Shape Memory cellulose membrane preparation

Author: ZhangJianWei
Tutor: ZhuPing
School: Qingdao University
Course: Textile Chemistry and Dyeing and Finishing Engineering
Keywords: cellulose fiber structure property 1,2,3,4-butanetetracarboxylic acid ionic liquid
CLC: TS195.55
Type: Master's thesis
Year: 2011
Downloads: 72
Quote: 0
Read: Download Dissertation

Abstract


Cellulose pulp was dissolved in the sodium hydroxide/urea/thiourea solvent system in this experimental. The best condition of dissolution was researched. Wrinkle-free cellulose spinning solution and its membrane were prepared by using cellulose as material, NaOH-thiourea-urea aqueous as solvent and BTCA as anti-crease finish agent. Structure and properties of wrinkle-free cellulose membrane was analyzed by using the FT-IR, the text of wrinkle recovery and tensile strength. The results demonstrated that esterification-crosslinking reaction was happened and the properties of anti-crease was existed. The balance between wrinkle recovery and tensile strength will be achieved with the change of BTCA wt ratio, reaction temperature and reaction time.The technologies of preparation of the cosolvent systems of cellulose、DMAc/LiCl and butanetetracarboxylic acid was studied. The best technologies of solvent of cellulose were got from the study on the influence of the amount of LiCl, the amount of cellulose, heating temperature, heating time. The influence on wrinkle recovery to the regeneration cellulose membrane of BTCA, the coagulation bath concentration, glycerol plasticizing was also studied. At the same time we studied wrinkle recovery, tensile strength and breaking elongation of membrane. The results showed that the wrinkle recovery of regeneration cellulose membrane with BTCA is improved,but tensile strength decreased. The tensile strength would be better when the concentration of the coagulation bath increased. The extension of the membrane would increase after glycerol plasticization, and tensile strength increased. Further studies showed that The balance between wrinkle recovery and tensile strength will be achieved with the change of BTCA wt ratio, reaction temperature and reaction time.By studying cellulose、1,2,3,4-butanetetracarboxylic acid dissolved in ionic liquid [AMIM]C1, Wrinkle-free cellulose membrane were prepared by using cellulose as material, ionic liquid [AMIM]C1 as solvent and BTCA as anti-crease finish agent and the effect of coagulation baths on cellulose membrane performance was studied. Structure and properties of wrinkle-free cellulose membrane was analysed by using the FT-IR, the text of wrinkle recovery and tensile strength. The results demonstrated that both cellulose and BTCA were dissolved in ionic liquid [AMIM]C1,esterification-crosslinking reaction was happened and the properties of anti-crease was existed, wrinkle recovery will be better when crosslinking at higher temperature for longer time with increased BTCA wt ratio, but tensile strength will decrease.

Related Dissertations

  1. Space right to the basic theoretical research,D923.2
  2. Synthesis, Structure and Properties of PBO/SWNT Composite Fibres,TQ340.64
  3. Research on Physical Properties and Data Processing in the Process of Removing Acid of LNG,TE644
  4. Optimizition of Compositions and Processing Parameters and Wear Properties of Cemented Carbides YG11R Modified by Nanosized Rare Earth,TG135.5
  5. Technology of Filling Clearance and Optimizing the Bonds during Ultrasonic Brazing,TG454
  6. Research on the Structure and Characteristics of Permanent Magnetic Coupling,TH139
  7. The Study on Structural Calculation and Analysis Method of Lattice-type Crane with Variable Cross-section Boom,TH21
  8. Study on Spherical Harmonics Discrete Ordinate Method for Radiative Transfer,TK124
  9. Influence of over Fired Air on Gas-Solid Flows in a W-Shaped Flame Boiler,TK229
  10. A Study on the Electrodeposition of Zn-Co and Zn-Ni Alloys in the Reline Room Temperature Ionic Liquid,TQ153.1
  11. Research on Stability of Hierarchical Sattellite Network,TN927.23
  12. Research on Autamatic Music Structrue Analysis,TN912.3
  13. Research on Attitude Control Law of Endo-Atmospheric Missile,TJ765.23
  14. Study on Nonlinear Variable Structure Guidance Law,TJ765
  15. Sliding Mode Variable Tructure Control for Separating-Mirror System and Inhibit Chattering,TP273
  16. Modeling Analysis and Slip Estimation for Lunar Rovers,TP242
  17. Mechanism Design and Kinematic Simulation of a Celiac Invasive Surgical Robot,TP242.3
  18. The Research on the Construction of the Board of Directors of State-Owned Individual Proprietorship Companies,F275
  19. Research on the Structure of Sports Anatomy Materials of P.E.Education in the Universities of China,G807.4
  20. Yunnan Province, human capital, the network structure of critical efficiency factor,F249.27
  21. Multi-walled Carbon Nanotubes Au _AT_ of Pt, Au _AT_ of Pd core-shell structure of the catalyst preparation and electrochemical properties of,O643.36

CLC: > Industrial Technology > Light industry,handicrafts > Textile industry,dyeing and finishing industry > Dyeing and finishing industry > Finishing > Chemical finishing > Resin finish ( anti-crease finish )
© 2012 www.DissertationTopic.Net  Mobile