A Study on the Properties of Magnesium Oxysulfate Cementitious Material

Author: ZhuHuiRong
Tutor: RuanJiongZheng
School: Jilin Architectural and Civil Engineering
Course: Materials Science
Keywords: magnesium oxysulfate cementitious material modifier Double salt hydration mechanism
CLC: TQ132.2
Type: Master's thesis
Year: 2010
Downloads: 76
Quote: 0
Read: Download Dissertation

Abstract


Magnesium oxysulfate cementitious material has good performance with light weight, good volume stability, flexural strength, fire-resistance.Although the compressive strength of magnesium oxysulfate cementitious material lower than magnesium oxychloride cementitious materials, in its water resistance, environmental protection and without corrosion to steel, active suppression pantothenic frost etc. Magnesium oxysulfate cementitious material has its own unique special in the production of decoration materials have an advantage.In consequence,it is necessary to improve the performance of magnesium oxysulfate cementitious material.First of all, we try an experiemt of basic ratio of magnesium oxysulfate cementitious material at room temperature and found out the good molar ratio of MgO: MgSO4?7H2O, then we mixed with 19 kinds different types of additives based on the benchmark ratio and screened some additives can improve obviously the strength of magnesium oxysulfate cementitious material-citric acid, sodium citrate and sucrose.Optimized admixture content of additives by orthogonal design.In order to reduce micro-cracks and improve the water resistance of magnesium oxysulfate cementitious material,we performed the experiment of inorganic packings.The experimental results indicated that silica fume, fly ash filler not only increase the strength of magnesium oxysulfate cementitious material,but also improve the water resistance of magnesium oxysulfate cementitious material.The paper also discussed the temperature, humidity, age, magnesium oxide fine sulfur oxide and other factors on the impact of magnesium oxysulfate cementitious material strength, these results indicated that controlling the temperature in 20 ~ 25℃and grelative humidity at 60% can increase the strength of magnesium oxysulfate cementitious material. The 7d compressive strength of magnesium oxysulfate cementitious material accessed to 44.5MPa. This article also confirmed that the complex admixture of magnesium oxysulfate cementitious material at room temperature formed a new double salt phase by XRD, DTA, TG test methods.We observed the morphology of complex salt by SEM and found that complex salt is a small needle crystals,this small needle crystals made the complex salt forming good density, and improved the water resistance of magnesium oxysulfate cementitious material.The article also examined simply the hydration mechanism of magnesium oxysulfate cementitious material from the standpoint of thermodynamics and kinetics ,and made a useful exploration for increasing the use of magnesium oxysulfate cementitious material.

Related Dissertations

  1. Risk Analysis and Mitigation Experiment of Heavy Metal Pollution in Croplands in Vicinity of Pollution Sources,X820.4
  2. Elementary Exploration in Applying Vegetable Oil to Study and Make Phosphorite Flotation Reagents,TD923.1
  3. The Synthesis and Application of Cationic Modifier ZY on Cotton Fibers,TS190.2
  4. English Interpreting attributive noun phrase with multiple pre- study,H315.9
  5. SBS Content Testing and Quality Evaluation of SBS Modified Asphalt,U414
  6. The Research on Interface Mechanism and Performance for Crumb Rubber Modified Asphalt,U414
  7. Study on the Performance of Bamboo Charcoal as Soil Modifier,S156.2
  8. Research on Experiment and Evaluation of Sewage Sludge Used as Cover Material in MSW Landfill,X703
  9. Graphite furnace atomic absorption spectrometry method for ceramic materials,TQ174.7
  10. The PRRS Attenuated Vaccine Immunity Effect Appraises and Oderman-1 to Its Immunity Effect Influence,S858.28
  11. Study on Wet Surface Modification of CaCO3 Powder Filled LDPE,TB332
  12. Research on Synthesis of High Purity Nanometer Magnesium Oxide via Chemical Precipitation,TB383.1
  13. Studies on Preparation and Performance of Nanometer Layered MnO2,TB383.1
  14. The performance of the core-shell structure modifier AIM toughened poly ( methyl methacrylate ),TQ325.7
  15. The functionalized ACR toughened PA6 research,TQ323.6
  16. Performance optimization of the elastomer toughened PVC,TQ325.3
  17. The microscopic structure of the core-shell particles on the fracture toughness of PA6,TQ323.6
  18. Study and Application of Minor Clinker Magnesium Slag Cementitious Material,TU526
  19. Screening Study on Activity of Ameliorating Insulin Resistance in Vitro of Berberine Hydrochloride Structure Modification Based on 3T3-L1 Pre-adipocytes,R587.1
  20. Magnesite Magnesium Hydroxide Preparation and Surface Modification of Nano Research,TB383.1

CLC: > Industrial Technology > Chemical Industry > Inorganic compounds, the chemical industry of the metal elements > Section II group metal elements of inorganic compounds > Inorganic compounds of magnesium
© 2012 www.DissertationTopic.Net  Mobile