The Research of the Synthesis and Properties of Several Mesoporous Oxides Materials

Author: GaoLan
Tutor: XiaoQi
School: Central South University
Course: Materials Science
Keywords: mesoporous BiVO4 TiO2 CuO photocatalysis
CLC: TB383.4
Type: Master's thesis
Year: 2011
Downloads: 135
Quote: 1
Read: Download Dissertation

Abstract


With the advantage of large specific surface area and ordered pore structure, mesoporous materials showed extensive application prospect in photocatality, adsorption and biology. In the past few years, study on synthesis and properties of functional mesoporus materials had become an important field for researchers. This thesis devoted to fabrication and performance study of types of mesoporous nano-semiconductor photocatalytic materials. Effective methods to synthetize mesoporous materials were found. And performance of as-synthesis samples via different methods was tested. The main contents were discussed as follows:(1) Ordered nanocrystalline mesoporous BiV04 with pure phase was successfully synthesized via nanocasting using cubic MCM-48 molecular sieves as hard template. Comparing with conventional BiVO4 synthesized by hydrothermal method, the nanocasting mesoporous BiVO4 have much higher specific surface of 22.9 m2.g-1, more ordered pore structure and smaller particle size (about 10nm), which decreased the recombination of optical excitation electrons and holes efficiently. As a result, the photocatalytic efficiency of mesoporous BiVO4 for xanthate in 90 mins reached up to 78%.(2) Highly visible light active mesoporous (C、W) doped/co-doped TiO2 were synthesized via hydrothermal method by controlling the dosage of inorganic titanium sulfate, glucose and sodium tungstate. The crytal size of as-synthesized samples was about 12nm and its surface area was greater than 100 m2.g-1. Its visible light absorbance enhanced with the increasing of the W doping amounts. W6+ played the role of the electron capture agent and transferring electron that well photoresponse performance under visible light was got. The photocatalyst doped with C 1.0% and W 10% showed the highest photocatalytic activity under visible light irradiation.(3) By means of capillary force, mesoporous CuO/SiO2 composites with high surface area were triumphantly synthesized via self-assembly basing on [Cu(NH3)4]2+ into the pore of well-organized molecular sieve. The results showed that:at the ratio of Cu:Si=1:2.5, surface area and pore volume of as-synthesized host-guest materials was 219 m2.g-1 and 0.3 cm3.g-1 respectively, and it exhibited a similar bimodal pore size distribution to the host sieve, distributing extensively at about 3nm. It exhibited fine adsorption charactors with methyl blue. Simultaneously, it revealed an excellent photocatalytic activity that 92% of xanthate was degradated in 90 min.

Related Dissertations

  1. Studies on the Synthesis and Technology of Dipentaerythritol and Its Derivative,TQ223.164
  2. The Preparation and Research of Magnetically Separable TiO2 Photocatalyst Nanofibers,TB383.1
  3. The Study of Preparation and Photocatalytic Activity of TiO2 by Electrospinning,O614.411
  4. Investigation of Fabrication, Characterization and Property of Fuctional Titanium Dioxide Nanoporous Materials,TB383.1
  5. Investigation of Preparation and Properties of Ordered Porous TiO2,TB383.2
  6. Photodegradation of Orange Ⅱ by Mesoporous TiO2,X791
  7. Inorganic filler of the modified polylactic acid,TQ320.1
  8. Copper oxide porous hollow microspheres Preparation and Characterization,O614.121
  9. Nano LaFeO 3 Controllable Synthesis and TiO 2 bridged construct composite photocatalyst,O643.36
  10. Preparation of Silica Hollow Spheres with Mesopores in the Walls,TB383.1
  11. Visible oxide catalyst with high activity and mechanism of Design and Synthesis,O643.36
  12. Preparation of Metal Oxides Electrode by Eelectrospining and Studies on Electrochemical Supercapactors,TM53
  13. Prepartion and Applicatons of Novel Flurescent Mesoporous Nanoparticles,TB383.1
  14. The Preparation and Properties Research on Anti-ultraviolet PVA Composite Films,TB383.2
  15. Modified Silica-Based Mesoporous Materials and Appliation in the Heavy Metal Adsorption,TB34
  16. Photoelectrocatalytic Characteristics of Different Kinds of Organic Compounds on TiO2 Nanotube Arrays,X703
  17. Preparation of Heterogeneous Metal Phthalocyanine Catalysts and Photodegradation of Toxic Organic Pollutants,X52
  18. Study on the Performance of Microwave-assisted Catalytic Oxidation of Volatile Organic Compound,X511
  19. Low-Temperature Sintering and Microwave Dielectric Properties of Ba2Ti3Nb4O18 Ceramics,TQ174.1
  20. BiVO 4 / bentonite Photocatalyst and Its Dyeing Wastewater Treatment,X791
  21. Composite Supercapacitor Electrode Materials Preparation and Properties,TM53

CLC: > Industrial Technology > General industrial technology > Materials science and engineering > Special structural materials
© 2012 www.DissertationTopic.Net  Mobile