.(3)Study on emulsion of nonlinear retanning agents PDEAThe factors which affected the products’stable properties and application performances were investigated and optimized by orthogonal test and by single factor experiment method. The results indicated the optical reaction conditions were that: n(DM-1):n(AA) is 1:6, mass fraction of 2-ethylhexyl acrylate 25%(base on total mass of monomer), mass fraction of initiator 6%, mass fraction of mixed emulsifier 11.2%, the range of reaction temperature 84℃～86℃, dropping time of active monomer 2h, the neutralization time of intermediate 1.5h, neutralizing agent ammonia.The prepared retanningand filling agents of PDEA not only exhibited the excellent properties of retanning agents of PDMA series, but also improve the properties of dying and fatliquoring. The treated leather showed good softness and fullness, plastic feel was not obvious.

Related Dissertations

  1. Penicillium Expansum TS414 Lipase in Pichia Pastori: Expression, Purification and Enantioselective Esterification of (R, S)-naproxen,Q814
  2. The Biodiesel Production from Wasted Edible Oil by Two Steps Catalyzed by Resin,TE667
  3. Study on the Synthesis and Properties of Poly(1,4-Cyclohexyledimethylene Terephthalate) (PCT),TQ323.4
  4. Biodiesel Production from Waste Oil and Study of Reduction of the Condensation Point,TE667
  5. Preparation and Characteration of Composite Microspheres with Dual-, Triple- Responsive Properties,O631.3
  6. Direct Oxidation of Primary Alcohols to Methyl Esters Catalyzed by Nano-Au/SBA-16 Catalyst,TQ225.241
  7. Core-shell polymer microspheres synthesis, modification and application,O631.3
  8. Synthesis of Fluorinated Short-chain Alkyl Acrylate Co-polymer Emulsion and Application on Texitle Finishing,TS195.2
  9. Intensification on Hydrolysis and Esterification Precess by Hydrodynamic Cavitation Technology in Biodiesel Preparation,TE667
  10. Synthesis and Properties of Functional Waterborne Polyurethane Coatings,TQ633
  11. Synthesis of Nobel Metal Nanoparticles in Spherical Polymer Brushes and Their Catalytic Activities,TB383.1
  12. Preparation of Novel Acrylic Polymer and Its Application on Cotton Fabric,TS195.2
  13. Superabsorbent salt tolerance studies,TQ324.8
  14. Synthesis and Application of Half-saturated Fatty Acid Alkanolamide Combined Fatliquor,TS529.4
  15. Study on Reduce High Acidity of Prickly Ash Seed Oil with Esterification,TS225.1
  16. PS/SiO_2 core-shell composite microspheres,TB383.4
  17. Organic acids control the synthesis of polyaniline satisfied / micron-sized structures,TB383.1
  18. Study on New Flocculants by Inverse Emulsion Polymerization and Its Performance,TQ314.24
  19. Synthesis of Poly (Butylene Succinate),TQ316.33
  20. Study on Acrylate Emulsion Pressure Sensitive Adhesive for Biological Surface,TQ436.3
  21. Study on the Preparation Andapplication in Textiles of Micropcms,TS101

CLC: > Industrial Technology > Light industry,handicrafts > Leather Industry > Raw materials and auxiliary materials > Auxiliary materials > Tanning agents,retanning agent
© 2012 www.DissertationTopic.Net  Mobile