Study on Preparation of Core-shell Organosilicon Particles and Modification of PVC Resin

Author: ZuoZuo
Tutor: SongQiuSheng
School: Hefei University of Technology
Course: Materials Science
Keywords: Polysiloxane Copolymerization Reaction kinetics Core-shell particles PVC Toughening
CLC: TQ325.3
Type: Master's thesis
Year: 2010
Downloads: 86
Quote: 0
Read: Download Dissertation

Abstract


In this paper, core-shell polysiloxane/polyacrylate particles were synthesized by seeding emulsion polymerization method. It presented great superiority and could be utilized as biomaterial, coatings, adhesives, and many other materials due to their combined excellent performance. The preparation, structures and properties of core-shell polysiloxane particles were studied. The main results were summarized as follow:1. Silicon rubber emulsion was prepared by pre-emulsion. The influence of pre-emulsification time, concentration of H2SO4 catalyst and concentration of emulsifier sodium dodecylbenzene sulfonate (SDBS), reaction temperature and the mol ratio of D4/TEOS on the kinetics of the reaction were investigated. The results showed that the finally conversion of D4/TEOS increased with the increasing of the time of pre-emulsification, and the rate of the copolymerization of D4/TEOS was promoted when the reaction temperature raised and the concentration of catalyst or emulsifier increased. The rate of the copolymerization was accelerated and the time of equilibrium become shorter with the increasing of TEOS. The apparent reaction order for sulfuric acid, emulsifier and TEOS was 0.42, 0.38 and 0.27 respectively. The total activation energy of the copolymerization of D4/TEOS was 14.67kJ/mol. The particle size was determined to SDBS and TEOS. The results demonstrated that the average that diameter of the latex particles decreased with the increment of the SDBS concentration, while increased with the increment of TEOS. The crosslinking density may be regulated with the amount of TEOS.2. PSi/PMMA core-shell particles had been synthesized with PSi latex as core and PMMA for shell. The polymers structure were analyzed by FT-IR, DSC and TEM. The influence to the core-shell polymer of dropping rate of MMA monomer, SDBS content and coupling agent MPS content during the course of preparation were studied. The result indicated that excellent core-shell structure can be obtained with the reducing of the dosage of SDBS and the dropping speed of MMA monomer. The formation of core-shell PSi/PMMA was based on the embedding mechanism.3. A series of PSi/PMMA core-shell particles were prepared. The relation between the toughening effect of PVC and the size of PSi core, crosslinking degree, MPS content, core/shell monomer mass ratio, resins ratio were researched. The results showed that the optimal PSi particle size was 90nm, monomer mass core/shell ratios was 1/2. MPS content of 4% and TEOS content of 4-6% was preferable. The toughening mechanism of PSi/PMMA on PVC was investigated by SEM, which indicated that PSi/PMMA core-shell particles were dispersed homogeneously in the matrix of PVC resin, with a typical“sea– island”distribution.4. The multi-layer structure of PSi/PSt/PMMA core-shell particles was prepared by a two-step preparation process. The particles were charactrizaed by FT-IR, DSC, XPS and TEM. The paper’s innovations include: The emulsion copolymerization kinetic behavior of D4/TEOS was studied. The multi-layer PSi/PSt/PMMA core-shell particles were prepared with two-step process. The influencing factors of toughening PVC by shell-core PSi/PMMA were studied, and the results have very important significances for the development of PVC resin toughened by core-shell silicone particles.

Related Dissertations

  1. The Preparation of Aluminum-Ammonium Cationic Starch and Its Application in Papermaking,TS727
  2. Imidazolium ionic liquids selective electrode and its research activity coefficient,O646
  3. Study on Preparation and Characterization of Polyvinyl Chloride Coated Polyester Multifilament,TQ342.2
  4. Research and Analysis for Routing Algorithm of Variable Traffic Based on the Private PVC Network,TN915.06
  5. Absorption - Photo-assisted oxidation process emissions of methylene chloride,X701.7
  6. Subgrade Soil Moisture Investigation and Drainage Experiment Study,U416.1
  7. Advanced EFA electrical failure analysis the positioning technology PFA physical verification technology research,TN407
  8. Basic Study on the Physical-Chemical and Pyrolysis-Incineration Characteristics of Typical Components in Medical Wastes,X799.3
  9. The Improvement of the PVC Packing,F426.8
  10. PVC / ASA / DOP blends structure and properties of,TQ325.3
  11. PVC-U inner tube laminated steel octagonal hollow axial bearing capacity of concrete columns,TU398.9
  12. Synthesize, Characterize and Photochromic Reaction Kinetics Study of Multifunctional Spiroypran,TB34
  13. The Preparation and Application of Nano-Titanium Dioxide with Surface Functionalization,TB383.1
  14. Electrostatic Self-Assembly of Iron Oxide/Polyaniline Core-Shell Nanoparticles,TB383.1
  15. The Preparation and Property Research of Exterior Water-based Anticorrosive Paints for Containers,TQ630.7
  16. Performance optimization of the elastomer toughened PVC,TQ325.3
  17. PVC alloy mechanical relaxation behavior research,TQ325.3
  18. Preparation and Properties of Vinyl-Based Thermoplastic Elastomer,TQ334
  19. Predictive Control Method on PVC Stripping Process Based on SVM,TQ325.3
  20. Anti-Dripping Flame Retardant Treatment of Polyester Fabric,TS195.6
  21. Research and Design on the Well Lane Prespliting Smooth Blasting of One Side Closed Cumulative Cuting Tube,TD235

CLC: > Industrial Technology > Chemical Industry > Synthetic resins and plastics industry > Polymer resin and plastic > PVC and plastic
© 2012 www.DissertationTopic.Net  Mobile