600V VDMOS power device process optimization study
Author: RenChuan
Tutor: LiBingZong；TaoYouFei
School: Fudan University
Course: IC Engineering
Keywords: Power semiconductor device VDMOS process VGS（th） Polyimide
CLC: TN386
Type: Master's thesis
Year: 2011
Downloads: 51
Quote: 0
Read: Download Dissertation
Abstract
|
The optimization of high voltage VDMOS process is studied in this paper.Threshold voltage (VGS(th)) before optimization is higher than-design target. Gate oxide thickness and doping concentration (NA) of p type body are related with VGS(th). Through design of experiment, VGS(th) can be reduced without any gate oxide thickness loss by adjusting the implant dose of JFET, P-Body and N-Plus. Also, MOS channel function can be improved with lightly doped tilted implant applied in N-Plus. VGS(th) meets target after optimization with none effect to breakdown voltage, on-resistance and drain leakage current.Zero layer is needed to form alignment mark for following lithography layers. The experiments show it can be replaced by the field oxide structure which matches the requirement of alignment mark. It can be recognized by the lithography alignment system. The production cycle time and cost of this product are reduced after removing zero layer.To improve product reliability, Polyimide is coated on device surface as passivation layer. It was found peeled up at the corners of die. Base on analysis of Polyimide formation and experiment, this issue is resolved by setting Polyimide develop time shorter.After the process optimization, the device yield is higher than-95%, and cost down over 10%. The product, technique and process described in this paper are all from fab manufacturing. It can be used as a reference for people who study or produce similar high voltage VDMOS.
|
Related Dissertations
- 1,4 - bis (4 - amino-2 - (trifluoromethyl) phenoxy ) benzene -type Schiff base imide copolymer synthesis and characterization,O631.3
- Electrically Conductive Adhesives Based on Epoxy Resins Modified by Polyimide Powder with Carboxyl Groups,TQ433.437
- Units containing bibenzimidazole polyimide synthesis , structure and properties,TQ323.7
- Synthesis Study and Property Research on Reactive Endcapped Imide Oligomers,TQ323.7
- The Synthesis and Performance of Thermoplastic Polyimide Film Materials,TQ323.7
- Fabrication and Properties of Polyimide Composite Films with Low Thermal Expansion,TQ320.721
- Fabrication and Properties of Surface-Silvered Polyimide Fibers,TQ340.1
- Preparation and Property of Polyimide (PI) Solvent Resistance Nanofiltration Membrane,TQ320.721
- High-temperature and High Toughness Resistant Thermosetting Polyimide Resins and Their Composites,TQ323.7
- Preparation of Ployimide Solvent Resistance Nanofiltration Membrane,TQ323.7
- Research on Microstucture and Properties of Silived Polyimide Films Prepared Through All-Wet Process at Room Temperature,TQ320.721
- Novel Polyimide Containing Donor and Acceptor Moities Synthesis and Characterization,TQ323.7
- Synthesis and Properties of Sulfonated Polyimides Containing Benzimidazole Groups,TM911.4
- Synthesis and Properties of Novel Sulfornated Polyimides for Fuel Cell Application,TM911.4
- Study on Modification of Polyimide Nanofiltration Membrane,TQ028.8
- Carbon Molecular Sieves Derived from Bituminous Coal and Pore Structure Adjustment,TQ424.25
- Preparation of Modified Epoxy Based Electrically Conductive Adhesives with Polyimide and Study on Curing Reaction Kinetics of the System,TQ437
- New meta- structure of polyimide plastic powder Molecular Design, Preparation and Properties,TQ323.7
- Preparation and Performance of Low-temperature Pyrolytic Carbon Membrane from Polyimide,TQ028.8
- Crosslinking wholly aromatic polyimide synthesis and properties of,TQ323.7
CLC: > Industrial Technology > Radio electronics, telecommunications technology > Semiconductor technology > Field-effect devices
© 2012 www.DissertationTopic.Net Mobile
|