Zeolite A and Al-MCM-41 Mesoporous Molecular Sieve from Hangjin 2~# Clay: Synthesis and Characterization

Author: ChenBing
Tutor: ZhaoRiGeTu
School: Inner Mongolia Normal
Course: Physical and chemical
Keywords: Hangjin 2~# clay zeolite A Al-MCM-41 layered-porous silicate mineral materials Cheap mineral raw materials
CLC: TQ424.25
Type: Master's thesis
Year: 2011
Downloads: 64
Quote: 2
Read: Download Dissertation

Abstract


Molecular sieves have attracted considerable attention in the region of chemical engineering, industrial catalysis, biomedicine,environmental protection, and fabrication of novel Nano-object materials due to their adsorption, separation, ion exchange and shape-selectivity properties Molecular sieves are prepared using water glass, sodium silicate tetraethoxysilne as silica sources, the resource consumption is expensive.Recently, attention has been paid to a new process to prepare molecular sieves from natural clays. The Zeolite A and the mesoporous molecular sieves Al-MCM-41 were first synthesized from hangjin 2# clay The samples were characterized by X-ray diffraction (XRD), Transmission electron microscopy (TEM), N2 adsorption-desorption measurements, Scanning Electron Microscope (SEM), and X-ray Flourescent (XRF). At last, a layered-porous silicate mineral was prepare by organic-modification method from acided-hangjin 2# clay. The main contents are as follows(1) The hangjin 2# clay was obtained from inner Mongolia China and its chemical composition was analyzed by XRF. The hangjin 2# clay was actived by acid-activated and alkali fusion methods.(2) Zeolite A was synthesized from hangjin 2# clay by hydrothermal treatment. The samples were characterized by X-ray diffraction (XRD) Scanning Electron Microscope (SEM) techniques. The optimum conditions of crystallization on the formation of Zeolite A were:n(SiO2)/n(Al2O3)=2 n(Na2O)/n(SiO2)=1, n(H2O)/n(Na2O)=65, crystallization temperature T=95℃, crystallization time t≥6h. The quality of products reached the standard of the industry.(3) The ordered mesoporous materials Al-MCM-41 were synthesized from hangjin 2# clay. The Al-MCM-41 materials were investigated by powder X-ray diffraction (XRD), N2 adsorption-desorption measurements and transmission electron microscopy (SEM). A lot of experiments were adopted to optimize the processing parameters. The optimum conditions of crystallization on the formation of Al-MCM-41 were:pH=10-11 crystallization temperature T=100℃, crystallization time t=48h,mCTAB=1g (4) Layered-porous silicate mineral materials were prepared from acidification hangjin 2# clay as raw material, CTAB as a directing agent. The materials had uniform size of mesoporous (2.6nm), high surface area (389m2/g).

Related Dissertations

  1. Study on the Chimisorption Removal of FCC Gasoline Sulfur Compound,TE624.55
  2. Research on Enhancing Coagulation Using Na-zeolite Powder in the Micro-pollutant Water Treatment,TU991.2
  3. Synthesizing NaY Zeolite with Big Pore,TE624.91
  4. Modifying Design of a Marine Air Purifier and its Purifying Materials’ Molecular Simulation Research of CO2 Adsorption Performance,U664.51
  5. Synthesis of Mesoporous Molecular Seive Al-MCM-41 with Coal Kalin and Catalytic Application,TQ424.25
  6. Mesoporous Al-MCM-41 grafted organotin compounds Synthesis and Characterization,O627.8
  7. Preparation and Hydrodesulfurization Performance of Al-MCM-41-Supported Nickel Phosphide Catalysts,O643.36
  8. Moidification and Application of New Catalytic Material for Hydrogenation and Modification of Gasoline,TE624.93
  9. Study on the Catalyst for Producing More Light Olefines by Catalytic Cracking Process,TE624.41
  10. Arsenic Removal from Water by Nano Titanium Dioxide Modified Zeolite,TU991.2
  11. The Research on Treatment of Eutrophication of Raw Water by O3-Biological Zeolite,TU991.2
  12. Ozone - Biological Nitrogen Removal micro-polluted raw water iron, manganese Experimental Study,TU991.2
  13. Pulse discharge collaborative TiO_2 / zeolite catalytic degradation of phenol wastewater Study,X703
  14. Study on Lactic Acid Dehydration to Acrylic Acid by New Catalyst,TQ225.131
  15. Preparation and Properties of polyaniline composite nano- particle ER fluid,TB383.1
  16. Study on Silver-Carrying Nano-antibacterial Agent and Its Application in PMMA Denture Base,TB383.1
  17. Supported Ionic Liquid Preparation and removal of arsenic adsorption material research,X703
  18. Study on the Preparation of Modified Zeolite and Its Adsorption Ability of p-Nitrophenol in Polluted Water,X703
  19. Operating Conditions and Kinetics Investgation of Liquid-Phase Alkylation of Benzene with Propylene over Zeolite Catalyst,O643.32
  20. Different Effect of Compatibilizers on Polypropylene/Molecular Sieves Composites,TQ320.1
  21. The Transalkylation of Diisopropylbenzen on the USY Zeolite,O643.32

CLC: > Industrial Technology > Chemical Industry > Reagents and the production of pure chemicals > Adsorbent > Inorganic adsorbent > Used as artificial silicate adsorbent
© 2012 www.DissertationTopic.Net  Mobile