Synthesis and Morphology Characterization of Indium Oxide （In2O3） Crystals

Author: TianShuai
Tutor: DongGuoYi;WeiZhiRen
School: Hebei University
Course: Optical Engineering
Keywords: hydrothermal synthesis In2O3 aftercrystal bixbyite-type octahedron
CLC: O614.372
Type: Master's thesis
Year: 2009
Downloads: 33
Quote: 0
Read: Download Dissertation

Abstract


In this paper, In(OH)3, InOOH and In2O3 crystals were synthesized by hydrothermal method with pure water or 1 mol/L KOH,5 mol/L KOH as mineralizer, and In(OH)3 as the precursor. The fill factor is 35%, and the reaction time is 24 h. The rules of phase transformation of In(OH)3, InOOH and In2O3 were explored at different temperatures of 200℃,250℃and 350℃. and their morphologies were analyzed.It is found that the phase transformation and obvious secondary crystallization of In(OH)3 did not occurred on the condition of pure water at 200℃. The crystals didn’t have specific morphology. And the crystals transformed to InOOH at the temperature of 250℃and 350℃.When 1 mol/L KOH and 5 mol/L KOH was used as mineralizer at the reaction temperature of 200℃, the crystals turned up secondary crystallization. Especially when using 5 mol/L KOH as mineralizer, the largest crystals scale reached to 20μm and the smallest was less than 100 nm, displaying the process of multiple-crystallization. When the temperature was up to 250℃, InOOH and a few In2O3 crystals were synthesized. When above 350℃, cubic bixbyite-type phase In2O3 were synthesized. The side length of the crystal exceeded 50μm, exposing{001},{010},{100} and{101} facets.The two phases of marketable-In2O3 crystalls, cubic bixbyite-type struture and corundum-type structure, converted into cubic bixbyite-type In2O3 crystalls with 3 mol/L KOH as mineralizer. The fill factor is 35%, and the reaction temperature is 430℃. It is indicated cubic bixbyite-type phase was more stable than corundum-type phase on the condition of hydro-thermal synthesis.The cubic bixbyite-type In2O3 crystalls were also synthesized with mineralizer of 10 mol/L KOH, the fill factor of 35%, reaction temperature of 430℃, and with precursor In2O3 and 10% mol ratio FeSO4·7H2O by hydro-thermal method. The morphology had been obviously changed by doping with Fe into In2O3. The crystalls exposed high index crystal {101} facets. Part of synthetic products were ferromagnetic Fe3O4 spinel, exposing {111} facets.The cubic bixbyite-type In2O3 crystalls were also synthesized by chemistry vapour method. They appeared octahedron shape, exposing {111} facets. The maximum length of edge was 50μm.

Related Dissertations

  1. Hydrothermal Synthesis of Oxide Hollow Spheres,TB383.4
  2. Flexible,rigid,Synthesis and characterization of mixed ligand complexes,O621.1
  3. Syntheses, Structures and Properties of Coordination Polymers with Aromatic Dicarboxylates,O631.1
  4. Syntheses, Structures and Properties of Metal-organic Coordination Polymers Based on Long-Chain Aromaticmulticarboxylate,O631.3
  5. Study on the Hydrothermal Synthesis of Spinel-type Lithium Ion-sieve and Ni-Cr Doping,P579
  6. Study on the Preparation of Potassium Ion Sieve Membrane of High SiO2/Al2O3 and Its Application Performance,P746.2
  7. Fly ash zeolite synthesis and treatment of coking wastewater,X703
  8. Selective Oxidation of Propane to Acrylic Acid over Mo-V-Sb-O Catalysts,TQ225.131
  9. Studies on the Hydrothermal Synthesis and Self-Assembly Principle of Dicarboxylic Acid Coordination Polymers,O631.1
  10. Preparation, Doping and Gas-Sensing Properties of Indium Oxides,O614.372
  11. Synthesis and Application of Mesoporous Alumina,O614.31
  12. Synthesis and Properties Research of Polyoxometalate Single Crystal Based on Phosphotungstate Anions,TB321
  13. Preparation and Properties of Cerium-based Compounds （CePO4, CeO2） Luminescent Materials,TB383.1
  14. Synthesis and Fluorescence Properties of Y2O3 :Eu3+,TB34
  15. Design and Synthesis of Microporous Compounds Based on Metal Clusters (Oxygen、Halides),O621.2
  16. Syntheses, Structures and Properties of Some Lacunary Polyoxometalates and Transitional Metal Tungstosilicates,O611.4
  17. Synthesis and Application of Titanium Silicate-1 Films,O614.411
  18. The Synthesis and Crystal Morphology Controlling of Zeolite-L,O643.36
  19. Synthesis and Photoluminescence Properties of Aligned ZnO Nanowire Arrays by Hydrothermal Synthesis Method,TB383.1
  20. Preparation of Nano/Micro Materials from the Solvent Extraction System,TB383.1

CLC: > Mathematical sciences and chemical > Chemistry > Inorganic Chemistry > Metal elements and their compounds > Section III group metal elements and their compounds > The gallium Vice family ( Ⅲ A group metal elements ) > Indium In
© 2012 www.DissertationTopic.Net  Mobile