Study on Preparation of New Type Coated TiH2 in Aluminum Production

Author: ZhangCongRong
Tutor: ZhaoKang
School: Xi'an University of Technology
Course: Materials Science
Keywords: Coated Vesicant Hydrogen Release Aluminum foam
CLC: TB383
Type: Master's thesis
Year: 2004
Downloads: 154
Quote: 0
Read: Download Dissertation


Technical Difficulties - this study prepared for the melt foam legal system of aluminum foam blowing agent into the high temperature aluminum melt quickly release hydrogen, limits the the homogenization unit operation time, proposed to use chemical-coated TIH 2 foaming agent to prepare aluminum foam, the main research the TiH 2 chemical foaming agent coated. Prepared surface coated Al 2 O 3 , the SiO 2 and composite coated Al 2 O 3 and SiO 2 of TiH 2 coated foam. Orthogonal experiment, the optimum parameters of the various coating process. Morphology observed by scanning electron microscopy (SEM) coated foaming agent; spectrometer coated foaming agent component test; using the the homemade the hydrogen releasing experimental device test TIH 2 coated hydrogen release characteristics of the blowing agent; to use coated foaming agent aluminum foam prepared in the laboratory. Experimental results show that: 1) coated Al the 2 O 3 of the optimum process parameters: of NaAlO 2 concentration of 0.06 mol / L, AL 2 (SO 4 ) 3 concentration of 0.01 mol / L, temperature 35 ° C, the titration rate to 60 ml / h, with vigorous stirring, titration the system PH value 5.2) coated SiO 2 optimal parameters: the Na 2 the SiO 3 concentration for 1 mol / L, HCl concentration for 2 mol / L, a temperature of 85 ° C, the titration rate as 60 ml / h, with vigorous stirring, titration system PH value of 9.3) coated TiH 2 hydrogen releasing performance major changes, single-coated Al 2 O 3 of TIH 2 will start to release hydrogen delay of about 60 seconds, single covered SiO 2 TiH 2 will begin to release hydrogen delayed for up to 70 seconds or so, first coated SiO 2 coated Al 2 O 3 the TIH 2 began to release hydrogen time of 75 seconds, the first coated Al 2 O 3 and then coated SiO 2 Ti H 2 postponed the hydrogen release time up to 90 seconds. To postpone the hydrogen release is better than the single-layer coated Al of coated SiO 2 of the TIH 2 2 O 3 of TiH 2 , the first coated Al 2 O 3 and then coated SiO 2 the TIH 2 < / sub> to postpone the hydrogen releasing effect. 4) Encapsulated the TIH 2 blowing agent can be prepared the holes more uniform aluminum foam, which TiH 2 composite coating prepared bubble Xi'an University of Technology Master's degree paper hole aluminum foam is more uniform. 5) to study the mechanism of chemical-coated: PH value of to control TIHZ suspension in about 5, through non-nucleation in TIH: A12O3 coating layer; control system pH value of about 9, available 510: film coated. 6) Analysis of the role of the cladding layer on the delayed release hydrogen, it is the result of the combined effect of the three aspects: the cladding layer delaying the process of heat conduction, coated slow TIH: the speed of the decomposition reaction, the coated hydrogen The diffusion of atoms to prevent escape play a role. Keywords: coated hydrogen releasing aluminum foam blowing agent

Related Dissertations

  1. Preparation and Characterization of the OCS/PLLA Composite Film for Biomedical Materials,R318.08
  2. Studies on the Preparation and Nutrient Release Characteristics of Low Molecular Weight Polylactic Acid Coated Urea,S145.6
  3. Research on Operational Life Span and Applications of Coated Electrode Resistance Welding for Galvanized Steel,TG453.9
  4. Study on Preparation and Characterization of Polyvinyl Chloride Coated Polyester Multifilament,TQ342.2
  5. Blue phosphor for PDP SrMgAl 10 O 17 : Eu 2 of combustion synthesis , surface modification and luminescence properties of,TN104.3
  6. Studies on Solid Dispersion of Indomethacin and Its Enteric-coated Tablets,R943
  7. Preparation of a Water Vapor Permeability Controllable Shape Memory Polymer and Its Application on Fabrics,TS195.2
  8. Chemical reduction process and properties of prepared copper clad iron,TF123.12
  9. Study on New Al-Coated Steel Enamel with Low Firing Temperature and Its Enamel Adherence Mechanism,TQ173.65
  10. Study on Postharvest Physiology and Storage Techniques of Apricot Fruits,TS255.3
  11. Experimental Research on Grindability of Aluminum Alloy,TG146.21
  12. Preparation and Structure of Carbon Encapsulated Fe Hollow Nanoparticles,TB383.1
  13. Study on Coating Characteristics of Lithium Iron Phosphate,TM912.9
  14. Preparation and Characterization of Anode Material Porous Li4Ti5O12/C for Lithium Ion Battery,TM912
  15. High Weatherability Titania Preparation Techinique and pH Control Method of Aqueous Suspension,TQ621.12
  16. Research of Synthetic Organic Fluorine Modified Acrylic Resin and Coating,TQ637.2
  17. Preparation and Mechanical Property Study of Aluminum Foam and Foam-filled Structure,TB383.4
  18. Study on Coated Electrodes in Resistance Spot Welding of Galvanized Steel Sheet,TG453.9
  19. Modification of Lithium Iron Phosphate as Cathode Material and Optimization of the Technics,TM912.9
  20. Preparation and Performance of Double-shell Phase Change Energy Storage Microcapsule,TB34
  21. Preparation and gas properties of transition metal phthalocyanine derivatives film,TB383.2

CLC: > Industrial Technology > General industrial technology > Materials science and engineering > Special structural materials
© 2012 www.DissertationTopic.Net  Mobile