Study on Characteristics of Contiuous Fiber-Reinforced Metal Matrix Composites under Hypervelocity Projectile Impact

Author: DingWei
Tutor: WuGaoHui
School: Harbin Institute of Technology
Course: Materials Science
Keywords: Hypervelocity impact Composites Damnification of impact Impact dynamics
CLC: TB332
Type: Master's thesis
Year: 2008
Downloads: 122
Quote: 0
Read: Download Dissertation

Abstract


Tif/Al composite, Tif/Cf/Al composite and Cf/Al composite were fabricated by pressure infiltration technique. Rolled LF6 aluminum alloy and the composites mentioned above were impacted by aluminum projectiles of different diameters at the speed of 2.5km/s.It can be judged from the critical diameter of the projectile staving in the material that Tif/Al composite is the best, and then the results of LF6 aluminum alloy, Tif/Cf/Al composite materials, Cf/Al composite dropped.Spark erosion wire cutting was used to dissect the sample, then followed polishing and corrosion to the section plane. Optical microscope and scanning electron microscope were used to observe the front and back and the section plane of the crater, also characters of the craters were measured. Comparing the characters of four kingds of materials above, aluminum alloy and Tif/Al composite performed plastic, and the performance of Tif/Cf/Al composites were between plastic and brittle, while Cf/Al composites performed brittle.The depth of craters in the composites caused by hypervelocity projectile impact was discussed from the aspect of impact dynamics semiquantitatively, and the resoults of analysis were consistent with the results of the experiment. The critical factors affected the depth of craters in the composites from, especially the effects of the high impendence mismatch under hypervelocity projectile impact, were given from theory.The reason for no adiabatic shear bands observed in the matrix of the composites was explained by using thermo-viscoplastic model and the results of the analysis of the depth of craters. The possible existing regions of adiabatic shear band in the composites were given from the aspect of mechanics, which was compared with the experimental results.After the analysis and explanation of the spalling phenomenon in the composites, it was found that the reason for spalling phenomenon in the composites was different from that for the aluminum alloy.After the measurement and comparison to the relationship between diametres of projectiles and the depth and width of craters, it is found that the depth of craters of Cf/Al composite is the smallest, LF6 alloy is the biggest.

Related Dissertations

  1. Preparation and Tribological Properties of TZ3Y20A-SrSO4 Ceramic Matrix Composites,TB332
  2. Reactive Hot-Pressing and Mechanical Properties of (ZrB2-ZrO2)/BN Composites,TB332
  3. Schiff base Synthesis, Characterization and Antibacterial Properties,O641.4
  4. Closed thin-walled beams composite modal damping prediction,TB33
  5. Carbon fiber reinforced epoxy resin surface treatment and interfacial properties of composite materials,TB332
  6. Synthesis and Visible Light-Driven Photocatalytic Performances of Silver Halide/Conducting Polymer Nanocomposites,TB383.1
  7. Reaction Sintering Preparation of Titaniferous Compound Ceramic Composites by Two-step Method,TQ174.1
  8. Preparation and Investigation on the Properties of Three-Dimensional Braided Quartz Fiber Reinforced Composites,TB332
  9. Studies on Damping Modification of Fiber Reinforced Composites,TB332
  10. Studies on Genotoxicity of Two Novel Contraceptive Materials,R114
  11. Large composite structures falling weight impact test technique,TB302
  12. Wood composite viscoelastic constitutive heat and thermal forming simulation study,TB332
  13. Preparation of Fe3O4-MWCNTs Nanocomposites by Microwave Assisted Polyol Method and Their MRI Enhancement Properties,TB383.1
  14. Research of Preparation Technology of High Performance and Low Cost Aluminum Composite Materials,TB331
  15. Fabrication of Microscale Ordered-reinforced Composite and Its Mechanical Characterization,TB33
  16. Composite materials by mechanical shear load connector pin load distribution of,V229.7
  17. Three-dimensional angle interlock woven composites mechanical properties of low-velocity impact and Finite Element Analysis,TB332
  18. Particle reinforced copper matrix composites mechanical behavior of finite element analysis,TB331
  19. Four -step braided composites under different stress levels bending fatigue behavior,TB332
  20. D braided composites bending properties of,TB332

CLC: > Industrial Technology > General industrial technology > Materials science and engineering > Composite materials > Non-metallic composite materials
© 2012 www.DissertationTopic.Net  Mobile