Study on Bonding Technology and Performance of Miscanthus Floridulus Stalks Laminated Timber

Author: LiBing
Tutor: QianJun
School: Zhejiang Forestry University
Course: Wood Science and Technology
Keywords: Miscanthus floridulus laminated timber isocyanate urea-formaldehyde resin phenolic resin bonding technology
CLC: TS653
Type: Master's thesis
Year: 2013
Downloads: 20
Quote: 0
Read: Download Dissertation

Abstract


Miscanthus floridulus is a gramineous class of non-woody plant resources, which is characterizedby widely distributed, fast growing, high biomass, and very strong regeneration capacity. Looking foralternatives is necessary due to shortage of forest resources and wood raw material supplies in ourcountry. From the current research and application practice perspective, production of man-made boardsusing wheat straw, rice straw, cotton stalk, hemp stalk as raw materials have achieved successfulexperience. Therefore, manufacturing Miscanthus floridulus stalks laminated timber is an effective wayto solve the shortage of wood resources. Miscanthus floridulus stalks laminated timber is a new type ofartificial boards, this paper mainly studies hot-pressing process parameters under different adhesives,and determines the best hot-pressing process conditions. Influence factors and law of Miscanthusfloridulus stalks laminated timber was investigated and found. The results of this study are as follows:1. The influence of crushing on Miscanthus floridulus stalks laminated timber performanceThe performance of MOE, MOR, IB of Miscanthus floridulus stalks laminated timber withcrushing are higher than those without crushing. And the value of24hTS of Miscanthus floridulus stalkslaminated timber with crushing is lower than those without crushing. It can be concluded that crushingon Miscanthus floridulus stalks can improve physical and mechanical properties of boards.2. Bonding technology of Miscanthus floridulus stalks laminated timber using isocyanate adhesive(1) Process of Miscanthus floridulus stalks laminated timber using isocyanate adhesive is feasible,which can press Miscanthus floridulus stalks laminated timber with good physical and mechanicalproperties.(2) The study of influence factors of hot-pressing temperature, hot-pressing time, board density andglue consumption on Miscanthus floridulus stalks laminated timber performance. After analysis, thebest bonding process conditions for Miscanthus floridulus stalks laminated timber withthickness(12mm): hot pressing temperature:160℃, hot pressing time:9min, board density:700Kg·m-3,glue consumption:5%.3. Bonding technology of Miscanthus floridulus stalks laminated timber using urea-formaldehyderesin adhesive(1) Process of Miscanthus floridulus stalks laminated timber using urea-formaldehyde resinadhesive is feasible, which can press Miscanthus floridulus stalks laminated timber with good physicaland mechanical properties.(2) The study of influence factors of hot-pressing temperature, hot-pressing time and glueconsumption on Miscanthus floridulus stalks laminated timber performance. After analysis, hot-pressingtemperature has very distinct effect on24hTS; hot-pressing time has very distinct effect on MOE andMOR; hot-pressing time has distinct effect on IB. The best bonding process conditions for Miscanthusfloridulus stalks laminated timber with thickness(12mm): hot pressing temperature:150℃, hot pressingtime:9min, glue consumption:10%.4. Bonding technology of Miscanthus floridulus stalks laminated timber using phenolic resin adhesive(1) Process of Miscanthus floridulus stalks laminated timber using phenolic resin adhesive isfeasible, which can press Miscanthus floridulus stalks laminated timber with good physical andmechanical properties.(2) The study of influence factors of Impregnation Concentration, Impregnation time, Hot-pressingTemperature and Hot-pressing Time on Miscanthus floridulus stalks laminated timber performance.After analysis, Impregnation Concentration has very distinct effect on IB, hot-pressing time has verydistinct effect on24hTS. The best bonding process conditions for Miscanthus floridulus stalkslaminated timber with thickness(12mm): Impregnation Concentration:7%, Impregnation time:7min,Hot-pressing Temperature:170and Hot-pressing Time:7min.5. Fire resistance of Miscanthus floridulus stalks laminated timber treated by diammonium hydrogenphosphate(1) Miscanthus floridulus stalks laminated timber treated by DAP has significant flame retardanteffect.(2) The flame retardant performance difference of Miscanthus floridulus stalks laminated timberwith6%and8%DAP respectively are not obvious. Therefore, in order to reduce the production cost,the appropriate option is6%DAP.

Related Dissertations

  1. Preparation of Based on the Phenolic Resin of Activated Carbon and Adsorption-Photopcatalytical Character of Supported TiO2,TQ424.19
  2. Studies on the Preparation of 20% Chlorpyrifos CS and Its Analytic Methods,S482.3
  3. Amine metal compound synthesis, structure and reactivity,O627
  4. Study on the Synthesis、Preparation and Properties of Modification Phenolic Resin/NBR Composite Adhesive,TQ433
  5. Study on Single and Combined Toughening Phenolic Foam and Flame Retardant Properties,TQ328
  6. Ortho - phenyl ether type phenolic resin synthesis and ammonia-free molding compound,TQ323.1
  7. Study of Titanium-modified Phenolic Resins,TQ323.1
  8. Agricultural urea resin formaldehyde emission laws and regulation,TQ323
  9. The Research of Phenolic Resin Wastewter Treatment in Membrane Bioreactor with Polyester Nonwoven Fabrics,X703
  10. The Synergy and Industrial Application of Two Components Waterborne Polyurethane Coatings,TQ633
  11. Study on High Flame Resistant PIR Foam,TQ328.2
  12. Preparation and properties of high performance room temperature curing phenolic binder,TQ433.431
  13. The Research on Modification of Glue Used in Bamboo Curtain Plywood and Innovation of Glue Application Means,TS653
  14. Study on Special-Shaped RIM-PU Product,TQ320.7
  15. Study of Producing UF-G Low Toxicity and Powder Urea-Formaldehyde Resin,TQ433.431
  16. The Study of Compounded Fire Resistants Added in Phenolic Resin,TQ323.1
  17. Nucleophilic Research of Benzimizole Carbenes and Seleno-isocyanates,O626.23
  18. Synthesis and Properties of Novel Diphenyl-containing Epoxy Resin,TQ323.5
  19. The Study of Compatibility on Polypropylene/Intumescent Flame Retardant Composites,TQ325.14
  20. Compressibility of automotive brake friction materials and friction properties of,U465
  21. Mg (II) -catalyzed cycloaddition reaction of its chiral oxazolidinone class of drugs Synthesis,R914

CLC: > Industrial Technology > Light industry,handicrafts > Wood processing industry,furniture manufacturing industry > Processing > Wood-based panel production
© 2012 www.DissertationTopic.Net  Mobile