Dissertation > Excellent graduate degree dissertation topics show

Synthesis and Characterization of Hierarchical-Structured Mordenite

Author: LiNaiXia
Tutor: YinDeHong
School: Dalian University of Technology
Course: Chemical processes
Keywords: Mordenite Hierarchical-structured De-alumination Hard Template Zeolites as silica-alumina source
CLC: O643.36
Type: Master's thesis
Year: 2009
Downloads: 298
Quote: 0
Read: Download Dissertation

Abstract


Hierarchical-structured zeolite has advantages of both zoelites（high acidity,high hydrothermal stability） and mesoporous materials（favorable mesopore structure）,and it is an effective strategy to combine shape selectivity with efficient mass transfer.These features make it high desirable in many very important fields,especially in cracking of heavy oil and catalytic reactions bulk molecules involved.In this dissertation,mordenite as the main object was investigated.Firstly,the optimal synthetic conditions of normal mordenite were confirmed.Furthermore,the de-alumination disciplinarian for mordenite with different Si/Al under the acidic circumstance was quested for.Ultimately,hard template method and method by using zeolites as original silica-alumina source were adopted to prepare the hierarchical-structured mordenite with the traditional hydrothermal method,respectively.The main results obtained were as follows:（1） A better crystallinity of mordenite was obtained with crystallization time prolonging and crystallization temperature upgrading.As a result,the optimal crystallization time was 24 h and crystallization temperature was 175℃.The aging time of zeolite gel had little effect on the crystallinity and morphology of mordenite crystals.Si/Al in the initiative zeolite gel had great influence on the morphology of mordenite crystals.Mordenite nanocrystal aggregates were produced with Si/Al=5;yet mordenite crystals were formed as plates with Si/Al=15. And lower Si/Al was favored for the forming of mordenite crystals.H2O/SiO2 also played great role on the morphology of mordenite crystals,well-shaped hexagonal column was manufactured with H2O/SiO2=16.7.（2） Higher Si/Al in the initiative zeolite gel didn’t always produce higher framework Si/Al.Framework of mordenite may still remain after beening treated in hydrochloric acid. And the framework Si could protect Al from being taken off from mordenite crystals under acid surroundings,just like the protection of the framework Al against Si in MFI zeolite under alkaline environment.The treatment in hydrochloric acid had much effect on acidity of mordenite.（3） Mesoporous mordenite crystals could be successfully synthesized by using commercial multi-wall carbon nanometer tubes as template.And while the self-prepared porous carbon was employed as template,two statuses occurred.In the case of firstly mixing silica source and carbon source then adding alumina source,mordenite nanocrystal aggregates with extracrystalline mesopores were obtained,and the size of single mordenite nanocrystal was about 200 nm.Yet when,silica source and alumina source were mixed earlier before adding the carbon source,hollow-structured mordenite single crystals were manufactured. The size of the hollow core was about 8μm,and its wall thickness was around 1μm with many mesoporosities whose size focuses on 9.0 nm existing in the wall.BET of hollow-structured mordenite was 358.1 m2/g.Hollow-structured mordenite really coorperated the high acidity of mordenite and favorable mesopore structure.（4） Framework of mordenite couldn’t be destroyed within 30 min under the action of 2.0 mol/L NaOH solution at room temperature.Higher concentration of NaOH solution aggravated the damage of framework of mordenite,and in the meaning while the intensity of the diffraction peak for mesoporous molecular sieve increased.The composite molecular sieve was a new kind of three-hierarchical-structured material with micropores,mesopores and macropores in simultaneity.The composite molecular sieve MOR/MCM-41（0.5） obtained by dissolving in 0.5 mol/L NaOH solution largely maintained the regular morphology of normal mordenite,and its BET was 355.6 m2/g.Furthermore,it had high hydrothermal stability and acidity,and its mesopores still remained after being treated in the boiled water for 100 h.

Related Dissertations

  1. Synthesis and Characterization of Mesoporous Mordenite Without the Addition of Organic Template,O643.36
  2. Preparation and Characterization of Mesoporous Mordenite,O643.36
  3. The mesoporous electrode material and its super capacitor performance,TM53
  4. Synthesis and structure of ordered organic polymer mesoporous materials,TB324
  5. Investigation of Adsorption Process on Zeolites and Modified Zeolites by Frequency-Response Method,TQ028.15
  6. Hierarchical Zeolite: Synthesis, Characterization and Catalytic Application,O643.36
  7. Modified zeolite for the semi-regenerative reforming catalyst,TQ426
  8. Preparation and Characterization of Porous Oxide Spherical Particles,TB383.4
  9. Adsorption and Hydrothermal Stability of C4 Hydrocarbon Catalytic Cracking Zeolite: Experiment, Simulation and Quantum Chemical Calcultion,O643.32
  10. Sheet mesoporous materials prepared in the template synthesis of nanostructures,TB383
  11. In Situ Solid-state ～(13)C MAS NMR Study of n-Butane Isomerization over Solid Acid Catalysts,O657.2
  12. Study on the Palladium-based Catalyst of C5/C6 Paraffin Isomerization and Its Commercial Application,TQ426
  13. Synthesis, Characterization and Catalytic Property of Zeolites with 12-membered Ring,TQ426
  14. Study on Selectivity of Hydrocracking Catalysts,TE624.9
  15. Synthesis and functionalization of the Ordered macroporous poly Alcohol assembled and ordered mesoporous carbon materials,O631.3
  16. Preparation and Physicochemical Properties of Mesoporous Metal Oxides MO_x (M=Cr, Fe, Co, Sm, Eu),O643.36
  17. Mesoporous Materials: Synthesis and Application as Drug Carrier,TQ460.1
  18. Study on Technical Conditions for Preparing 2,6-diisopropyl Naphthalene from Refined Naphthalene,TQ242
  19. Mordenite Membranes: Preparation, Modification and Their Pervaporation Performance,TQ028.8
  20. The Catalytic Performance for Methane Dehydro-aromatization over Mo/HZSM-5 Catalysts,O643.32

CLC: > Mathematical sciences and chemical > Chemistry > Physical Chemistry ( theoretical chemistry ),chemical physics > Chemical kinetics,catalysis > Catalytic > Catalyst
© 2012 www.DissertationTopic.Net  Mobile