Preparation of Low Temperature Sintered Nanoscale Silver Paste

Author: WangShuai
Tutor: LiMingYu
School: Harbin Institute of Technology
Course: Materials Processing Engineering
Keywords: electronic packaging thermal interface materials low-temperature sintering nanoparticles
CLC: TB383.1
Type: Master's thesis
Year: 2010
Downloads: 564
Quote: 0
Read: Download Dissertation

Abstract


Thermal interface materials play an important role for the heat dissipation of integrated chips and other elements in electronic packaging. The heat-conducting property of traditional thermal interface materials such as thermally conductive adhesive and solder have not been competent, so that they have restricted the heat dissipation. Low-temperature sintered nanoscale silver paste which acts as a kind of thermal interface materials has high heat conducting property which the other thermal interface materials do not possess. However, this kind of thermal interface material has not been studied systematically inland. What is more, the related dispensation and technique abroad are still secretive. So, the content of this thesis is to study the recipe of this kind of thermal interface material and test the properties of low-temperature sintered nanoscale silver paste.Low-temperature sintered nanoscale silver paste is comprised of organic components and nanoscale silver particles. The fundamental principle of nanoscale silver paste is that with the temperature rises, the organic components burn out and the nanoparticles are sintered together. Moreover, the nanoparticles were connected with the substrate which is plated with silver by the mechanism of diffusion. The sintered silver layer has high heat conducting property. The thermal conductivity is 193.7W/(K·m). The shear strength of sintered joint is 37.5MPa.Because of the heat-proof restriction of the other materials in the system of electronic packaging, the sintering temperature must be controlled within a lower temperature range. The reason why we choose nanoparticles is that they possess so high surface energy that can reduce the needed sintering driving force which is sintering temperature dramatically.The main content of this thesis are as followed:(1) Resolve the problem that the agglomeration of nanoparticles. Both chemical approach and physical approach are adopted. Disperse the nanoparticles by adjusting the kind, dosage of dispersive and the time of supersonic.(2) The selection of organic components. The organic components must be stable chemically when they are mixed with nanoparticles. They also should be able to burn out at the temperature which below the sintering temperature so that they can not affect the heat conducting property of sintered silver layer. Moreover, they should not volatilize so quickly that make the screen-printing hard to be done. On the other hand, too slowly to volatilize will result in more defects after sintering process.(3) Observe the microstructure and test the properties of the low-temperature sintered nanoscale silver paste. Verify whether or not such thermal interface material is suitable for electronic packaging.

Related Dissertations

  1. Preparation and Bioavailability Evaluation of Fenofibrate Nanosuspension,R944
  2. Electroporation Assisted Surface-enhanced Raman Spectroscopy for Living Cells,R318.51
  3. Water-soluble hypocrellin / titanium dioxide dosing system and its properties of,TQ460.1
  4. A New Method for Thrombin Detection by Using Aptamers and Gold Nanoparticles,Q55
  5. Study on Electrochemistry and Raman Spectrum of Picoline Electro-Oxidation Beavior in Non-aqueous System,O626.321
  6. Inorganic filler of the modified polylactic acid,TQ320.1
  7. Complex functions drug-loaded microspheres and in spinal cord injury treatment Application of,R943
  8. Cyclodextrin -modified magnetic nanoparticles synthesis and study drug carrier,TQ460.1
  9. Nano LaFeO 3 Controllable Synthesis and TiO 2 bridged construct composite photocatalyst,O643.36
  10. Fabrications and Applications of Microelectrode Array of Silicon Dioxide Cavities and Magnetic Ferroferric Oxide Nano-Bioconjunctions,TB383.1
  11. Fabrication of a Uniform Surface Enhanced Raman Scattering Substrate and Its Application,O657.37
  12. Templated Synthesis of Surface Enhanced Raman Scattering Substrate and Its Application,O657.37
  13. The Synthesis, Assembly, and Property of Core-shell Structured Noble Metal Nanomaterials,TB383.1
  14. Fabrication of TiO2 and MoO3 Nanowires Based Sensor,TB383.1
  15. Green Synthesis of Ag Nanoparticles and Its Functionalities Research,TB383.1
  16. Multifunctional Magnetic Nanoparticles Used for EPR Bio-probes,TB383.1
  17. Preparation and Catalysis of Supported Palladium Nanoparticles Catalyst for Hydrogenation of 2-tertiary Butyl Anthraquinone to Produce H2O2,TQ123.6
  18. Synthesis of Silver Nanoparticles on Modified Multi-walled Carbon Nanotubes and Their Antimicrobial Effects,TB383.1
  19. Metal Nanoparticles Prepared in Spherical Polyelectrolyte Brush Nanoreactor and Their Catalytic Activity,TB383.1
  20. The Affect of Microstructure and Properties Adding ZrO_ 2 Nanoparticles on Carbon Steel,TG142.31
  21. Synthesis of Poly(Ethylene Glycol)-b-poly (γ-amino-ε-caprolactone) and Its Application for Drug Delivery,O631.3

CLC: > Industrial Technology > General industrial technology > Materials science and engineering > Special structural materials
© 2012 www.DissertationTopic.Net  Mobile